And the value drop to the lowest at ph = 0. 8. as the increase of heat treatment temperature, the pore size distribution peak of sio2 microspheres is very narrow, meanwhile the specific surface area is the smallest before 160 c. the polymer template is removed at 350 c, so the pore structure of sio2 particles has a big change which involve the increase of specific surface area and the broaden of pore size distribution peak. with the continuous raise of temperature the sio2 network will shrink little, as a result the average pore size will decrease, but the specific surface area has no obvious change
結果發現:
二氧化硅膠體顆粒均勻分佈於
脲醛聚合物網路中,煅燒去除有機模板后微球表面變粗糙,而粒徑沒有明顯變化; ph值較小時,復合微球中聚合物含量較大,而ph值較大時,得到復合微球結構鬆散,因此熱處理后的
二氧化硅微球孔容及平均孔徑都較大,而在ph = 0 . 8時,得到最小值;武漢理工大學碩士學位論文隨著熱處理溫度的變化,小於160時,空分佈較窄,而比表面積較小,在350時,由於有機模板的去除,微球孔結構發生突變,比表面積明顯增大,而孔徑分佈變寬,溫度繼續升高時,
二氧化硅網路發生收
縮,平均孔徑變小而比表面積由於有機炭化物的完全去除沒有太大變化;微球中的微孔在熱處理過程中處于平衡狀態,分佈沒有太大變化。
Puyang puzhong chemical co., ltd is mainly produces carboxymethyl cellulose and thiourea dioxide and auxiliary agent of petroleum. it was founded in 1998, and today, it has developed into a high - tech non - government cooperation combined with researching, producing marketing. our company has advanced equipments, technicals and management. at the same time, . we also owns the operation right of import export business
濮陽市濮中化工有限公司創建於1998年,是從事羧甲基纖維素鈉carboxymethyl cellulose英文縮寫「 cmc 」二氧化硫脲thiourea dioxide油田助劑等集科研開發生產製造市場營銷為一體的高科技民營企業。