旋塗法 的英文怎麼說

中文拼音 [xuántúfǎ]
旋塗法 英文
spin coating
  • 旋 : 旋Ⅰ動詞1 （旋轉） whirl 2 （用車床切削或用刀子轉著圈地削） turn sth on a lathe; lathe; pare Ⅱ名詞...
  • 塗 : Ⅰ動詞1 （抹） spread on; apply; smear 2 （亂寫或亂畫） scrawl; scribble 3 （抹去） cross [blot; s...
  • 法 : Ⅰ名詞1 （由國家制定或認可的行為規則的總稱） law 2 （方法; 方式） way; method; mode; means 3 （標...
  1. The bandgap is found to broaden with increasing dopant concentration, and it is found that doping with al has the effect of shifting the optical absorption to the shorter wavelength, with both cases being attributed to the burstein - moss shift. we report a study on the fabrication and characterization of ultraviolet photodetectors based on zno : al films. using sol - gel technique, highly c - axis oriented zno films with 5 mol. %

    為了研究zno : al薄膜在紫外光探測方面的性能，我們採用溶膠-凝膠旋塗法在si襯底上生長出具有高度c軸取向的zno : al薄膜，摻al濃度為5mol . % ，並以此作為有源區成功制備出了au / zno : al / au光電導型紫外探測器的原型器件，並對其i - v特性、紫外光響應和光致發光等方面的性能進行了研究。
  2. Based on the features of the spraying - cup, such as large lagging, strong coupling, serious nonlinearity the system applies the fuzzy control method

    根據旋杯噴塗大遲滯性、強偶合性和非線性的特點，系統採用了噴塗參數模糊控制的方法。
  3. Then the gel film can be prepared by dip - coating or spin - coating technique on the surface of glass and followed by drying in the ethanol vapor

    使用浸漬提拉法或旋轉塗敷法，並通過放在乙醇蒸汽中乾燥，可在玻璃表面得到均勻的凝膠膜。
  4. The composite films can be prepared by in - situ polymerization processes, spin - cast from doped polyaniline / polymer solution, or by casting from polyaniline / polymer solution or dispersion

    原位聚合法、摻雜聚苯胺旋轉塗膜法和機械共混澆鑄法均可制備透明導電復合膜。
  5. To make cds / k4nb6o17 powder on the base of the k4nb6o17 powder which by the courses of ion exchanging, amine intercalation, sulfuration etc. to obtain cds / k4nb6o17 thin film through the same course of making cds / k4nb6o17 powder on the base of k4nb3o17 thin film on the quartz which made by the spin coating and after heat treatment. to make experiments with additives ( na2so3, 0. 1mol / l ) of photocatalytically decomposing water into h2 and o2 to evaluate the photocatalytic activities of the catalyst knb6o17 powder, cds / k4nb6o17 powder, k4nb6o17 film, cds / k4nb6o17 film. the crystalline structures of the midst powder and film productions were investigated by using the x - ray diffraction ( xrd )

    本課題的主要內容是：高溫固相反應合成具有層狀結構的k _ 4nb _ 6o _ （ 17 ）晶體材料，然後以此為母體材料，通過離子交換、層間胺插入、硫化處理等過程制備出cds / h _ 4nb _ 6o _ （ 17 ）粉末形式的光催化材料；通過旋轉塗覆法在石英玻璃基片上制備了k _ 4nb _ 6o _ （ 17 ）薄膜，採用一定的熱處理制度后對薄膜分別進行離子交換、層間胺插入、硫化處理等處理過程制備了cds / h _ 4nb _ 6o _ （ 17 ）薄膜形式的光催化材料。
  6. The spin - coated films are single - phase and highly oriented with the c - axis perpendicular to the quartz substrates. this type of materials has good thermal stability, and their decomposition points are near 300 c

    旋塗法沉積的該類材料的薄膜具有較好的單相結構，材料成膜后，其單相晶體的c軸很好地垂直於石英基片表面。
  7. At last tcnq and snpc films as well as poly ( metheyl methacrylate ) ( pmma ) films doped by tcnq and snpc were prepared by spin coating method. the influence of different spin speeds on the sensitivity of organic film was studied

    最後本文採用旋塗法制備tcnq和酞菁錫兩種材料的敏感薄膜，並用這兩種材料對pmma （聚甲基丙烯酸甲酯）進行了摻雜，運用sem觀察了薄膜表面形貌。
  8. Lppp thin films were prepared by spin coating from a solution of lppp in toluene and alq was formed by vapor deposition. different configuration devices with lppp single - layer, lppp micocavity and lppp / alq heterojunction were fabricated

    利用lppp甲苯溶液旋塗制備lppp薄膜，真空蒸鍍法制備alq膜和電極，分別製作了lppp單層無腔、 lppp單層微腔、增強型lppp / alq異質結結構的有機電致發光器。
  9. ( 2 ) zno thin films were prepared on glass substrates by sol - gel spin - coating method. the optical properties and surface morphologies of the films were investigated using photoluminescence ( pl ), optical transmission spectra, and atomic force microscope ( afm ), respectively

    （ 2 ）利用sol - gel旋塗法在普通蓋玻片上生長了zno薄膜，用光學透射譜、光致發光譜和原子力顯微術研究了zno薄膜的光學性質和表面形貌。
  10. In this work, zno thin films were prepared by sol - gel method on the glass substrate in order to study the influence of the preparation techniques on the crystallization, orientation and morphology of the films. we adopted a two - step heat treatment technique to optimize the micrcjstructure of the films, and subsequently discussed the forming process of the zno thin films

    本論文研究了在載波片和si （ 001 ）上溶膠凝膠旋塗法的制備工藝對薄膜的結晶、取向狀況以及薄膜形貌的影響，探討了溶膠凝膠旋塗法制備的氧化鋅薄膜的形成過程，同時引入兩步熱處理方法來優化薄膜的結構。
  11. The result showed that the spin coating method was better relatively. the obvious blue shift of pl was found in spectra of the ps / pmma composite prepared with spin coating. compared to the spectra from original ps sample, the luminescence quenching was greatly decreased for ps / pmma composite due to the prevention to ps layer with coated with pmma film and modification of dielectrical penetrability of the medium in quantum threads by the pmma

    實驗結果表明，用旋塗法實現的pmma固化后再與多孔硅復合而制得的樣品的結果最好，它與原始的多孔硅樣品相比發光峰發生了藍移而且發光強度下降很小，我們認為pmma層有限的厚度和pmma對多孔硅表面的保護使復合后發光強度下降很小，而且制備的多孔硅pmma復合體系的發光強度幾乎不隨時間而下降。
  12. Firstly, choose an appropriate solution system to make a steady solution, and then limn2o4 film precursor was prepared on stainless steel by spin coating method with the solution

    在前驅體溶液體系選擇過程中，確定了最佳前驅體溶液體系組成;在最佳的前驅體溶液組成體系下，採用旋轉塗覆法在不銹鋼基體上制備前驅體濕膜。