礦渣混合物 的英文怎麼說
中文拼音 [kuàngzhāhúngěwù]
礦渣混合物
英文
slag mix- 礦 : 名詞1. (礦床) ore [mineral] deposit 2. (礦石) ore 3. (開采礦物的場所) mine
- 渣 : 名詞1 (渣滓) dregs; residue; sediment:煤渣coal cinder; 殘渣 dregs; 豆腐渣 soya bean residue; 豬...
- 混 : 混形容詞1. (渾濁) muddy; turbid2. (糊塗; 不明事理) foolish; stupid
- 合 : 合量詞(容量單位) ge, a unit of dry measure for grain (=1 decilitre)
- 物 : 名詞1 (東西) thing; matter; object 2 (指自己以外的人或與己相對的環境) other people; the outsi...
- 混合物 : mixture; compound; mix; varia; intermixture; hodge poadge; miscellany; impurity; mix up admixture...
- 混合 : (攙雜在一起) mix; blend; mingle; admix; mixture; mix up; interfusion; commixture; blending; cre...
-
It focuses on the theory of the mineral functional materials " improving the anti - chloride permeability and the chloride binding. the main achievements of this article include : 1 ) use the technology of xrd, sem, bet, laser particle size distributor etc to test the component, the construction, particle size distributor, specific surface etc of micro - silica, ultra - fined slag, high quality fly ash, meta - kaolin clay, four types of the mineral functional material, theoretically analysis the functions which the four mineral functional minerals act on cement concrete, namely pozzolanicity effect, filling effect, micro - aggregate effect, surface adsorption effect and so bring into play the affect of plastification, lowing of temperature, reinforcement, improvement of durability. base on this analysis we can conclude that the proper diameter of the mineral functional material is 5 m - 15 m, that is blain fineness 4500cm2 / g - 7500cm2 / g
本論文的主要成果包括以下幾個方面: ( 1 )採用xrd 、 sem 、 bet 、激光粒度分析儀等多種測試手段,探明了以硅灰,超細磨粒化高爐礦渣,優質粉煤灰及偏高嶺土超細粉等4種超細礦物功能材料的組成、結構、粒度分佈、比表面積等基本性質;從理論上分析了礦物功能材料在混凝土中的4種效應,即火山灰效應、填充密實效應、微集料效應、表面吸附效應,並由此發揮出增塑、溫峰削減(降熱) ,增強及耐久性改善等作用;通過相關理論分析,推導出礦物功能材料的合理粒徑范圍在5 m 15 m ,即勃氏比表面積為4500cm ~ 2 g 7500cm ~ 2 g 。The paper introduced in brief the basic chemical and mineral component, and analysed the effect and the evaluation index of the chemical component, vitreous body quantity and structure and the fineness degree of the phosphorus slag on its chemical activity, and finally, discussed the effect of phosphorus slag as additive on cement hydration property and the micro structure of the harding body
摘要簡要介紹了磷渣的基本組成,包括化學組成和礦物組成;分析了磷渣的化學成分、玻璃體數量和結構、磷渣細度對其化學活性影響及其評價指標;探討了磷渣用作水泥混合材對漿體水化性能和硬化體微觀結構的影響等。The scc has the following advantages : remarkably reducing the noisy pollution and the worker s labor intensity in construction, deducing the rough surface or segregation because of missing - vibration or excessive - vibration in conventional construction, resolving the quality - defect problems resulting from lacking - vibration in the section of complex shapes and densely - packed reinforcement area. at the same time, large of industrial solid waste such as fly ash and blast furnace slag is utilized in the proportioning of scc. it is helpful in comprehensive utilization of resource and environment protection, so the scc belongs to " green concrete ", it is a branch of hpc which will be developed in the future
這種混凝土可以顯著降低混凝土施工中的噪音污染;大幅度減輕工人的勞動強度;減少傳統混凝土施工中因漏振或過振造成的麻面或離析;解決了配筋密集、結構復雜部位因振搗不足而造成的質量缺陷問題;同時,由於自密實混凝土在配製中,大量利用粉煤灰、高爐礦渣等工業固體廢棄物,有利於資源的綜合利用和生態環境的保護;從而被譽為「綠色混凝土」 ,是未來混凝土向高性能發展的方向之一。Abstract : during construction of the capital international airport ' s garage building project, the c50 and over c60 high performance concrete has been adopted for its construction. for the aim of 1, to get a maximum reduction of cement comsumption 2, to lower the concrete ' s hydration heat 3, to reduce concrete ' s shrinkage and cracks, and 4, to promote concrete ' s performance, a high quality chilled blast furnace superfine slag has been adopted as an admixture. furthermore, the adoption of some other minerals as the admixtures to get a high performance concrete has been carried out. as a result, these procedures and operations would have developed considerably the potential activity of concrete, and eventually the multiple performance and multiple function of concrete would have been improved and promoted. in conclusion a good result has been achieved in practice
文摘:首都國際機場停車樓工程中,採用c50及c60以上高性能混凝土,為最大限度減少水泥用量,降低水化熱,減少收縮與裂縫,提高混凝土的性能,優選了有效成分含量高、質量好的水淬高爐礦渣磨細后單獨摻用,或再與其他礦物組分復合作為高性能混凝土的摻合料,以充分發揮礦渣的潛在活性,從而使混凝土的多項性能得到極大的改善和提高,並在實際應用中取得了良好的效果。During construction of the capital international airport ' s garage building project, the c50 and over c60 high performance concrete has been adopted for its construction. for the aim of 1, to get a maximum reduction of cement comsumption 2, to lower the concrete ' s hydration heat 3, to reduce concrete ' s shrinkage and cracks, and 4, to promote concrete ' s performance, a high quality chilled blast furnace superfine slag has been adopted as an admixture. furthermore, the adoption of some other minerals as the admixtures to get a high performance concrete has been carried out. as a result, these procedures and operations would have developed considerably the potential activity of concrete, and eventually the multiple performance and multiple function of concrete would have been improved and promoted. in conclusion a good result has been achieved in practice
首都國際機場停車樓工程中,採用c50及c60以上高性能混凝土,為最大限度減少水泥用量,降低水化熱,減少收縮與裂縫,提高混凝土的性能,優選了有效成分含量高、質量好的水淬高爐礦渣磨細后單獨摻用,或再與其他礦物組分復合作為高性能混凝土的摻合料,以充分發揮礦渣的潛在活性,從而使混凝土的多項性能得到極大的改善和提高,並在實際應用中取得了良好的效果。From the research on hpec we can know that expansion property of high strength superplasticized expansive concrete shows obvious particularity compared with ordinary expansive concrete. when bfs is not put in, high strength superplasticized expansive concrete shows autogenous shrinkage in 1 day standard curing. and in 14 day ' s age e2 is less than half of middle strength superplasticized expansive concrete ' s with same csa dosage, and this shows expansion effect is confined more
對hpec混凝土的研究發現,與普通膨脹混凝土相比,高強流態膨脹混凝土的膨脹性能表現出明顯的特殊性,在不摻超細礦物質摻合料(磨細礦渣)時,高強流態膨脹混凝土標準養護1天時出現自收縮, 14天時其限制膨脹率不到相同csa摻量的中強流態膨脹混凝土限制膨脹率的一半,表現為膨脹效應受到更大限制。By research the effect of mineral mixture on cement and admixture, we can improve it ' s utility in cement concrete. in this article we use the slag and fly ash as research object. we study the effect of the mineral " s dosage on the compability of different fineness cement and admixture, the effect of mineral fineness to the compatibility of cement and admixture. wo also research the effect of mineral to different cement and admixture in chongqing. by the study, we continue changing the character of mineral to improve it ' s effect to compatibility. slag and fly ash mix each other can have better character to the compatibility of cement and admixture. changing slag by admixture and gypsm also can improve it ' s compatibility to cement and admixture
礦物摻合料對水泥與不同摻量的外加劑之間的相容性影響。並結合重慶市現有的資源,研究了礦物摻合料對重慶地區不同廠家的水泥與外加劑的相容性影響。進而對礦物料的缺陷進行改善,採用礦渣與粉煤灰混摻,膨脹劑與礦渣混摻,礦渣與石膏,礦渣與外加劑混磨,優化礦物摻合料,更好的促使其在重慶市水泥混凝土中的應用。This paper analyses the problem of concrete cracking and leakage, and set up the model of the middle or low - strength steel slag anti - cracking and impermeable concrete ( acic ) on the base of the analysis. the four principles of water permeable resistance character, volume stability character, toughness and anti - chemical corroded character have been put forward for raw materials selection and durability design of acic, acic is designed by the theory of composite material and the theory of fiber - reinforced, and two series of acic, such as fly ash series and steel slag series, have been manufactured by means of mineral admixture, hybrid fiber and chemical admixture. hydrating heat, macro - mechanics quality, durability and microstructure of the acic have been researched
本文對中低標號大體積混凝土滲透開裂問題進行了研究,從混凝土自身結構形成與經濟角度指出大摻量粉煤灰與膨脹劑復合配製大體積混凝土的問題所在,提出採用鋼渣微細礦粉配製中低標號防滲抗裂混凝土的思路,運用復合材料理論設計中低標號防滲抗裂混凝土,提出了低水化熱、抗滲性能、體積穩定性、韌性和抗沖磨性能是中低標號防滲抗裂混凝土材料選擇和耐久性設計的主要原則,採用鋼渣微細粉復合混雜纖維、化學外加劑的技術路線,配製了適合於深水等特殊環境中的大體積中低標號鋼渣系列防滲抗裂混凝土,對其進行水化特性、宏觀物理力學性能、耐久性和微觀結構研究。The result indicated that, mix the mineral mixture of fly ash, flag into concrete can optimize the concrete pore structure, improve the concrete compressive strength and impermeability, and along with the age increment the improvement become more obviously ; after saturated freezing and thawing, the concrete pore structure changed apparently, total porosity increased, macro porous quantity rapid increased, small pore quantity reduced, mean radius and most probable aperture increased ; and the more saturated degree, the more obviously destructive effect
研究表明:在混凝土中摻加粉煤灰、礦渣等礦物摻合料優化了混凝土的孔結構,提高了混凝土的抗壓強度和抗滲性能,且隨齡期的延長這種改善作用更加明顯;飽水凍融后混凝土的孔結構變化明顯,總孔隙率增加,大孔數量急劇增大,小孔數量減小,平均孔徑和最可幾孔徑增大;且飽水程度越大,這種破壞作用越明顯。分享友人