Abstract : this article is about two series of borate and phosphate comprising seven directions. the experiment result shows that both of the two gl ass antioxidants can reduce apparent porosity , raise oxidation resistance and th e crushing strenth after fire , but lower refractoriness under load. phosphate glas s is superior to borate in refractoriness under load. which c an attain over 1600 ; so the phosphate glass is a d esirable antioxidant
文摘:研究了硼酸鹽和磷酸鹽兩個系列七種配方的玻璃防氧化劑,實驗表明這兩種玻璃防氧化劑均可降低鋁鎂碳磚的氣孔率,提高鋁鎂碳磚的抗氧化能力及燒后的耐壓強度,但也不同程度地降低了鋁鎂磚的高溫荷重軟化變形溫度,其中磷酸鹽玻璃優于硼酸鹽玻璃,其高溫荷重軟化變形溫度可達到1600以上,仍是可取的防氧化劑The reaction between the boron carbide and aluminum interface changes the properties of the composites during the post infiltration heat treatment
碳化硼與鋁界面的反應是熱處理改變碳化硼鋁復合材料性能的基礎。The researches indicate that after a heat treatment at high temperature ( 1700 ? ), the chemistry properties of the boron carbide surface are changed. the new boron carbide surface, react weaker with aluminum, thus a better infiltration can be achieved
碳化硼預制體經高溫預燒后,碳化硼表面化學狀態發生改變,預燒后形成的碳化硼新表面與鋁的反應活性降低,從而保證在本文工藝條件下浸滲過程的順利進行。Standard specification for nuclear - grade aluminum oxide - boron carbide composite pellets
核純級的氧化鋁碳化硼復合丸料的標準規范Standard test methods for chemical, mass spectrometric, and spectrochemical analysis of nuclear - grade aluminum oxide and aluminum oxide - boron carbide composite pellets
核純級的氧化鋁碳化硼復合丸的化學光譜和光譜化學分析的標準試驗方法In the process of alloy melt and infiltrate the boron carbide, reaction between the boron carbide and aluminum interface occur, the key of achieving a good interface bond is the control of the reaction between the boron carbide and aluminum interface
研究表明,在熔融鋁潤濕碳化硼預制體並向碳化硼預制體中浸滲的過程中,取得良好界面結合的關鍵是保證在預制體達到完全浸滲前不發生過度的界面反應。分享友人