塑性水泥漿 的英文怎麼說
中文拼音 [sùxìngshuǐníjiāng]
塑性水泥漿
英文
plastic cement grout-
Standard practice for mechanical mixing of hydraulic cement pastes and mortars of plastic consistency
塑性稠度的水硬性水泥泥漿和灰漿機械攪拌標準實施規程The properties of the new superplasticizer were studied by comparison with naphthyl type, including its effects on the fluidity and the slump - loss of cement paste and concrete ; its effects on the strength of the cement was also investigated. it has a good compatibility with cements of different types
將合成的hp高效減水劑與萘系高效減水劑的性能進行了系統的比較研究,包括分散性能、保塑性能;對水泥凈漿的流變性能的影響;與水泥的相容性;對水泥凝結時間的影響等等。In the paper the effects of the made parameters, the main materials and environmental conditions on plastic shrinkage cracking were investigated. it can be concluded as following : 1 ) there was a critical w / c ratio of maximum plastic shrinkage cracking between lower and higher w / c ratio of concrete mixtures made with the same cement content per cubic meter, concretes with lower or higher w / c ratio being less prone to plastic shrinkage cracking and the w / c critical ratio critical of maximum plastic shrinkage cracking being about 0. 5
本文研究了配製參數、主要原材料以及環境條件對新拌混凝土塑性收縮裂縫的影響,結果表明: 1 )單方混凝土水泥用量一定時,較低水灰比和較高水灰比對應的混凝土拌合物不易開裂,而中間某一臨界水灰比對應的混凝土拌合物開裂較嚴重,這一臨界水灰比為0 . 5 ;單方混凝土水用量或水泥漿量一定時,混凝土拌合物的塑性開裂趨勢與上述情況相似,但臨界水灰比分別為0 . 45 - 0 . 4和0 . 4 。The judge criterion of plastic shrinkage cracking for cement based material was studied through the testing of plastic tensile strength and plastic shrinkage capillary stress of cement mortar and concrete
摘要採用自行設計的塑性抗拉強度、塑性收縮開裂應力測定裝置測試了水泥砂漿、混凝土塑性抗拉強度和塑性收縮開裂應力。The experiment includes three parts. in the first part, we tested the coherence of the cfrp tendons with concrete, epoxy resin and neat cement grout and got the cohesion strength correspondingly. base on these data, we pointed out the problem of the tendons and provided the solution method
在這些試驗中我們首先對碳纖維塑料筋在混凝土、環氧樹脂和素水泥漿中的粘結性能進行了研究,分別測出了碳纖維塑料筋在這幾種介質中的粘結強度並對實驗數據進行了分析,指出了存在的問題和應該採取的解決辦法。Abstract : the article introduces cement slurry rheological characteristics and the method of determining the main parameters for cement slurry rheological characteristics, and analyses the difference between the rotation type and funnel type of viscometers in measuring plastic viscosity and apparent viscosity of cement slurry, and then the limitation of the funnel type of viscometer is described. the difference between rigidity and yield value is pointed out. finally through analysis of cement slurry rheological characteristics, the cement slurry filling mechanism is proposed, and the main factors affecting cement slurry are studied
文摘:介紹塑性流體水泥漿的流變性及確定水泥漿主要流變參數的一般方法;分析旋轉式粘度計與漏斗式粘度計在測定水泥漿塑性粘度、表觀粘度時的區別,說明漏斗式粘度計在使用上的局限性;針對粘聚力(動切力)的測定進行分析,認為粘聚力與動切力為不同的概念.通過對水泥漿流變性分析,提出水泥漿充填機理,並對影響水泥漿擴散的主要因素,即粘度影響水泥漿在節理裂隙中向前擴散的速度,動切力限制水泥漿擴散距離作了說明分享友人