斷裂紋 的英文怎麼說

中文拼音 [duànlièwén]
斷裂紋 英文
failure crack
  • 斷 : Ⅰ動詞1 （分成段） break; snap 2 （斷絕;隔斷） break off; cut off; stop 3 （戒除） give up; abstai...
  • 裂 : 裂動詞[方言] （東西的兩部分向兩旁分開） open
  • 紋 : 名詞（花紋; 紋縷兒） lines; veins; grain
  • 斷裂 : break; disrupt; flying off; fracture; fragmentation; out break; rift;crack;bursting;rupture;rendi...
  1. Subordinate are plagioclase granite dike, layered tonalite, tonalitic conglomeration dispersed in amphibolite, ultramafic rock and metabasalt etc. plenty of igneous accumulated banding were discovered in amphibolite from nujinshan and bujing area some residual clinopyroxene also were found in a few of sample

    超鎂鐵巖多為構造透鏡體分佈於斷裂帶中，多蝕變為蛇紋石巖，在牛井山及布京一帶已發現並圈定了9個巖體（塊） 。
  2. There are typical laminated structure, soft sedimentary - slipping deformed structure, syngenetic brecciated structure in the ore which are the mirror of syngenetic sedimentation. the other type of ore has the charactristic of epigenetic mineralization, which is called as telescoped ore. the ore occurs in vein, pocket, lensoid and bedd

    礦石中發育典型的紋層狀構造、軟沉積滑動變形構造、同生角礫構造等反映同生沉積特徵的礦石構造；另一類礦石具有明顯的後生成礦特點，稱之為疊生改造型礦石，礦石產于脈狀、囊狀、透鏡狀及似層狀礦體中，與燕山期巖漿巖及斷裂裂隙構造關系密切。
  3. Crazing is the invariable precursor of brittle fracture.

    出現小裂紋必然是脆性斷裂的前兆。
  4. The crack eventually caused the chord to fracture.

    裂紋最終致使弦桿斷裂。
  5. Grow grain, say to expand again grain, as a result of, be adrenal had secreted fill, of human body adrenal coriaceous can secrete a kind of candy coriaceous hormone, this hormone can decompose the bounce fibrin in the skin carbohydrate character, make stretch fiber produces denaturation ; in the meantime, return the hyperplasia that can restrain fiber mother cell, bring about skin flexibility thereby fiber happening ruptures

    生長紋，又稱膨脹紋，是由於腎上腺分泌過盛，人體的腎上腺皮質能分泌一種糖皮質激素，此激素能將皮膚中的彈力纖維蛋白質分解成糖類，使彈性纖維發生變性；同時，還能抑制纖維母細胞的增生，從而導致皮膚彈性纖維發生斷裂。
  6. The cracking with these two types of underfill might become unstable and lead to catastrophic failure at the end. the critical length was about 12m for the assembly with no - flow underfill and 20m for the package with capillary - flow underfill at 20 ?

    模擬表明，山固化溫度冷卻到室溫時，所研究的倒裝焊封裝在填充不流動膠時晶元斷裂臨界裂紋長度為12pm ，而填充傳統底充膠時為20hm 。
  7. A dynamic fracture analysis of center - cracked brazilian disc specimens under mixed mode diametric impact loading

    徑向沖擊中心直裂紋巴西圓盤的復合型動態斷裂分析
  8. By means of bending tests of three - point and four - point, complex fracture experiments were made for cast iron material with crack. the stress intensity factor and breaking direction angle of cast iron material were measured and compared with theoretical values. based on the research some useful conclusions are given for engineering design and application

    通過3點彎曲和4點彎曲實驗方法，對含有裂紋的鑄鐵材料進行復合型斷裂實驗研究，測試鑄鐵材料的應力強度因子、斷裂方向角，將實驗結果與理論值進行分析、比較，找出兩者之間的異同點，得到一些對工程設計及應用具有實際意義的結論。
  9. Research about ctod and its components 8 ", " shows that the direction angle of ctod vector is identical with the fracture angle of void - mode fracture, which is obtained through experiments, and it is also identical with the result got by peak value line of stress triaxiality. besides, 8 i " was compare with vgc as criterion for initiation of void - mode fracture

    對裂紋尖端張開位移ctod及其張開型分量~ 1和剪切型分量~ 11的分析表明，在試件發生韌窩型斷裂時，按照圓弧裂紋中ctod矢量的垂直方向預測的斷裂角與試驗測得的斷裂角符合較好，與三軸度脊線預計的結果也比較一致。
  10. The pipe is complete enwrapped by cement after grouting, not loose and rupture when pulling wire

    外壁環狀波紋，灌漿后可完全包裹在水泥中，拉線時不會松動或斷裂現象。
  11. The solicitation development and rupture of craze in exiguous hierarchy play an connective work in the course of polymer ' s damage and rupture, it is a bridge in distortion mechanism of macroscopical and microcosmic

    細觀層次的銀紋引發、生長和斷裂在聚合物損傷斷裂的整個過程中起著承前啟后的作用，它是溝通宏、微觀變形機制的橋梁。
  12. : 36 < kth < 37 mpa / m3 / 2, 42 < kih < 44mpa / m3 / 2, 51 < kc < 52 mpa / m3 / 2 through the sem fractography, it is know that the susceptibility to brittle failure at room temperature is more than below 100 ?. and the susceptibility to brittle failure increase with hydrogen increasing, under the sustained loading, ductile cracking appears. the quantity of brittle cracking is more with crack growth

    T44mpa m 『 q ， sl lt52mpa in 』 」斷口分析表明，該合金充氫后其室溫時的氫脆敏感性大於100oc時的氫脆敏感性；且隨氫含量升高，氫脆敏感性增加：在恆載荷的作用下，該合金裂二紋開始擴展時顯示的是韌性起裂；隨裂紋增長，試樣脆性斷裂的比例增大。
  13. Fracture criterion of - mixed mode crack for orthotropic plate

    正交異性板復合型裂紋相對周向應力斷裂準則
  14. Thus the fracture likely initiated from fatigue sharpened cracks originating from slag and void in the plug welds.

    因此，斷裂可能是由於從塞焊焊縫內的焊渣和氣孔外形成的尖銳的疲勞裂紋而產生的。
  15. In conclusion, the research of this thesis indicate that the behavior of crack with a arc - tip is the same as that of a spiculate crack, but its load of fracture initiation is higher than the latter

    總之，本文的研究結果表明，裂尖寬度為0 . 12mm的非尖銳裂紋的斷裂行為與尖銳裂紋基本相同，但起裂載荷較高。
  16. The method for measuring the plane strain fracture toughness klc has been introduce to high polymer bonded explosives ( pbx ) by systematically studying technologies concerning the shape of specimen, the depth and its machining of crack, the loading rate, the measurement of critical fracture load, and the computation of klc, etc. the method has been used to test and study klc of three typical high polymer bonded explosives which are j2, jl, j3 respectively both at normal temperature and unmoral temperature

    本文以高聚物粘結炸藥為研究對象，對測試高聚物粘結炸藥的平面應變斷裂韌度所涉及的樣品形狀、裂紋深度及裂紋制備、加載速度、臨界斷裂載荷p _ q的確定及平面應變斷裂韌度k _ （ ic ）的計算等方面進行深入研究，建立了較為完善的炸藥平面應變斷裂韌度測試方法。
  17. The main beam of type 4sw - 40 potato digger easily engenders crack or breaking damage in the practical application. therefore, by means of modern test technology, the paper does some research on the vibration of the separating sieve and its influence on dynamic load of the main beam under the condition of laboratory

    4sw ? 40型馬鈴薯挖掘機在實際生產中主粱易出現裂紋或斷裂破壞。為此，本文提出在實驗室條件下，利用現代測試技術，就分離篩的振動及其對主梁的動載作用作研究。
  18. Because the propellant grain is viscoelastic material, the liner and adiabatic layer are also viscoelastic one, the interface debond problem is actually interface crack about elastic - viscoelastic or bi - viscoelastic materials. research about this problem relates to the knowledge of viscoelastic mechanics and interface fracture and combustion. numerical analysis method about interface debond on solid rocket motor is researched in this paper

    由於固體火箭發動機的推進劑藥柱是一種粘彈性材料，襯層和絕熱層也具有粘彈性性質，因此其界面脫粘問題實際上是彈性-粘彈性或雙粘彈性各向同性材料界面裂紋問題，對該問題的研究涉及到粘彈性力學、界面斷裂力學和燃燒學等相關學科。
  19. By means of the transformation from the focal coordinate system to the observation system, we obtained the external normal vector of the focal fault plane expressed in its observation system, and obtained the macrodamage degree of the researched block, which is calculated in dyadic

    由震源坐標系表示的震源斷層面換算到觀測坐標系得到其外法向矢量，可求得研究地塊以地震裂紋密度張量計算的宏觀損傷度的變化。
  20. The main purpose of this paper is to study crack growth rate of a class of nonlinear viscoelastic materials under the condition of constant load and small - strain. in this paper : the new test program is raised by referencing the existing test programs and by our trial and error ; in the new test program, facilities involved in the nonlinear viscoelastic crack tests are relatively few, the test process is relatively simple and the data obtained from the experiments are credible. on this basic, the calculation of j integral of nonlinear viscoelastic double cantilever beams specimens and the parameter of fracture work of corresponding nonlinear viscoelasticity are derived

    具體成果包括： 1 、證實了雙懸臂梁試件用於非線性粘彈性裂紋擴展實驗研究的優點：雙懸臂梁試件在實驗中能觀測到的擴展過程持續時間比較長，在計算j積分時，計算方法簡單； 2 、得到了改性聚丙烯材料用於非線性粘彈性裂紋擴展實驗的兩種有效的試件構形和相應的試件尺寸；採用不斷改善夾具的方法使得加載穩定； 3 、經過連續四個多月的時間得到了一組有用的實驗數據； 4 、得到了裂紋長度與時間的關系、裂紋擴展速度與時間的關系、裂紋擴展速度與裂紋長度的關系。