粗晶組織 的英文怎麼說

中文拼音 [cūjīngzǔzhī]
粗晶組織 英文
coarse structure
  • 粗 : Ⅰ形容詞1 （長條東西直徑大的） wide （in diameter）; thick 2 （長條東西兩長邊的距離寬的） wide （i...
  • 晶 : Ⅰ形容詞（光亮） brilliant; glittering Ⅱ名詞1. （水晶） quartz; （rock） crystal 2. （晶體） any crystalline substance
  • 組 : Ⅰ名詞1 （由不多的人員組成的單位） group 2 （姓氏） a surname Ⅱ動詞（組織） organize; form Ⅲ量詞（...
  • 織 : 動詞（編織） knit; weave
  • 組織 : 1 （組織系統） organization; organized system 2 （組成） organize; form 3 [紡織] weave 4 [醫學] [...
  1. Influenced by the alternating current field, all of the eutectic microstructure of al - 20si - 5fe - ti alloy changed into very small particles which is well - distributed on the base of a - al. electromagnetic stirring stimulates the forming of equiaxed crystal in al - 20si - 5fe - mn alloy. primary iron - phase is transformed from thick needle into smooth block

    電磁攪拌促進al - 20si - 5fe - xmn合金中等軸晶的生成，初生富鐵相由原來粗厚的片狀物轉化成比較圓整的塊狀，共晶組織中鐵相主要以較短的針片狀存在。
  2. It is indicated after laser remelting, the density of the nano material infiltrated coating is improved and grain size is decreased greatly. in above researches, it is found that the nano material is distributed among general material grains to form inter - granular structure of the coating

    研究發現，在各種塗層中納米顆粒明顯填充在粗顆粒間，構成晶間型組織結構；初步測試還表明，在al _ 2o _ 3 + 13 wt
  3. Microstructure and toughness of welding coarse - grain heat affected zone in ti - v - nb microalloy pipeline steel

    微合金管線鋼焊接粗晶區組織及韌性
  4. The results show that the carbon / carbon composites with rough lamina have preferred orientation, higher anisotropy and graphitization degree than the carbon / carbon composites with smooth lamina

    結果表明：具有粗糙層熱解炭的炭炭剎車副由於其晶格結構較為完善，生長組織擇優取向度和各向異性度均高於含有光滑層結構熱解炭的炭炭剎車副。
  5. The fractue experimental research of maraging 350 torsional rods

    大型連桿分模面混晶及粗晶魏氏組織
  6. 3. simpler microstructure and mechanical properties classification criterions have been established. if f1 3. 8, the grains must be large grains ; if 0 f1 < 3. 8, the grains must be medium grains ; if f1 < 0, the grains must be fine grains

    由新的表徵變量建立了更簡單明確的顯微結構和力學性能分類準則：當f _ 1 3 . 8 ，則為粗大晶粒組織；當0 f _ 1 3 . 8 ，則為中等晶粒組織；當f _ 1 0 ，則為細晶粒組織。
  7. The network carbide and acicular martensites that existed in the microstructure of the root grooves of the spline due to improper carburating and quenching process of the shafts, led to the initiation and propagation of the intergranular microcracks and were the main reason that caused the early fracture of the shafts

    由於滲碳淬火工藝不當，在二軸花鍵槽根部的組織中產生了網狀破化物和粗大的針狀馬氏體，在外力作用下形成沿晶顯微裂紋並擴展，是導致二軸疲勞斷裂的主要原因。
  8. The mechanisms of the defects forming are discussed and the improving measurements of quality of laser beam welding al - fe - v - si aluminum alloy are pointed out

    激光焊接的al - fe - v - si耐熱鋁合金，焊接區域存在粗大的枝晶組織和焊接氣孔。