楔形壓制 的英文怎麼說
中文拼音 [xiēxíngyāzhì]
楔形壓制
英文
sequential motion compaction-
As an advanced materials preparation technology, spray - deposition has shown remarkable superiority in producing large - sized alloys and metal matrix composites. however, the spray deposeted preforms usually contain a certain quantity of porosity. besides, the oxide films on the surface of the particles lead to week metallurgic conjunction between the particles. in order to obtain an ideal structure and performance, the porous preforms need further densifying and plastical forming. in this paper, a new technology named wedge pressing was used to densify spray - deposeted 5a06 aluminium alloy, in which the large deformation can be obtained through the sum - up of local deformation and multi - step small deformation. this method can also solved the problems in traditional processing and greatly decreased the producing cost. what ’ s more, the reserch on the wedge pressing desification rules about the large - sized spray deposeted preforms was significant it was vital not only to the further densification of the prefoums but also to the further research on plastical deforming the research was also benefit to the industrialization an the application of the spray deposeted porous materials
坩堝移動式噴射沉積技術作為一種先進的材料制備新技術，在制備大尺寸合金及金屬基復合材料方面具有顯著的優越性。然而噴射沉積坯件特別是大型坯件通常存在一定量的孔隙，顆粒表面存在一定量的氧化膜，顆粒之間未能完全達到良好的冶金結合狀態，因此需要進行后續緻密化和塑性變形才能獲得理想的組織和性能。本文採用一種新型的楔形壓制工藝，即通過局部變形、多道次小變形累積實現大變形的緻密化加工方法，對噴射沉積多孔坯料進行后續緻密化和塑性變形，很好地解決了傳統加工工藝的難題，大大降低了生產成本。Firstly, the comparation study between the wedge pressing and the contour forging has shown that the transverse deforming initiated from the surface of the preforms. when the superficies reached the moulding wall, the deforming moved downwards as the high - direction deforming increased, till the moulding chamber was full of stock ; the transverse deforming of the moulding pressing stock initiated from the center of the stock then surned into a drum - type. the distribution of the density and hardness of the high - direction indicated that the wedge pressing acquired a better ability of pressing penetration
首先對比研究了楔形壓制工藝與模壓緻密化工藝，發現楔壓坯料的橫向變形從上表層開始，當上表面與模壁接觸后，隨著高向變形量的增加逐步向下移動，直至坯料充滿模腔;模壓坯料的橫向變形從坯料中間開始，形成鼓形。高向的密度、硬度分佈表明楔壓比模壓具有更好的壓透能力。Secondly, the effect of transverse deforming on the property of the wedge pressing was studied. the results showed that : the wedge pressing stock with the transverse deforming amount of 10 % acquired the best performance. the highest density got the biggest rate of slope while with the amount of 30 % the curve was more some special structure and performance as following : the large porosities was crushed into small or linear ones with the high - direction deformation amount of 20 % ; as the increasing of the high - direction deforming, the particles got a further deforming, the porosities got a further crushing, the small porosities were mergered by the large ones and the former then disappeared ; when the amound reached 60 %, the quantity of the porosities would obviously decrease which made the materials compact, the microstructure more uniform and the density and hardness curves more horizontal, the relative desity could reach 99. 7 %, the tensile strength b of the as - compacted samples reached 408mpa with the yield strength s teached 289mpa and the elongation percentage reached 13. 6 %. in addition, the microstructure of the wedge pressing stock under the pressing temperectureof 450 was uniform, the porosities and the boundries of the grains basically disappeared and the conjunction between particles was great
採用雙向楔形壓制，大尺寸噴射沉積5a06鋁合金楔壓坯的組織和性能變化具有如下特點:當高向變形量為20 %時，大的孔洞變形破碎為小的孔洞，或呈線狀孔;隨著高向變形量的增加，顆粒進一步變形，孔洞進一步破碎，大孔「吞併」小孔，小孔塌陷並逐步消失;當高向變形量達到60 %時，孔洞量大為減少，材料基本緻密，組織趨于均勻，楔壓坯料的密度、硬度變化曲線接近水平線，坯料的相對密度達99 . 7 % ，抗拉強度_ b = 408mpa ，屈服強度_ （ 0 . 2 ） = 289mpa ，延伸率= 13 . 6 % ;對比其它的壓制溫度，在450楔形壓制的坯料組織均勻，孔洞及顆粒邊界基本消失，顆粒之間冶金結合良好。
分享友人