Cu - zn - cr - zr conducting bar alloy and cu - cr - zr end ring alloys used for superpower asynchronous traction motor rotor were prepared by ingot metallurgy. using hardness measurement, tensile test at room and higher temperature, electrical resistance test at room and higher temperature, optical microscopy, xrd, sem, and tem, the mechanical and electric properties and the microstructure of above alloys at different treatment were studied. them were also analysed and explained in theory
採用鑄錠冶金法制備了大功率異步牽引電動機轉子用導條合金和端環合金,通過硬度測試、室溫拉伸、高溫拉伸、電導率測定、金相分析、 xrd 、 sem 、 tem等方法研究了不同加工工藝和熱處理工藝對上述合金力學性能、導電性能及其組織結構的影響和變化規律,並從理論上進行了分析和解釋。Ltd. a coupled vibration method on suspended free poles is employed to determine the initial young ' s modulus at elevated temperatures, also the thermal expansion coefficients of fire - resistant steel
通過高溫下的恆溫加載拉伸試驗,得到不同溫度下耐火鋼的屈服強度、極限強度、延伸率、面縮率和應力應變關系,並測定高溫下耐火鋼的熱膨脹系數,採用懸絲耦合共振法測定高溫下耐火鋼的初始彈性模量。Based on the characteristics of silicon whisker, the research on the modification of pa6 by silicon whisker sio2 - jx was made, and the result showed that the tensile strength, impact strength, brinell hardness, and heat resistance increased with the increase of the content of the whisker ; sio2 - jx could replace short glass fiber in the modification of pa6, improving the heat distortion temperature, removing the appearance of glass fiber, reducing shrinkage and the cost
摘要利用晶須矽纖維狀的特性,對其填充于龍玻纖改性進行研究,結果表明,隨晶須用量的增加,材料的拉伸強度、沖擊強度,布氏硬度、耐熱溫度均得到提高;晶須矽可取代短玻纖使用,提高熱變形溫度、消除玻纖外露,降低收縮率及生產成本等。Tensile heat - distortion
拉伸熱變溫度Gloss. color. tensile strength. yield tensile strength flexural rigidity. flexural. elasticity. lmpact resistance. coating thichness. coating hardness. adhesion lmpact. abrasion. chemical resistance. cosfficicent of linear. thermal expan - sion thermal transmission properties. hdt
光澤.顏色.拉伸強度.屈服抗拉強度.彎曲強度.彎曲模量.抗沖擊性.塗膜厚度.硬度.附著力.耐沖擊.耐磨耗性.耐化學性.熱膨脹系數.熱傳導系數.熱變形溫度If there are high temperature gradient between cool liner and hot liner, compressive plastic strain appear at that transient time, which lead to gas film wall bearing high tensile stress at high temperature. high tensile stress is one of main reasons which destroy combustor
分析表明,起動過程中由於熱傳導滯后引發的溫度梯度可以導致火焰筒氣膜唇邊在起動瞬間發生較大的壓縮塑性應變,進而使得該區域在工作時承受較高水平的拉伸應力,高的拉應力會導致火焰筒萌生裂紋。And we also give the intercalation mechanism of emulsion polymerization, the reaction calories will be benefit to the exploit of montmorillonite. the properties of acr / mmt / pvc composites were characterized. the addition of montmorillonite can improve the strain strength ; enhance the decomposition temperature and vicat soft point, little influence to impact strength
將聚丙烯酸酯/蒙脫土納米復合物與pvc樹枝共混,考察了蒙脫土對pvc的改性效果,發現呈納米分散的蒙脫土可以明顯的提高pvc的拉伸強度、熱分解溫度和熱變形溫度,對抗沖性能影響不大。分享友人