magnesium aluminum phosphide-
The key products of the company are high alumina brick, fireclay brick, phosphate - bonded wearable brick, exfoliation - resistant high alumina brick, high refractoriness under load brick, corundum brick, magnesite brick, magnesite ? chrome brick, series of corundum, sic furnace chamber and pipe, ceramisite brick, corundum - mullite brick, corundum - chrome brick, sillimanite brick, magnesite alumina spinel brick, acid - resistant brick, alkali - resistant brick, zirconia - corundum brick, alumina bubble products, series thermal insulating refractory products, high alumina castable, corundum castable, corundum ramming, brown - corundunm castable, sic castable, low - cement castable, alkali ? resistant castable, light silica alumina products, stainless steel fibre reinforced castable, etc
主要產品有:高鋁質磚、粘土質磚、磷酸鹽耐磨磚、抗剝落磚、高荷軟磚、剛玉磚、碳化硅磚、鎂磚、鎂鉻磚、各種剛玉、 sic爐膛、爐管製品、陶粒磚、剛玉莫來石磚、鉻剛玉磚、硅線石磚、鎂鉻尖晶石磚、耐酸磚、耐堿磚、鋯剛玉磚、氧化鋁空心球製品及各種輕質保溫材料、高鋁質澆注料和剛玉澆注料、搗打料、棕剛玉澆注料、碳化硅澆注料,低水泥澆注料、抗堿性澆注料、輕質硅酸鋁製品、鋼纖維增強澆注料等80餘種系列耐火材料。Abstract : this article is about two series of borate and phosphate comprising seven directions. the experiment result shows that both of the two gl ass antioxidants can reduce apparent porosity , raise oxidation resistance and th e crushing strenth after fire , but lower refractoriness under load. phosphate glas s is superior to borate in refractoriness under load. which c an attain over 1600 ; so the phosphate glass is a d esirable antioxidant
文摘:研究了硼酸鹽和磷酸鹽兩個系列七種配方的玻璃防氧化劑,實驗表明這兩種玻璃防氧化劑均可降低鋁鎂碳磚的氣孔率,提高鋁鎂碳磚的抗氧化能力及燒后的耐壓強度,但也不同程度地降低了鋁鎂磚的高溫荷重軟化變形溫度,其中磷酸鹽玻璃優于硼酸鹽玻璃,其高溫荷重軟化變形溫度可達到1600以上,仍是可取的防氧化劑The results show that : the fillers of sio2 based investment consist of sio2, al2o3 and mgo, and the binder is nh4h2po4 for sio2 based investment, the bulk density and the compression strength decrease, the apparent porosity and the thermal expansion increase, when the specimens are heated to 900 ; the fillers of al2o3 based investment consist of al2o3 and mgo, and the binder is nh4h2po4 ; for al2o3 based investment, the bulk density decreases and the apparent porosity increases when the specimens are heated to 900 ; the fillers of mgo based investment consist of mgo and al2o3, and the binder is ca cement ; for mgo based investment, the compression strength decreases and the thermal expansion increases greatly when the specimens are heated to 900
結果表明:氧化硅系包埋料的骨料是氧化硅、氧化鋁、氧化鎂,結合劑為磷酸二氫銨,其900鍛燒后顯氣孔率增加,體積密度下降,耐壓強度降低,熱膨脹增大;氧化鋁系包埋料的骨料是氧化鋁和氧化鎂,結合劑為磷酸二氫銨,其900燒后顯氣孔率增加,體積密度下降,熱膨脹變化不大;氧化鎂系包埋料的骨料是氧化鎂和氧化鋁,結合劑是鋁酸鈣水泥,其900燒后耐壓強度明顯降低,熱膨脹明顯增大。
分享友人