melt treatment process-
This article choosed out organic phase change materials, and, the solid - liquid - equilibrium of eleven binary system including fatty alcohol / fatty acid, n - octadecane / fatty acid, n - octadecane / fatty alcohol system were determined by cooling curve, and, t - x phase diagrams of these systems were drawn. the result shows that all these systems are simple eutectic, at the same time, the entropy of phase change of every system in the eutectic point is determined by using differential scanning calorimetry ( dsc ). and n - octadecane / fatty acid systems were calculated theoretically
本文初選出部分有機相變貯能材料,採用步冷曲線法測定了12醇-羧酸系列、 18烷-羧酸系列、 18烷- 12醇體系共11組體系的二元固液相平衡關系,繪制了這11組體系的t - x相圖,測定結果表明,這幾組體系均為簡單低共熔體系;同時利用差熱掃描量熱法( dsc )對上面各組體系低共熔點處的相變焓進行了測定;並對18烷-羧酸系列進行了熱力學理論預測。The difference of reactive mechanisminduced the difference of their structure. v _ 2o _ 5 product prepared by melting - cooling showed more notable undefined structure. after heat - treating under300, particle size becomes smaller, and aggregate to globate grain, showesbetter electrochemical performance at low charge - discharge rate
熔融淬冷法合成的樣品其無定型結構更明顯,前驅體經過300熱處理后,材料的粒徑變細,團聚成球狀的顆粒,球狀特徵更顯著,在低倍率下具有較好的電化學性能。In this paper, pure and doped ktp crystals were grown from the flux using a top - seeded method, and special technique have been used to lower the electrical conductivity to three orders of magnitude than common flux ktp, the values is up to 10 - 10 ( cm ) - 1, this overcame the shortcoming that common flux ktp cannot be used in e - o application field because of having higher electrical conductivity. the growth condition, doped elements and annealing technology were investigated. single crystals of ktp with high quality and big z - cut cross section were obtained by optimizing the parameter of crystal growth
本實驗採用頂部籽晶熔劑法生長了純的以及不同摻雜的ktp晶體,用特殊工藝處理技術將普通熔劑法ktp的電導率降低了三個數量級,達到了10 ~ ( - 10 ) ( cm ) ~ ( - 1 ) ,解決了普通熔劑法ktp晶體由於離子電導率太大而無法用於電光應用領域的困難;對ktp晶體的生長條件、摻雜元素以及退火工藝等進行了研究,通過優化生長工藝技術參數,突破了工藝技術生長難關,得到了高光學均勻性、具有大z切面的ktp單晶。Differential scanning calorimeter ( dsc ) combined with melt fluxing technique was used to realize undercooling of melt and its specific heat was measured at the same time, and its thermodynamics were calculated simultaneously and compared to four well - known models
本文將差示掃描量熱法( dsc )和助熔劑處理技術相結合,研究了熔體的過冷現象,測量了過冷狀態下熔體的比熱,計算了過冷熔體凝固過程中的其它熱力學參數,並與四種近似模型進行了比較分析。Treated with prudent chosen intercalation regent, hydrophilic montmorillonite becomes hydrophobic ; the interlayer distance of montmorillonite is expanded and the compatibility of montmorillonite with polymer matrix is improved. montmorillonite disperses in the polymer matrix promoted by mechanical force and chemical interaction, which make it possible to prepare polymer / clay nanocomposite by melt intercalation process
通過對蒙脫土進行有機化處理,使蒙脫土由親水性變為親油性,蒙脫土層間距增大並改善蒙脫土與聚合物基體的相容性;利用受限空間內力化學作用促進蒙脫土在聚合物中的分散,使熔融插層法制備聚合物粘土納米復合材料成為可能。分享友人