浸漬強度 的英文怎麼說
中文拼音 [jìnzìqiángdù]
浸漬強度
英文
bucking strength-
The strength and wear resistance of diamond drill bits for petroleum exploitation will be increased considerably when cast tungsten carbide is applied and adheres to the substrate firmly with cast tungsten carbide of 80 - 200mesh as the skelton and copper alloy as the soldering material in a process of non - pressure immersion
石油鉆探行業用的金剛石鉆頭,用粒度為80 ? 200目的鑄造碳化鎢粉作骨架,採用無壓浸漬工藝,以銅合金作釬焊料,將鑄造碳化鎢與基體牢固結合,強度、耐磨性大大提高。Test methods for the determination of bond strength of impregnating agents to an enamelled wire substrate
浸漬劑對漆包線底襯的附著強度的測定試驗方法Ptfe braid ( soaked ) is modeled and weaved with unprocessed f4 ribbons, which is chemically stable, lubricating, tensily unchanged in surroundings of high temperature or damp, and is easly installed or moved
聚四氟乙烯編織(浸漬)盤根採用f4生料帶經編織(浸漬)定型而成,具有良好的化學穩定性、自潤滑性能好,在高溫和潮濕環境下強度不變,易裝填和拆除。The parameters of impregnation are as follows : ph is about 3, the range of temperature is from 20 to 45, and the time is about 2 to 6 hours. after the necessary treatments, zirconia cloths had the optimal strength when the diameters of zirconia fibers were controlled in 4um to 7um, and the sizes of zirconia grains were in 50nm to 100nm. the affec - ting factors were discussed and the liner regression analysis of the cloths was made, from w hich they show that the diameters and grain sizes have the significant influences on zirconia cloths. the obtained zirconia cloths have been accepted for use in nickel - hydrogen batteries by practical use
研究結果表明:粘膠類纖維布最適合制備氧化鋯纖維布的前軀體;鋯液濃度以飽和溶液為宜;浸漬工藝參數為ph值3左右,溫度20 45 ,時間2 6小時;多餘鋯鹽的去除、浸鋯液后纖維布的整平處理及平燒施應力燒成有利於氧化鋯纖維布的柔軟及平整; 200 600燒成溫度段應緩慢燒成,控制氧化鋯纖維直徑在4 7 m ,氧化鋯晶粒尺寸50 100nm時氧化鋯纖維布的強度最好。Precast concrete products - test method for glass - fibre reinforced cement - determination of the absorption of water by immersion and determination of the dry density
預制混凝土製產品.玻璃纖維增強水泥的測試方法.浸漬時水吸收性的測定和干密度的測定分享友人