未熔透 的英文怎麼說
中文拼音 [wèiróngtòu]
未熔透
英文
nonpenetration-
This indicated that the fracture had initiated at the unfused butt weld in the longitudinal stiffener.
研究表明裂紋是從縱向加勁助未熔透的對接焊縫中起始的。Some crack extension probably developed from the unfused section of the butt weld across the thickness of the stiffener during transport and erection.
有些裂紋可能在運輸和安裝過程中就從加勁肋對接焊未熔透處開始發展。Hence lack of fusion and slag would exist at the weld root and create a large initial crack condition.
因而未熔透及夾渣存在於焊縫棍部，並造成大的初始裂紋條件。Slag, blowholes, and paint on unfused regions were observed at the welded junctions.
在焊接處看到了夾渣，氣孔及未熔透區的油漆。Often lack of fusion adjacent to the girder web in the transverse groove welds led to the cracking.
在靠近主梁腹板的橫向坡口焊縫處常常出現未熔透而導致裂紋。It has mang virtues such as weld moulding beauty, weld quanlity credibility and so on, espcially it can conquer not weld fully, not fusion and so forth fatal vice
它具有焊縫成型美觀、焊接質量可靠等優點，特別是對克服常規焊接方法中的未焊透、未熔合等危險性缺陷具有重要意義。Internal defects : lack of penetration, lack of fusion, slag, gas pole, carck, overheating
內部缺陷：未焊透、未熔合、夾渣、氣孔、裂紋、過熱。Each pass shall be cleaned free of slag before the next pass is deposited. each weld layer shall be visually free of slag inclusions, cracks, porosity and lack of fusion
每一層焊道都應在熔敷下一層焊道前清除熔渣。每一焊層都不得有可見的夾渣、裂紋、氣孔及未熔透現象。分享友人