水泥煅燒 的英文怎麼說
中文拼音 [shuǐníshāo]
水泥煅燒
英文
cement burning-
Clinker burning of special cement with precalciner kiln
用預分解窯煅燒特種水泥熟料Industrial waste containing wolfram acted as mineralizer in the burning of cement clinker
用含鎢工業廢棄物作礦化劑煅燒水泥熟料Influence of mno2 on the burnability and mineral formation of alite - sulphoaluminate cement clinker
硫鋁酸鹽水泥熟料煅燒及礦物形成的影響Experience of burning white cement clinker in precalciner kiln
預分解窯煅燒白水泥熟料的體會The analysis results of reaction between calcined kaolin and saturation ca ( oh ) 2 solution and xrd results of reaction products of calcined kaolin and cement indicated that calcined kaolin has a high volcanic ash active
通過對煅燒高嶺土與飽和石灰水的反應及煅燒高嶺土與水泥混合后的xrd分析,確認煅燒高嶺土具有較好的火山灰活性。Kiln simple structure, convenient and reliable control of the production process, the vulnerability of small, high rates of operation, the plant is calcined high - grade cement equipment, but also widely used in metallurgical, chemical, construction and other industries
回轉窯結構簡單,生產過程式控制制方便可靠、易損件少、運轉率高,是水泥廠煅燒高標號水泥的設備,同時也廣泛用於冶金、化工、建築等行業。The addition of calcined kaolin to cement increased the chemical shrinkage of cement stone, but it had no distinct impact on the self - shrinkage of cement stone
煅燒高嶺土摻入水泥中,增加了水泥石的化學收縮,對水泥石的自收縮的影響並不明顯。Repair with true bone ceramic composite for infectious bone defect in rabbits
牛煅燒骨顆粒復合抗生素骨形態發生蛋白和骨水泥修復兔感染性骨缺損Measurement and clinical significance of elastic modulus of composite of true bone ceramic granule and bone cement
活性煅燒骨顆粒骨水泥復合材料的彈性模量測定及其臨床意義Considering energy conservation and effects of calcined kaolin on the strength of cement, it was optimum method to produce calcined kaolin by calcining it at 980 c for 0. 5h and then cooling it suddenly
結合煅燒高嶺土對水泥強度的影響,考慮到節約能源,以採用980恆溫0 . 5h然後快速冷卻的方法作為最佳煅燒溫度與時間。Rotary kiln calcine capital equipment, cement of grog, there are dry process production and wet process production, have already been used such trades as metallurgy, chemical industry, etc. extensively
回轉窯是煅燒水泥熟料的主要設備,可分為干法生產和濕法生產,亦已被廣泛應用冶金、化工等行業。The relation between addition content of calcined kaolin, aluminium powders and aluminum sulfate in concrete and compressive strength, slump constant, 30min slump and permeability altitude were studied, and according to the experiment results, the component percent contents of crack - resistant and water - repellent admixture in cement were determined as following : calcined kaolin 6 %, aluminum sulfate 4 % and aluminium powders 0. 005 %
通過對煅燒高嶺土、鋁粉、硫酸鋁在混凝土中摻量對其抗壓強度、初始武漢理工大學碩士學位論文坍落度、 3omin坍落度保留值及透水高度的影響,確定了配製抗裂防水外加劑的各組成成分以其占水泥質量的百分比分別為:鍛燒高嶺土6 % ,硫酸鋁4 % ,鋁粉為0 . 005 % 。The calcined kaolin, aluminium powders and aluminum sulfate were used as components of water - repellent agent, which effects on cement hydration and concrete impermeability were discussed in this paper
本文以煅燒高嶺土、鋁粉、硫酸鋁作為防水劑的組份,研究了它們對水泥水化及混凝土的抗滲性的影響。The results show that the shrinkage of cement paste can be compensated by the new mgo - based expansive materials well, only if the burning temperature and burning time of expansive material are controlled and the dosage of expansive material in cement is suitable according to the hydration temperature and with fly ash or not
結果表明,根據一定條件下(如養護溫度、摻加粉煤灰等)水泥漿體的收縮特性來調整膨脹材料的煅燒溫度和煅燒時間,控制合理的摻加量,新型鎂質膨脹材料可以有效地補償水泥漿體的收縮。Because the calcining of cement kiln has characteristics of more variables, non - linearity, pure lag, strong coupling etc., controlling cement kiln with traditional control ways is very difficult
由於水泥回轉窯的煅燒過程具有多變量、非線性、純滯后和強耦合等特點,使得採用傳統的控制理論對水泥窯的控制變的十分困難。The experiment was done that the cured cement stone with addition of calcined kaolin were dipped into nacl solution of 2. 5wt %, and the experiment results showed that addition of calcined kaolin made cement stone pore fine and cement mortar displayed high property of impermeability
煅燒高嶺土的摻入可以使水泥石中的孔細化,通過對煅燒高嶺土摻入水泥中標養后在2 . 5氯化鈉溶液中浸泡試驗發現,煅燒后的高嶺土摻入水泥砂漿使其具有極好的抗滲透性。分享友人