泥漿結構粘度 的英文怎麼說
中文拼音 [níjiāngjiēgòuniándù]
泥漿結構粘度
英文
rigidity of mud- 泥 : 泥名詞1 （含水的半固體狀的土） mud; mire 2 （像泥的東西） any paste like matter; mashed vegetable...
- 漿 : 漿同「糨」
- 結 : 結動詞（長出果實或種子） bear （fruit）; form （seed）
- 構 : Ⅰ動詞1 （構造; 組合） construct; form; compose 2 （結成） fabricate; make up 3 （建造; 架屋） bui...
- 粘 : 粘動詞（粘附） glue; stick; paste; adhere to; bond
- 度 : 度動詞[書面語] （推測; 估計） surmise; estimate
- 泥漿 : slurry; mud
- 結構 : 1 （各組成部分的搭配形式） structure; composition; construction; formation; constitution; fabric;...
-
The result of macro - quality experiments show : mineral admixtures markedly slow the hydrating velocity of cement slurry, decrease and delay the hydrating max - temperature, in which steel slag is more effective ; expansive agents compensate concrete shrinkage, enhance the concrete dense degree, strengthen the interfacial layer between fiber and cement matrix and improve the physical mechanics qualities of acic ; minimal admixtures markedly improve the concrete workability property, increase the concrete later intensity & density and the capability of anti - chemical attack and anti - permeability ; hybrid fiber reinforces the toughness of obviously acic by the means of anti - cracking effect of fiber with different sizes and different properties in the corresponding construction levels
實驗結果顯示：鋼渣摻合料能顯著減緩水泥漿體水化速率，降低砂漿的水化溫升並延遲最高溫升時間；補償混凝土收縮，提高混凝土密實度，加強纖維與水泥石的界面粘結，增強混凝土力學性能，但不能明顯改善混凝土韌性。混雜纖維通過纖維的不同尺度與不同性質在相應的結構層次上產生阻裂效應，增韌鋼渣防滲抗裂混凝土；增加混凝土的破壞極限能，極大提高混凝土抗彎曲能力和韌性指數，改善混凝土脆性。To significantly improve both strength and durability of repair interfacial layer between old and new concrete, two attempts were firstly put forward in this thesis : ( 1 ) a kind of new modified primer would be produced by introducing shrinkage reducing admixture into cement mortar, which may both reduce the shrinkage of the interfacial layer, and lessen the content of large crystal in the repaired interface layer, accordingly, remarkably increase the van der waals force of interfacial layer
為大幅度提高新老混凝土修補界面層的強度和耐久性，本文首次提出並實現兩個設想： （ 1 ）以國產減縮劑為外加劑，配製新型改性水泥砂漿界面劑。該界面劑既能減少界面層宏觀干縮裂縫，又不增加大晶體，使界面層形成密實的微細觀結構，顯著提高粘結界面層內晶體間的范德華力。