Results show that : ( 1 ) for each particle size of andalusite, variation tendency of the properties of the material is generally the same : the maximum of bulk density, compressive strength and rupture strength appears in the range of 5 % - 10 % content of fiber, these properties of the material remarkably decrease as the fiber content exceed 10 % ; while at the same fiber content, the properties of the material increase with the increase of firing temperature
結果表明: ( 1 )對于不同粒度的原料,性能變化規律大致相同:在同一燒成溫度下,體積密度、常溫耐壓強度、常溫抗折強度在5 10之間出現峰值,加入量超過10之後材料的性能明顯下降;在相同的纖維含量下,隨著燒成溫度的提高,試樣的各項性能均有所上升。When the alumina fiber accounted for 10 %, the density of the composites was chiefly high and the fiber evulsion effect was reinforced ; when the alumina fiber accounted for 30 %, the fiber evulsion effect, fracture and bridge - connection effect were mainly strengthened, when the fiber proportion was 50 %, at the temperature of 1500 c, the bending strength reached 26. 11 mpa while the compressive strength was 79. 30 mpa
氧化鋁纖維含量為10和30的試樣增強機理不同,含量為10時,復合材料以基質密實度高、纖維拔出效應增強為主;氧化鋁纖維含量為30時,復合材料以纖維拔出、斷裂、橋聯效應增強為主。當纖維含量為50時,在1500下燒成,其抗折強度達到26 . 11mpa ,耐壓強度達到79 . 30mpa ,該復合材料可用作輕質保溫材料。Effects of the content of fiber, vesicant, pore ratio and pore diameter were investigated, the results indicates the variables have great effects on the sound absorbing performance of the samples
實驗發現,孔隙率、平均孔徑大小、玻璃纖維含量、發氣劑含量對材料吸聲性能有顯著影響。We also studied the dynamic characteristics of cf / cu ( c ) - cu composites, the results show that, by the method of graphite is coated with copper, the coefficient of friction and the wear rates remarkably decreased. with the increase of the copper coated carbon fiber content, the wear rates of cf / cu ( c ) - cu composites is notably decreased, while the coefficient of friction is increased. with the increase of electric current density, the wear rate of cf / cu ( c ) - cu composites is increased
研究發現,碳纖維鍍銅石墨-銅復合材料的電摩擦磨損性能與碳纖維含量存在一最佳值,當碳纖維含量為0 . 6時,其電摩擦磨損性能最好;對于不同電流密度下的電磨損性能的比較可以發現,通電磨損時的電摩擦系數要小於機械磨損時的摩擦系數,碳纖維鍍銅石墨-銅復合材料的電摩擦系數隨電流密度增大先減小而後增大,在電流密度為15a cm ~ 2時達到最小值;通電磨損量要遠大於機械磨損量,且隨著電流密度增大,磨損量增加。Using non - saturable polyester resin as its basal masal and unidirectional fiberglass woven fabrics as its skel eton, the frp pole is taken shape by ce - ntrifugal kr twine forming process and has high axial strength and its content if fiberglass is over 50 %. the frp light pole
Frp燈桿系採用不飽和聚酯樹脂為基材,以單向布為主的玻璃纖維織物為骨架,採用離必成型工藝或發纖維骨架通過纏繞成型工藝製作而成,玻璃纖維含量在家50 %以上,軸向強度很高。Textile - test method of elastane fibre content
紡織品氨綸產品纖維含量的實驗方法To increase the fibre content, you can add a small amount of brown rice in place of part of the white rice
若要進一步增加纖維含量,可以混入少量紅米來代替部份白米。High fiber length variation and immature fibers
纖維長度差異大和未成熟纖維含量高。Their infused dried fruits and vegetables, fridge - n - fresh vegetables, and soft - n - frozen fruit products are low in fat and calories, and high in fiber
他的浸漬乾果/浸漬蔬菜乾/軟凍果粒/鮮凍蔬菜產品都是低脂肪、低熱量、高纖維含量的健康食品,是當今關注健康的消費者的理想選擇。The approaches of enhancing the mechanical properties of ramie and flax composites were studied in this paper. the effects of surface pretreatment, fiber content, molding temperature and pressure as well as the effect of electron beam, microwave and ultrasonic wave on the mechanical properties of the composites were explored. the experimental results show that : 1
本文以苎麻、亞麻纖維為增強材料,線性低密度聚乙烯( lldpe )為基體,研製了兩種麻纖維層壓復合材料,研究了麻織物表面處理、纖維含量、成型溫度、成型壓力等對該復合材料力學性能的影響,得到了性能較為優異的麻纖維復合材料,探討了復合材料的增強機理。Test method for determination of wood fiber in asbestos cement
石棉水泥中木纖維含量的測定方法Standard test method for neps, vegetable matter, and colored fiber in wool top
羊毛條中毛結,植物性物質與有色纖維含量標準測試方法Standard test method for organic fiber content of asbestos - cement products
石棉水泥製品中有機纖維含量的標準試驗方法Precast concrete products - test method for glass - fibre reinforced cement - measuring the fibre content in fresh grc, ' wash out test '
預制混凝土製品.玻璃纖維增強水泥試驗方法.新鮮grc纖維含量的測量.沖刷試驗Compared with traditional cakes, the cakes containing peanut residue powder not only have the aroma of peanut but also increase the multifunctional dietary fiber and protein thus, the application of peanut residue in cakes provides an efficient way for peanut industry
研究結果表明:添加一定量的花生渣粉不僅使酥性糕點具有花生香味,而且增加了膳食纖維含量,大大提高了產品的營養價值。Sprinkle a spoonful of bran onto the stew to increase the fibre content
往燉煮的食物上加一匙麥麩,以增加其纖維含量。This paper mainly study two kinds of smart materials which are both reinforced by chopped carbon fiber mat but use two different kinds of polyester resin as matrix and discuss the influence of content of carbon fiber on conductivity. focus on the relationship between strain and volume resistivity under tensile condition influenced by the factors such as resin matrix and fiber content
研究了其含量與導電性之間的關系;重點對不同基體樹脂材料及不同碳纖維含量等因素對復合材料在單軸拉伸條件下,拉伸狀態下應變與體積電阻率之間的變化關系進行了研究;確定了電阻率與應變之間變化的數學關系。Silk as a high - mannose dietary fiber content of ordinary food, as long as a small amount of food every day, it can be conveniently enough dietary fiber volume, but will not affect other effective nutrient absorption and excretion through maintaining a good effect, the spirit of people more abundant
甘露絲作為一種高膳食纖維含量的普通食品,只要每天少量食用,就方便地能獲得足夠的膳食纖維量,同時不會影響其他有效營養素的吸收,並且通過保持良好的排泄效果,使人精神更加充沛。Standard test method for overlength fiber content of man - made staple fiber
人造短纖維中超長纖維含量的標準測試方法Methods for analysis of animal feeding stuffs - determination of crude fibre content - method with intermediate filtration
動物飼料分析方法.粗纖維含量的測定.中間過濾法分享友人