溶脹橡膠 的英文怎麼說
中文拼音 [róngzhàngxiàngjiāo]
溶脹橡膠
英文
swollen rubber-
Rubber, vulcanized - determination method of swelling index
硫化橡膠溶脹指數測定方法Making sensitive material : made in non - sulfur vulcanization system with the formula : epdm 100kg, dicumylperoxide ( dcp ) 2kg as cross - linking agent, stearic acid 1kg as processing aid, oxidized zinc ( zno ) 3kg as accelerant, wax oil 10kg as lubricant ; and made in vulcanizing condition : vulcanizing temperature 170 c, vulcanizing time 15minutes, vulcanizing pressure 3 mpa, the vulcanized epdm is optimal sensitive material for petrol. the sensing head equipped with the vulcanized rubber possesses two qualities : better swelling response and better anti - interfere against temperature variation
敏感材料的制備:用無硫硫化體系;配方為:生膠100kg , dcp2kg ,硬脂酸1kg , zno3kg ,石蠟油10kg ;硫化條件:硫化溫度170 ,硫化時間15分鐘,硫化壓力3mpa ,制備的硫化橡膠對汽油的監測較理想,用其裝備的傳感頭不僅有較好的溶脹響應性能,而且有很好的抗溫變干擾能力。When the sensing head equipped with rubber 4 # with diameter of 8mm and length of 12mm is pressed and its incipient wavelength shifts 0. 5 - lnm, its alarming level can be set as 1nm, and its response tune for petrol is 5 minutes
用直徑為8mm 、長為12mm的4 # (上述配方)橡膠棒裝備該傳感頭,傳感頭的初始波長預漂0 . 5nm ? 1nm時,傳感器的漏油報警限可設定1nm ,對汽油的溶脹響應時間為5分鐘。Standard test method for rubber, raw - determination of gel, swelling index, and dilute solution viscosity
測定生橡膠的凝膠膨脹指數及衡釋溶液粘度的標準試驗方法Swelling behavior and distribution coefficient in the silicone rubber membranes
硅橡膠膜中的溶脹行為及分配系數The conclusion of swelling experiment is that elastomer swelling of compound alcohol fuels is stronger than that of gasoline and elastomer swelling is more stronger when more bigger blend ratio
溶脹作用實驗結果表明,甲醇與汽油的混合燃料對橡膠件的溶脹作用比純汽油的強,並且隨著摻燒甲醇比例的增大,甲醇汽油混合燃料對橡膠件的溶脹作用是逐漸增大的。Standard test method for determining the effect of lubricants on swelling property of synthetic rubbers
潤滑劑的合成橡膠溶脹性測定法This paper primarily studies the delamination and elastomer swelling of compound alcohol fuels
本文首先進行了醇類混合燃料的分層以及對橡膠件的溶脹作用實驗。分享友人