氣體摻雜 的英文怎麼說
中文拼音 [qìtǐchānzá]
氣體摻雜
英文
gas doping-
Some gas - sensitive test to deoxidizing gas have carried out based on tio _ 2 films by sputtering and doped some impurity. the experimental results showed that tio _ 2 films have different electron injecting principle and reactive mechanism, the behaviors of gas - sensor for hydrogen and ethanol manifest dissimilitude. this is due to that the oxygen vacancies were compensated by the impurity
用濺射制備的薄膜摻入部分雜質對還原性氣體進行氣敏測試,發現tio _ 2薄膜對酒精氣體和氫氣有不同的反應機制和電子注入機理,氣敏特性也表現出不同,而雜質的引入反而降低了tio _ 2薄膜的敏感性,可能是由於雜質對氧空位的補償所引起。This conclusion can also be applied in other synthesis methods such as chemical co - precipitation, aerosol synthesis, cryochemical method and hydrothermal synthesis
這一關鍵對稀土摻雜鋇鐵氧體的其他制備方法,如化學共沉澱法、氣溶膠法、低溫化學法和水熱法等也同樣適用。Two kinds of wo3 powder are prepared by sol - gel method and gas - phase reaction method with tungsten filament, and heater type gas sensors to trimethylamine are made. under different work temperatures, these sensors ’ sensitivities are measured, and the result indicates that wo3 by sol - gel has better gas sensing performance to trimethylamine. at the same time, the wo3 - based gas sensor to trimethylamine can work at low temperature, which
3 、本課題對不同摻雜的wo3材料進行了研究,發現摻雜3 % pd的wo3基氣敏元件在150ppm三甲胺氣體中,最佳工作溫度僅為85 ,該溫度下元件最高靈敏度可達11 . 7 ,並且元件的靈敏度隨tma濃度的升高而變大,這表明摻雜pd的wo3材料在低溫下對tma氣體有很好的響應。Thus the areas of the overlapping regions are compensated efficiently and the accuracy of measurement is highly improved. the volume of the bubbles can be estimated on the bubbles " area information, and a genetic algorithm ( ga ) based method is used to match and track bubbles in the image sequences, which solve tracking problem under complex conditions efficiently, such as some bubbles may have kinetic occlusion and crossover, some newly generated bubbles may entered into flow field and run away. a smooth kinetic locus is obtained by fitting the discrete centroids with a cubic spline function and at the same time the visual measurement is realized
根據氣泡在圖像平面中的面積估計氣泡的體積,並對流場中的所有氣泡採用遺傳演算法進行最佳的匹配跟蹤,有效地解決了氣泡群在流場中出現如遮擋、交又、新它『出現、逃逸等復雜情況下的準確跟蹤,並採用三次樣條插值方法對離散的質心點軌跡進行擬合,得到氣泡在流場中平滑的運動軌跡,從而實現了摻氣水流特性的可視化測童。The effect of storage time, syringing of methane and different gas adulteration on the activity of methane was studied
摘要討論了甲烷貯存時間和各種洗氣劑對甲烷活性的影響,研究了不同摻雜氣體對甲烷與空氣混合的爆炸極限影響。It shows that the particle number will fluctuate with the recombination coefficient ; 3 ) the dynamic process of the n - type doped diamond film is simulated. the particle distributions of s, s + and ar + are gotten. the result has important reference to the investigation of n - type diamond film doping at low temperature
( 3 )對不同氣壓、偏壓和不同的配比情況下n型硫摻雜的金剛石薄膜的動力學過程進行了模擬,得出了摻雜元素s和s ~ +以及惰性氣體ar ~ +的粒子數分佈,計算結果對摻雜過程的研究有重要的參考價值。Testing of materials for semiconductor technology ; determination of impurities in carrier gases and dopant gases ; determination of c - c - hydrocarbons in nitrogen by gas - chromatography
半導體工藝材料的檢驗.運載氣體和摻雜劑氣體中雜質的Through study on the electrical performance of sn - in2o3 nano powder, some conclusions were drawn. when sn - in2o3 precursor was calcinated at 700 - 1000, low square resistance was got. the resistance was lower when sn - in2o3 precursor was calcinated in vacuum than air condition
Sn - in _ 2o _ 3納米粉體的電性能研究表明: sn - in _ 2o _ 3前驅物在700 - 1000煅燒,方塊電阻較低,真空條件下煅燒試樣的電阻比空氣條件下煅燒試樣的電阻低,南京工業大學碩士學位論文中文摘要sno :摻雜10wt %左右時,試樣方塊電阻最低。This paper presents the effects of some features on the productivity of raw c60 materials, such as distance and approaching speed of electrodes, helium partial pressure and arc current etc. then we separate and purify the raw materials and obtain pure solid c60 of 99. 9 % and compare the purification efficiency and effect of different fluxion phase and fixed phase and discuss the effects of the experimental conditions, such as the depositing speed, the type of the substrate, the surface structure of the substrate and the temperature of the substrate. finally, we use xps, afm, ultraviolet, infrared and raman to analyze the component, structure and feature of the films qualitatively and quantitatively
本文首先研究了氦氣分壓、弧電流大小、電極間距以及電極推進速度等實驗條件對制備c _ ( 60 )粗品產率的影響;接著選用柱色譜法分離提純得到了純度大於99 . 9的c _ ( 60 )固體,比較了不同流動相和固定相的提純效率和效果;然後採用自己改進后的真空鍍膜機,利用電阻式加熱蒸鍍方法,得到了純c _ ( 60 )薄膜和不同摻雜比的銀摻雜薄膜;探討了沉積速率、襯底種類、襯底表面結構以及襯底溫度等實驗條件對薄膜結構的影響;最後通過xps , afm ,紫外,紅外,拉曼對薄膜的成分、結構和特性作了定性和半定量分析。( 7 ) the gel made from the aqueous solution of al + and fe + ion was calcined at 500, then the powder received were reduced in h2 atmosphere at different temperature, and the fe - al2o3 nanocomposites will be obtained as the reducing temperature increased to 900. ( 8 ) the transition phase feal2o4 was found during fe2o3 was reduced to fe
( 7 )將均勻摻雜法制各的, fe _ 2o _ 3含量為30wt的復合干凝膠,經500預處理後作為還原的前驅體,在氫氣氣氛下,經900還原1小時得到了純相的fe - al _ 2o _ 3納米復合粉末。In the experiments, the polypyrrole gas sensor was prepared on screen - printed electrodes by cvd ( chemical vapor deposition ). the effect of the electrochemistry undoping and doping on the characteristic of the gas sensor was studied
實驗採用化學氣相沉積的方式在絲網印刷電極上沉積聚吡咯氣敏膜用於氣體的檢測,並研究了電化學去摻雜?摻雜對傳感器氣敏特性的影響。With computations and analysis, the comprehension on the mixing and combustion process is increased, and some significative results are listed below : a ) there are three recirculation regions and one vortex region in the combustor, and these recirculation regions affect the combustion process deeply, b ) increasing side - arm angle and moving side - air inlet position toward the fuel inlet can improve mixing and combustion characteristics, and increase the combustion efficiency, c ) when the angle between two air - inlets equals to 180
通過計算與分析,增進了對補燃室內摻混燃燒過程的理解,為固體火箭沖壓發動機補燃室設計提供了一些有意義的結果: 1補燃室內的流動十分復雜,存在三個迴流區和一個旋渦區,迴流區對摻混燃燒過程有重要影響; 2增大空氣入射角度、向前移動進氣道出口位置有利於增強頭部迴流區強度,增強摻混效果,燃燒效率上升; 3In order to otain high quality zno thin films, we, for the first time, employ the plasma enhanced chemical vapor deposition ( pecvd ) to prepare high quality zno thin film at low temperature using a zinc organic source ( zn ( c2h5 ) 2 ) and carbon dioxide ( co2 ) gas mixtures. the effects of the growing condiction and the native oxide layer of si substrate on the quality of zno thin films was studied in detail. to prepare p - zno and overcome the dufficulty of reverse due to the interaction between the n atomic, we obtain high qulaity p - zno by a easy way of thermal zn3n2
為了在低溫下制備高質量的氧化鋅薄膜,我們採用金屬有機源和二氧化碳氣源,首次利用等離子體增強化學氣相沉積的技術在低溫下制備了高質量的氧化鋅薄膜,系統地研究了生長條件以及襯底表面氧化層對薄膜質量的影響,確定了生長高質量氧化鋅薄膜的優化條件;為獲得p - zno材料,克服在zno中摻n雜質間相互作用影響摻雜效率不易獲得p - zno的困難,我們通過熱氧化zn3n2的方法制備了p - zno ,獲得了一系列研究結果: 1 、詳細研究了氣體流速比,襯底溫度和射頻功率實驗參數對氧化鋅薄膜特性的影響。The paper put forward an aim to deposit n - doped titanium dioxide film on glass substrate by the atmospheric pressure chemical vapor deposition ( apcvd ) method. using ticl4 and oa as precursors, titanium dioxide thin films had been deposited by apcvd method. nitrogen had also been doped in the film when n2o gas was added as the dopant
在實驗室條件下以ticl _ 4和o _ 2為先驅體,採用常壓化學氣相沉積法( apcvd )制備得到具有一定光催化性和親水性的tio _ 2薄膜,並且以n _ 2o作為摻雜劑,對薄膜進行了n的摻雜,在一定程度上提高了薄膜可見光照射下的光催化性和親水性。It is concluded that for cvd method the cubic phase content and adhesion are highly effected by the crystal lattice mismatch between c - bn and substrate materials, however, for sputter method the crystal lattice mismatch between c - bn and substrate materials affects the quality of c - bn thin films very little. 5 n - type doping of bn thin films and preparing of bn ( n - type ) / si ( p - type ) heterojunctions adding s into the mixture of argon and nitrogen used as working gas, we sputtered 1ibn target to deposit bn thin films so as to study the n - type doping of bn thin films, and bn ( n - type ) / si ( p - type ) heterojunctions were prepared
5實現了氮化硼薄膜的n型摻雜,成功制備出bn型)乃…型)異質結並且首次系統研究了其卜v和cv特性我們用射頻濺射法濺射六角氨化硼靶,在工作氣體氮和氮中混入s ,沉積氮化硼薄膜,以研究氮化硼薄膜的n型摻雜,並得到bnh型)侶i …型)異質結。分享友人