The dual - bath coagulation method suggested by j. a. va n ' t hof could be used in membranes with high selectivity clearance rate of low - molecular weight substances and moderate water flux theoretically. therefore it may be applied in the field of hemofiltration. to improve and optimize the performance of the pes ultrafiltration membrane applied in the hf, here the flat membranes and hollow fiber ( hf ) membranes are made in certain conditions based on the dual - bath coagulation method where pes is used as the membrane material, dmso as solvent and pvp & peg as additives this paper includes five parts as follow : 1
為了改善和優化聚醚
碸超濾膜（單浴法）在血液過濾實際應用中的性能，本論文以j . a . van ' thof等提出的雙凝固浴法為基礎，以聚醚
碸（ pes ）為主要成膜材料，以二甲基
亞碸為溶劑，並添加一定分子量的致孔劑（ pvp ，聚乙烯吡咯烷酮）以及一定分子量的添加劑（ peg ，聚乙二醇）按照一定配比在一定溫度下製成透明均一的鑄膜液，靜置脫泡后在一定的工藝條件下製成聚醚
碸平板膜和中空纖維膜，然後通過測試膜的結構和性能來評估其用於血液過濾中的前景。
An excellent adhesive was prepared from bismaleimide ( bmi ), epoxy resin ( e - 51 and tde - 85 ), 4, 4 ' - diaminodiphenyl sulfone ( dds ) in this thesis. the influence of liquid rubber and polymer ether imide ( pei ) on the properties ( especially high - temperature strength and the peeling strength ) were discussed, their different toughening characteristics and mechanisms were discussed. last, the process and effection of heat - resisted structural adhesive were studied by adhesive experiment of synchronizer in automobile. the results of investigation made clear : the adhesive, has good properties, especially heat - resisted properity
根據材料分子設計的原理，研究了二苯甲烷雙馬來酰
亞胺（ bmi ） 4 ， 4 』 ?二胺基二苯基
碸（ dds ） e ? 51 tde ? 85組成的環氧膠粘劑體系，研究該體系在作為高溫結構膠粘劑使用時的粘接性能；然後研究了用無規羧基液體丁腈橡膠（ ctbn ? x ）和聚醚酰
亞胺（ pei ）分別來增韌該體系的增韌效果；最後通過碳纖維耐磨材料與同步器圓錐環的粘接實驗，研究了耐高溫結構膠粘劑的粘接工藝和使用效果。
Effect on sublayer structure formation of pes membranes
聚醚
碸膜
亞層結構形成的影響因素
The result shows that dmso were intercalated into the interlayer of kaolinite and basal spacing was swelled from 0. 715nm to 1. 110nm, so the kaolinite - organic matter intercalation compound was formed
結果表明，二甲基
亞碸進入了高嶺土的層間，層間距由0 . 715nm增加到1 . 110nm ，形成高嶺土有機插層材料。
Syntheses and properties of coordination compounds of daphnetin with rare earths
鈾酰萃取劑雙
亞碸的合成及其微膠囊萃取鈾性能的研究
Flexor digitorum profundus tendons of chickens wer e cultured in the presence of deoxyguanosine ( dgua ) for 5 days, then cryopreserv ed in liquid nitrogen ( 196 ) without affecting their viability
用脫氧鳥苷培養處理雞屈趾深肌腱5天，無創凍存於液氮貯存器（ 196 ）中3個月，使用前將凍存腱在40溶液中融解並洗去腱中吸收的二甲基
亞碸。
In this study, it has been put forward that taking reactive nanometer magnetic fe304 particles as magnetic nucleus, and the copolymer of styrene ( st ) ? crylic acid ( aa ) as macromolecular shell, we could synthesize, magnetic polymer composite microspheres containing carboxyl groups on their surface, then microspheres are activated by thionylchloride, the surface of such magnetic composite microspheres thus produced had reactive acid chloride groups which then react with the free amino groups of the free soluble enzymes to give peptide bonds ( ? o ? h ?,
本研究首次提出了以納米級磁性fe _ 3o _ 4粒子為核心，苯乙烯（ st ） ?丙烯酸（ aa ）共聚物為高分子殼層，合成了表面帶羧基的磁性高分子復合微球，然後將這種微球用二氯
亞碸進行活化處理，在其表面形成了反應性酰氯基團，該基團可以與游離酶的氨基形成肽鍵，從而將游離酶固定化。
Methods the 54th generation of transformed human embryonic tendon cells and artificial composite materials of carbon fibers ( cf ) and polyglycolic ( pga ) were co - cultured in vitro to construct tet. lt was frozen in liquid nitrogen with four kinds of cpa for 2 months. post - thawed quickly and transplanted into hind limbs of nude mice, and repaired the defects of achilles tendon. after 2, 4, 6, 8, 12 weeks, the morphological, histological, ultrastructure, short tandem repeat loci and immunohistochemistry examination were detected, and biomechanical strength of tet were examined. result tendon cell survived and could secret type i collagen after 12 weeks to transplanted into nude mice. in the group of dmso + raffmose + kh2o4, vacuole in mitochondrion degraded i tendon cell ranged in order, abundant collagen fibers were found and linked each other and the biomechanical strength was increased as time elapsed. c onclusion dmso + raffmose + kh2o4 could protect tet in deep low temperature
組織工程肌腱制備完成後在四種抗凍劑保護下液氮凍存2月；快速復溫后植入裸鼠以修復跟腱缺損， 2 、 4 、 6 、 8 、 12周后取出，觀察形態學、組織學、電鏡和免疫組織化學變化，短串聯重復位點檢測和生物力學變化。結果實驗組組織工程肌腱體內植入12周后仍有肌腱細胞存活並分泌型膠原；隨著時間延長， 10二甲基
亞碸（ dmso ） +棉子糖（ 30mmol l ） + kh _ 2po _ 4 （ 25mmol l ）組線粒體空泡減少，肌腱細胞排列整齊，膠原纖維增粗並連接，抗拉強度增高。
The most efficient way to generate chiral sulfoxides is asymmetric oxidation of prochiral sulfides catalyzed by chiral metal complexes
摘要手性金屬絡合物催化硫醚的不對稱氧化是合成手性
亞碸最有效的方法。
Observation of curative effects of dolobene plus acupuncture on ankle joint sprain
二甲
亞碸凝膠加針灸治療踝關節扭傷療效觀察
Fluoroalkyl acetic acids were converted to their corresponding carbonyl chlorides, which was then reacted with o - amino benzaldehyde and ammonia gas to give 3 - ( 1 - iminofluoroalkyl ) - 1h - qunolin - 2 - ones in moderate yields
摘要用2 -氟烷基乙酸為初始原料，用氯化
亞碸或五氯化磷將其轉化為相應的酰氯，後者在室溫與鄰胺基苯甲醛縮合，通入氨氣迴流反應得到3 - （ 1 -
亞胺基氟烷基） 1h -喹啉2 -酮類化合物，產率中等。
Theoretical study on 2 - butyl - tetrahydrothiophene - 1 - oxide and its pd complex isomers
四氫噻吩
亞碸及其鈀配合物異構體的理論研究
The preparation of chiral sulfoxides and their applications in organic synthesis are reviewed
摘要本文對手性亞碸的制備及其在不對稱反應和天然產物合成中的應用進行了綜述。