Method for determination of threshold stress intensity factors and fatigue crack growth rates in metallic materials
金屬材料的閾限應力強度因子和疲勞裂紋增長率的測定方法There is a slight drop of the fcpr when the specimen s thickness increases. however, the thickness of the specimen exerts a great influence on kth and fatigue life ( n ) : the thicker specimen is, the higher fatigue life ( n ) becomes, and the greater kth shows. under control of the same conditions, the fcpr of am50 is not so high as that of az91. there are some correlations between load ratio ( r ) and the fatigue surface : when load ratio becomes great, small flat surfaces increase while dimples decrease
試樣厚度增大,穩態裂紋擴展速率略有減小。但是,試樣厚度影響試樣的疲勞壽命和門檻值:試樣越厚,疲勞壽命越長,門檻值越大;在試樣尺寸和加載條件相同的情況下, am50的疲勞裂紋擴展速率較az91小,疲勞壽命則比az91長。載荷比r影響試樣的斷口形貌:載荷比r越大,對應相同k值出的斷口小平面越多,韌窩越少。It was demonstrated that the values of domain strain decreased while the rate in reduction of the domain strain lowered with larger n. combined the xrd with sem results, the non - fracture mechanism of the sample when pure electric fatigue was applied can be described as : at an earlier stage of electric fatigue, the high repeated incompatible strain led the major fracture mode for the fatigued sample to be of inter - granular. the ability of domain switching in a - - > c of the sample along with the direction of an applied electric field kept dropping, hence, reduced the domain strain
結合xrd和sem觀測,提出了純電疲勞作用下試樣不會發生斷裂的機理:電疲勞初始階段,試樣中的非協調高應變導致沿晶微裂紋,隨著微裂紋的增加,使得試樣沿外電場方向發生a c疇的能力不斷降低,從而導致疇變應變減小,當應變減小到一定程度時,將不足以在試樣中引起新的微裂紋或使原有微裂紋繼續伸長。