  1. The results show that, with the quenching temperature ( 270 ~ 380 ) increasing, the carbon content and percentage content of retained austenite increase first and then decrease, which are up to a maximum value at 360 ; the tensile strength of adi decreases ; the elongation and impact ductility of adi increase first and then decrease, which are up to a maximum value at 360 ; but the hardness of adi decreases first and then increases, which is up to a minimum value at 360

    結果表明，在試驗溫度范圍內（ 270 ~ 380 ） ，試樣中殘余奧氏體的含碳量及其含量隨著等溫淬火溫度的升高先增大后減小，均在360等溫淬火時出現最大值；抗拉強度隨著等溫淬火溫度的升高而逐漸降低；伸長率和沖擊韌度隨著等溫淬火溫度的升高先增大后減小，在360等溫淬火時出現最大值；硬度則隨著等溫淬火溫度的升高先減小后增大，當360溫淬火時硬度最低。