均勻淬火 的英文怎麼說

中文拼音 [jūnyúncuìhuǒ]
均勻淬火 英文
uniform hardening
  • 均 : Ⅰ形容詞（均勻） equal; even Ⅱ副詞（都; 全） without exception; all
  • 勻 : Ⅰ形容詞（均勻） even Ⅱ動詞1. （使均勻） even up; divide evenly 2. （分出一部分） spare
  • 淬 : 動詞（淬火） temper by dipping in water, oil, etc. ; quench
  • 火 : fire
  1. Induction heated oil tempered spring wire is a kind of new technical material which has been developed since 1980s. it can be heated by means of eddy induced into itself through electromagnetic coil and this method is mainly used in surface quenching. with correct designing and reasonable current frequency, induction coil and heat treatment process selected, as well as plc controlling applied, the wire can be uniform heated along cross - sectional and longitudinal direction and can be quenched and tempered continuously

    應加熱油淬火-回火彈簧鋼絲，是二十世紀八十年代發展起來的新技術材料，在國外稱為itw induction heat oil tempered spring wire 。是通過線圈電磁感應鋼絲本身產生的渦流進行加熱，通常主要用於表面淬火。經正確設計，選擇電流頻率，合理的感應線圈及熱處理工藝，並實施plc控制，可使鋼絲整個截面及長度上得到均勻加熱，進行連續整體淬火和回火。
  2. Smooth tempered glass is manufactured by heating up float glass to swiftly and uniformly, with this special heat treatment and quenching process which increases glass strength up to four to five times vs, annealed glass, in case stresses beyond its capacity, smooth tempered glass simply disintegrates into innumerable small pieces, significantly reducing the risk of serious injury

    鋼化玻璃是將浮法玻璃經過物理性淬火處理，使其表面形成均勻的壓應力，而內部則形成張應力，從而有效的提高了玻璃的抗彎和抗沖擊性能，強度達到了普通玻璃的3 - 4倍，當其破碎時則分裂成均勻純角不易傷人的小顆粒，使其成為一種現代生活中理想的安全玻璃。
  3. Abstract : by means of metallographical examination and sem, the microstructure characteristics, macro - and microfractographs of the brittle broken wheel hull bolt of bj212 automobile have been studied. the results show that the thin - headed screw, with excessively deep carbonitriding layer and hardening layer, has less resistance to brittle fracture in the thin area of its head. at the root of the head connecting the stem, a tensile stress may emerge owing to the non - even quenching stress. those are the two reasons for low torque fracture of bolt

    文摘:藉助金相、掃描電鏡等手段對低扭矩脆斷的bj212汽車輪殼螺栓的金相組織特徵，宏觀和微觀斷口形貌等進行了研究，結果表明：這種頭部薄的螺栓，滲層和淬透層過深，使頭部薄區脆斷抗力降低，在頭部與桿的根部，由於淬火應力不均勻導致根部產生拉應力，均是導致螺栓低扭矩斷裂的原因。
  4. Analysis which was based on the fracture mode of mould in wire - cutting processing, and the results show that the partial - quenched of mould, the non - uniformity of blank temperature and the carbide segregation inside the material are the main reasons of deformation and cracking

    摘要通過分析在線切割加工中模具的破壞形式表明：模具不完全淬火、坯料溫度的不均勻分佈、材料內部的碳化物偏析是模具變形與開裂的主要原因。