  1. The result of experiment shows that und er the conditions of proper ai r - entraining, concrete with 20 % fly ash has excellent frost - resistance. the frost - resistance of concrete with 55 % fly - ash which is admixed with united expansive agent ( uea ) has been improved greatly. the frost - resistance of sulfate aluminate cement concrete with high volume of fly - ash is dramatically lower than that of silicate cement concrete with the same volume of fly - ash

    試驗結果表明：粉煤灰摻量為20的混凝土在適量引氣的條件下具有良好的抗鹽凍性能；粉煤灰摻量為55的混凝土在摻加uea膨脹劑后其抗鹽凍性能有明顯改善；大摻量粉煤灰硫鋁酸鹽水泥混凝土的抗鹽凍性大大低於同摻量的硅酸鹽水泥混凝土。
  2. The investigation of a lot of parameters about treated sandstone, brick materials and earthen materials with fluorited polymers has been carried out, such as the formation of polymer, the penetration depth, porosity, capillary absorption and penetration coefficient, water uptake, compressive strength, drilling resistance, absorption isotherms of water vapor, water vapor diffusion, color changes as well as resistance to desegregation of water, frizzing - throwing cycles, worming - cooling cycles, and so on. in addition, the influence of salt crystallization, acid and base, and uv aging have also been assessed in order to better understand the protection effects and utilization possibility of two fluorinated polymers, mainly according to astm standard and the combination of international methods together with general technological

    分別以國家級文物保護單位的土質、砂巖和磚材文物樣品為對象，依據astm標準及國際通用文物保護研究方法與評估準則相結合，通過膠化物形成周期、滲透深度、孔隙度、毛細吸水和滲透系數、持水量、抗壓強度、抗鉆強度、吸附水蒸氣的能力、透氣性、外觀顏色等系列參數的測定，及凍融、冷熱循環、酸堿腐蝕后抗壓強度的衰減、可溶鹽對保護效果的影響、酸堿及光照對表面保護效果的影響，對兩種含氟聚合物及其與有機硅的共混物在文物加固保護和表面防護中的可行性和保護效果給予了系統研究。
  3. Abstract : the result of experiment shows that und er the conditions of proper ai r - entraining, concrete with 20 % fly ash has excellent frost - resistance. the frost - resistance of concrete with 55 % fly - ash which is admixed with united expansive agent ( uea ) has been improved greatly. the frost - resistance of sulfate aluminate cement concrete with high volume of fly - ash is dramatically lower than that of silicate cement concrete with the same volume of fly - ash

    文摘:試驗結果表明：粉煤灰摻量為20的混凝土在適量引氣的條件下具有良好的抗鹽凍性能；粉煤灰摻量為55的混凝土在摻加uea膨脹劑后其抗鹽凍性能有明顯改善；大摻量粉煤灰硫鋁酸鹽水泥混凝土的抗鹽凍性大大低於同摻量的硅酸鹽水泥混凝土。
  4. The paper discusses mechanism performance, durability and resistance to de - icing salt concrete, this kind of concrete is made with air - entraining agent or silica fume and used in the trial section construction of benxi - dandong freeway ' s charge square which is located in dandong

    本文通過在混凝土中摻入引氣劑或硅粉，來配製抗除冰鹽混凝土，並對其進行力學性能和耐久性測試，重點試驗其抵抗鹽凍能力，並用於本丹高速公路丹東段的收費廣場試驗路施工。
  5. 9 series pressure cavity is made of stainless steel single unit integration structure by processing so may guarantee for the better seal performance. the characteristic of product are no o - ring, no welded, no silicon oil or other organic, structural durability ; the most apply to pump and compressor, liquid pressure and pneumatic system, go - anywhere vehicle, energy and water processing system, pressure instrument, refrigerating equipment, agricultural machinery device, locomotive braking system

    9系列壓力腔採用不銹鋼單件一體式結構加工而成，因而可以保證較好的密封性能， 9系列產品的特點是無o形圈無焊縫無硅油或其它的有機物，經久耐用，主要應用於泵及壓縮機，液壓及氣動系統越野車能源及水處理系統壓力儀表冷凍設備農機設備機車剎車系統。
  6. The research of high performance pavement concrete ( hppc ) is done in two sides. one is mixture design, the other is pavement performance. the mixture design and design flowchart of hppc is given on the base of nc with the consideration of characteristic of both hppc and nc. the grow law, influencing factor and formation mechanism of hppc strength is analisised by perpendicular experiment. in the same, the fatigue equations are set up for hppc and hppc i on the base of fatigue experiment. the fatigue mechanism of hppc is analysised by damage mechanics and fracture mechanics. brittleness, frost resistance and abrasion resistance of hppc is researched with the camparition to nc i. at last, the economic analysis of hppc is done by two kinds of way

    結合高性能混凝土與普通路面混凝土的特點，提出了建立在普通路面混凝土基礎上的高性能路面混凝土配合比設計方法，給出了設計流程；通過正交試驗（強度試驗） ，分析了高性能路面混凝土的強度發展規律、影響因素與形成機理；同時，根據疲勞試驗結果採用雙參數weibull分佈模型分別建立了高性能路面混凝土和高性能路面混凝土（沒有摻加硅粉）疲勞方程，應用損傷力學和斷裂力學，分析了高性能路面混凝土的疲勞機理；並採用了對比分析方法，研究了高性能路面混凝土的脆性、抗凍性和耐磨性等。
  7. Methods of test for masonry units - determination of freeze - thaw resistance of calcium silicate masonry units

    圬工砌塊的試驗方法.硅酸鈣磚的耐凍融試驗
  8. At the same time fly ash and silica fume also can repress the anti - sulfate attack and the alkali - aggregate reaction ; in addition, the relation between air - entraining admi xture, cementitious materials quantity with freezing - thaw property of concrete were studied ; and according to the different affecting factors the durable life of concrete was estimated

    同時粉煤灰、硅灰還可以抑制硫酸鹽侵蝕及堿集料反應；此外，分析了混凝土中含氣量、膠凝材總量等與混凝土抗凍性的關系。並且，根據相應影響因素對混凝土耐久性壽命進行了預測。
  9. Pavlova viridis, isochrysis zhanjiangensis and isochrysis galbana 3011 were cryopreserved in liquid nitrogen using encapsulation - dehydration. algal cells in early stationary phase were encapsulated in 3 % ca - alginate beads with 30 nacl, 2 million cells in one bead. beads were desiccated with silica gel then directly immersed in liquid nitrogen. the cell viability after warming was evaluated by chlorophyll content. the main factors influencing the cell viability, such as water content of beads, dehydration rate, dehydration procedure, preculture and recovery methods after thawing were studied. the results are as follows : 1

    本文以綠色巴夫藻（ pavlovaviridis ） 、湛江等鞭金藻（ isochrysiszhanjiangensis ）和球等鞭金藻（ isochrysisgalbana3011 ）等三種餌料金藻為試驗材料，用包埋脫水法進行冰凍保存。選擇靜止初期的藻細胞包埋在含有30氯化鈉的3 %的褐藻酸鈣膠球中，細胞負載約200萬個細胞/膠球，經過硅膠吸濕法脫水后，探討了膠球含水量、脫水速率、脫水程序、預培養以及化凍后恢復方法對冰凍保存存活率的影響。
  10. The concrete ’ s anti - frozen can reflect concrete ’ s synthesis durability in the certain degree. this paper changed the former research mentality which enhanced concrete anti - frozen to use an extra material, aimed at the inner mongolian characteristic, utilized compound cement substituted ordinary portland cement, mixed the dula - fiber, the grade 2 inner mongolian pulverized coal ash, the extra material that was highly effective reduces the quantity of water outside the concrete to improve the concrete ’ s main performance, especially the concrete ’ s anti - frozen

    混凝土抗凍性在一定程度上能夠反映混凝土的綜合耐久性能，本論文改變以往提高混凝土抗凍性只採用一種外摻料的單一研究思路，針對內蒙古地區特點，運用復合水泥取代普通硅酸鹽水泥，在混凝土中摻入杜拉纖維、內蒙2級粉煤灰、荼系高效減水劑三種外摻料，來提高混凝土的主要性能，尤其是混凝土的抗凍性。
  11. Two - addition technique of flying ash and silica fume can meliorate durability of concrete ; air - entraining admixture possesses anti - freezing, descending ice point, and improving workability, and thereof it should be used in concrete. but controlling its dosage is very important to avoid strength loss

    發現粉煤灰和硅灰的雙摻技術能夠顯著改善混凝土的耐久性能，引氣劑具備防凍抗凍、抗滲及提高負溫混凝土工作性的優點，在負溫混凝土中應該加大使用范圍，但必須控制其摻量，確保強度損失較小。
  12. The good quality 425r silicate cement and 525 silicate cement, which are produced by the use of rotary kiln and up to the national standard gb175 - 92, are particularly suitable for the construction of buildings for civil use, airport, road, port, and dam because of its good early strength, quick condensation, good freeze and abrasive resistance, and low basicity content

    我公司出品的425r 525普通硅酸鹽水泥，系採用國濕法旋窯生產工藝，按國家標準gb175 - 92精心組織生產。具有早期強度高凝結硬化快抗凍性好耐磨性好含堿量低等特點，曾獲得福建省優質產品稱號。