浸出速率 的英文怎麼說
中文拼音 [jìnchūsùlǜ]
浸出速率
英文
leaching rate-
Some main results of testing research were as fellows : i. in the course of testing of leaching zinc dross, leaching zinc dross by sulfuric acid was researched and the effects on the leaching rate of the zinc dross were analyzed by author, the optimum conditions of leaching testing of zinc dross were determined as fellows : liquid - solid ratio 6 : 1, stirring ratio 250r / min, granularity 120 mesh, the soaking time 5h, the concentration of sulfuric acid of 30 %, and under these conditions, the rate of leaching zinc is above 92. 0 %. ii. in the course of testing of purification, on the basis of comprehending and comparing all present methods of the manganese - removal and iron - removal, the oxidizing method of manganese - removal in zinc sulfate solution using ammonium persulfate was put forward and the oxidizing method of iron - removal in zinc sulfate solution using the goethite process and oxidation - hydrolysis process was adopted
研究的主要結果具體如下: 1 、研究了硫酸浸出鋅浮渣並分析了影響浸出率的各種因素,確定了浸出鋅浮渣的最佳條件為:液固比為6 : 1 ,攪拌速度為250r min ,粒度為- 120目,酸浸時間為5 . 0h ,硫酸濃度30 ,鋅浮渣的浸出率大於92 . 0 ; 2 、在綜合和比較了目前除錳和除鐵的各種方法基礎上,提出了過硫酸銨氧化除錳方法和選擇了針鐵礦-氧化水解聯合法除鐵方法,並分析和討論了影響除錳率和除鐵率等各種因素,確定了除錳的條件為:溫度90 , ph值5 . 4 ,反應時間3h ,過硫酸銨達到理論值的1 . 2倍,除錳率超過99 . 86 ;聯合法除鐵的條件為:氧化反應時間1 . 5小時、溫度控制在90 92 、 ph值5 . 2 5Abstract : combined with fundamental characteristics of in - situ leaching mining, this paper presents primary factors influencing the reation rates, such as lixivant concentration, oxidizer, porosity, permeability, seepage volocity, structure of ore, minerals of competition, etc. the factors which influence the reaction rates of in - situ leaching have been discussed
文摘:結合原地浸出工藝的特點,總結提出了影響原地浸出反應速率的主要因素,並就溶浸劑濃度、氧化劑、孔隙度、滲透系數、滲透速度,礦石的結構、構造及礦物的嵌布特徵,競爭礦物等對原地浸出反應的影響進行了分析與討論。The research results indicate that this technology has some advantages of low cost, high immersion speed, high leaching ratio and low environmental pollution, this technology is a new way of hydrometallurgical treating refractory gold ores of jiangxi
研究結果表明,該法具有成本低、浸金速度快、浸出率高、環境污染少等特點,為江西難浸金礦石的濕法冶金探索出了一條新的途徑。To explore why the ratio of collectable wort extract is higher than that of non - extruded, the influences of all parameters of rice extrusion system ( barrel temperature, material moisture, screw speed ) on resistant starch content of extuded rice were studied by using second - order quadratic orthogonal rotating combination design method
摘要為探索擠壓蒸煮大米啤酒輔料麥汁浸出物收得率高於傳統不擠壓蒸煮啤酒輔料收得率的原因,用二次正交旋轉組合試驗法設計安排試驗,研究了大米擠壓蒸煮系統諸參數(套筒溫度、物料含水量、螺桿轉速)對大米抗性澱粉含量的影響規律。The data acquisition and data flow for various sensor carriers are analyzed systematically, and the calculation models are put forward. the model of quantification of wall - loss defects for in - line inspection with ultrasonic pigs has been established. and inspection data can be pretreated with this model, compressed with dpcm technique and treatd by dsp instruments
建立了檢測頭數據採集量及數據處理速率模型,首次建立了管道壁缺陷液浸超聲檢測的量化分析模型;提出採用該模型進行數據預處理后,採用差分脈碼調制技術進行數據壓縮,採用dsp器件提高數據處理速率。In the macroscopical field : ( 1 ) the relationship between the moisture and the speed of average collapse was attained, that is, the speed of average collapse will increase with increasing of the moisture at first, but it will decrease when the value get to certain max with increasing of the moisture ; ( 2 ) the model of relationship between the pressure and the speed of average collapse was established on the basis of experiment. the conclusion of that the speed of average collapse bouncing increase with increasing of the pressure was attained and the relationship between stress and distortion was established ; ( 3 ) the method of synthetical evaluation for collapsibility loess under the effect of time, pressure and moisture was offered
在宏觀角度上: ( 1 )以遼寧阜新地區黃土試樣的固結試驗數據為分析對象,得到了黃土濕陷速率與含水量的關系曲線呈單峰狀態的結論,即黃土濕陷速率在土體浸水初期會隨著含水量的增加而增大,但當含水量超過某一數值趨于飽和含水量時,黃土濕陷速率卻隨著含水量的增加而減小; ( 2 )立了黃土濕陷速率與壓力之間關系的數學模型,得出了黃土濕陷速率隨壓力的增大而呈階越增長的結論以及阜新地區濕陷性黃土的本構關系; ( 3 )提供了在時間、含水量及壓力等因素共同作用下,對黃土濕陷性進行綜合評價的方法。Hydrogen peroxide and cyanide consumptions can be reduced with the similar gold leaching speed and recovery
在金浸出速度和浸出率基本相同的情況下,可以降低過氧化氫和氰化物的耗量。Compared with ordinary cyanide process, the gold leaching speed and recovery can be greatly increased and cyanide consumption greatly reduced by the cooperative use of potassium permanganate and hydrogen peroxide
與常規氰化法相比,過氧化氫與高錳酸鉀聯合使用時,金的浸出速度和浸出率顯著提高,氰化物耗量大大降低。This paper analyses the result of in - situ mining and dump leaching briefly, using kinetics method of certain low quality copper ore in hunan province, get the reaction speed of this ore, and it offers the gist for leaching this ore
摘要簡要的對湖南某低品位銅礦石原地破碎浸出進行了動力學分析,得到了此種礦石原地破碎浸出的反應速率,為此種礦石進行浸出提供了依據。A grey - system - theory - based approach for predicting the leaching rate of heap leaching
堆浸浸出速率的灰色預測Prediction of leaching rate of in - place blasting - fragmented ore using gary system theory
原地爆破浸出速率的灰色預測By calcining low humidity pelleted kaolin, a kind of metakaolin pellet, inside which the macroporous structure developed , has been prepared. the structure remarkbly benifits reactant ion transference. so, the variety has high acid leaching reactivity, even coarse as the pellets are, its reaction kinetic is still maintained zero order up to a significant conversion rate
在用鹽酸加熱浸取時,該類球粒內的鋁質組分表現出高酸溶反應活性,不同粒級的該類球粒有相似的浸出率時間曲線,且大部分鋁能被迅速浸出。分享友人