thermal weldability-
The welding performance of homemade wear - resistant cast steel has been studied base on the weldability tests, the repair welding procedures of wean - resistant cast steel ( abrasion - plates ) have been made up, the results show that satisfying repair welding quality can be attained with such welding conditions as the low hydrogenous alkalescent welding rod, preheating and slow cooling, strictly maintaining the interbedded temperature of 250 ~ 300 and controlling welding technique
通過對其焊接性能的試驗研究,制定了該類鑄鋼件(磨耗板)的補焊工藝:低氫型堿性焊條,預熱與緩冷相結合的工藝措施,嚴格控制層間溫度( 250 ~ 300 )及焊接工藝規范,可獲得滿意的修復質量。Before repairing, basing on the actual working condition, concerning the weldability, stress and deformation issues, the scheme of the cold welding technology whose essential being gtaw, low temperature preheating, postweld hammer the welded seam was established
修理前,圍繞兼顧解決焊接性、應力和變形問題,結合實際施工條件制定了以手工鎢極氬弧焊、鎳基焊絲、焊前低溫預熱、焊后錘擊焊縫為要素的冷堆焊工藝。( 2 ) design of the implantating device : some quantity of 316l stainless steel, perform forging and thermal rolling, drawing filament ( diameter 0. 4mm and 0. 23mm respectively ), enlacing and jointing, after that assembling the products into guiding filum, a technical examination was carried out to appraise their physical capability. the second part : experimental study : animal experiments were used to screen and observe its validity and security : under general anesthesia, tracheotomy was performed on the healthy dog, the bronchus was localized using x - ray fluoroscopy fibrobronchoscope and with the help of the implanting equipment, several niti alloy occludes were implanted into the target bronchus of the dogs through the biopsy channel in the fibrobronchoscope
( 2 )推送器的研製:取316l不銹鋼熱軋,分別拉製成不同直徑的不銹鋼絲分別用作製作內芯、外環及車制螺絲,再經纏繞、焊接、裝配成推送器。對上述兩者進行技術鑒定。第二部分:支氣管封堵器的實驗研究:四種形狀的封堵器分四組(上述四種封堵器各12隻)進行動物實驗,分別觀察其安全性與有效性。Welding of thermoplastics - machines and equipment for hot gas welding including extrusion welding ; german version en 13705 : 2004
熱塑性材料焊接.熱氣焊機械和設備Railway fixed equipment. thermit welding of rails. welds performed by compagnies. performance and acceptance conditons of works
鐵路固定設備.鋼軌熱劑焊.由compagnies執行的焊接.工程特性和驗收條件To validate the formulated transition element for the calculation of the hot - spot stress and stress concentration factor in the welded components by experimental results, the stress concentration factor of the experimental welded specimens carried out in the research group is calculated by using the developed plane - transition element. the calculated stress concentration factor in the two types of tested welding components agrees well with that obtained from the experimental result. and the calculated result on the tendency of hot - spot stresses agrees well with that from the measured result
為了驗證文中構造的過渡單元模型用於分析焊接節點附近的應力集中問題的正確性和有效性,進一步又對過渡單元模型進行實驗結果驗證,採用平面過渡單元模型計算了本課題組進行的兩類焊接構件的應力集中系數,並與根據實測方法得到的應力集中系數進行了比較,計算結果與實驗測試得到的應力集中系數和相應的熱點應力變化趨勢比較吻合,為本文建立的過渡單元的實際應用提供了初步的基礎。Plastics. sheets. assessment of suitability for thermal welding hot bar method.
塑料.薄板.熱焊接適應性評估熱棒法Railtech international is the world leader in manufacturing a wide range of railtrack products such as track maintenance equipment , conductor rails , insulators , rigid catenary systems, fasteners, ballastless track … our staple products being rail welding with the alumino thermic ( at ) method or electric flash butt welding
拉伊臺克國際有限公司是一家製造多種鐵道產品的專業化公司,產品包括鐵路養護設備、導電軌、絕緣子、剛性接觸網系統、扣件、無渣道床、等等… ,其中的主導產品是鋼軌鋁熱焊及閃光對接焊產品。Corrosion resistance of nickel - base alloy spray welding layers after undergoing weld thermal cycle
帶噴焊層鋼管焊接接頭熱影響區耐蝕性能的研究It is a dozen metals in one ; now almost diamond - hard - - and again almost as soft as copper ; here brittle as glass ? there malleable1o as silver ; now welding quite readily - - again, very difficult to weld ; melting rather easily - - at other times difficult to diffuse ; usually very magnetic - - and : again almost non - magnetic ; an excellent conductor of heat and electricity - - and at times stubbornly resistant to both
鐵將十多種金屬特性合而為一:時而幾乎堅硬如金剛石,時而又柔軟如銅;此處易碎如玻璃,彼處又可展延如銀;時而很容易焊接,時而又很難焊合;有時相當易熔,有時又極難擴散;通常情況下富有磁性,但有時又幾乎磁性全無;本是熱和電的優良導體,但有時卻頑強地抗拒二者。The thermoelectric power outputs of laminated structures with various thermoelectric materials have been mathematically optimized and experimentally measured. some conclusions have been drawn in the present work as follows : 1. the performance, microstructures and the failure mechanism of laminated bi2te3 / fesi2 prepared by dip coating using tin - based alloys as bridge materials have been investigated
本項研究獲得了以下主要成果: 1 、以sn基合金為焊接材料,採用熱浸焊技術制備了bi _ 2te _ 3 / fesi _ 2疊層熱電材料,並系統地分析研究了疊層熱電材料的性能,焊接過渡層的微觀組織結構以及過渡層在熱加工及模擬服役過程中的破壞機制。By vacuum - electron - beam weld of ti3al and tc11 the technology of hot die forging, and then use different heat treatments, study the influence law of the different degree of deform, different heat treatments to the microstructure and properties
採用熱模鍛技術,通過對tac - 1b 、 tc11進行不同程度的變形、真空電子束焊接,然後採用不同的熱處理工藝,研究熱加工工藝對合金組織,性能的影響規律。Recently, train is running faster and faster, and considering the stability and security, seamless welded rails ( swr ) are used as the train orbits gradually. the temperature of the rails will vary with weather. so that the rails may release the energy due to the metal characteristic of expanding or contracting with temperature, there is some badly distortion in the swr, worsly occurring accidents on expanding orbits. the portrait thermal stress ( pts ) of the swr should be monitored in some parts regularly, as to avoid such accident
近年來,隨著火車的提速造成的穩定和安全問題,軌道逐步轉為採用無縫焊接鋼軌,隨著鋼軌溫度的變化,無縫鋼軌可能會因為熱脹或冷縮的金屬特性並且在扣件阻力小而且路基較差的路段釋放能量,可能會發生鋼軌嚴重變形,更甚者會發生脹軌跑道等嚴重鐵道事故,為了避免發生如此事故,有必要定期對鋼軌的溫度應力進行檢測。In view of theproperties of infrared thermal images, narrow - range zero - crossing edge detection method was applied to detect the edges of welding flaws and good results were obtained
針對紅外熱圖象的灰度特性,提出了窄范圍二階導數過零邊緣檢測用於焊接缺陷的邊緣提取,獲得了較好的效果。The necessarily of post - weld heat treatment of spherical tanks was emphasized
強調了焊接球罐焊后熱處理的必要性。Wdl is a certain steel which has lower sensitivity to weld cold crack and need not or a little warm - up before weld
國產wdl鋼種是一種對焊接冷裂紋敏感性低、焊接前不要預熱或稍加預熱而不產生焊接冷裂紋的鋼板。For more years, the welded members of steel structure are more popular than the rolled ones in china, but as is well known, the mechanical performance of welded members are effected by many factors : such as the material property of plates, the heat effect during welding process, the residual stress, the weld techniques and so on
一直以來我國使用的鋼結構構件以焊接為主,軋制的較少。眾所周知,焊接構件的力學性能將受諸多因素的影響,如焊接板材的材性是否一樣、焊接產生的熱影響以及焊接殘余應力和焊接工藝等。According to these, the paper put forward some countermeasures : select low carbon steel or low metal alloy steel with lower intensity, like 20r steel ; while welding, adopt strict craft measures with lower welding heat to input ; after jointing, proceed the whole hot dissolving on time ; control each welding joint with hardness hb 185 ; add 0. 25 % water into the liquid ammonia as decay eclipse ; enhance checking in operation, repairing equipment in time through regular interior and exterior checking
針對上述原因提出了防止氨冷器類臨氨壓力容器產生應力腐蝕裂紋的對策:選用強度稍低,但抗裂性較好的低碳鋼和低合金鋼,如用20r鋼製造;焊接時應採用嚴格的工藝措施和較低的焊接熱輸入量;焊后應及時進行整體消除應力熱處理;控制焊接接頭各區硬度hb 185 ;在液氨中添加0 . 25 %的水作為緩蝕劑;在運行中加強檢查,及時進行停車檢修時的內外部檢查和定期檢驗。Good corrosion resistant, heat - resistant, high - temperature resistant and antioxidizing in high - temperature, very good mal lea bil i ty and weldability
具有良好的耐蝕性、耐熱性,高溫強度及高溫抗氧性能良好,加工性、焊接性能良好。Tp - 56b, resistance to soldering heat test procedure for electrical connectors and sockets
電氣連接器和插座的tp - 56b耐焊接性加熱試驗過程分享友人