In this paper, the effects of fly ash, cement, lime, fine sands, foam agent, w / c ratio and additional agent on foamed concrete were studied by experiments, the best combination ratio of fly ash foamed concrete whose density varies from 551kg / m3 to 650kg / m3 was obtained through orthogonal test design, the foam agent quantity and the fly ash quantity effect the fly ash foamed concrete greatly, so the author selected them as independents to establish duality linear regression equations, the equations were quite ideal through the test of model summary r. moreover, the author also did some experiments about the water resistance of magnesium oxychloride cement fly ash foamed concrete, the outcome showed that phosphoric acid has good effect on water resistance, and its appropriate quantity was found
本文通過試驗研究了粉煤灰、水泥、石灰、細砂、發泡液、水灰比及外加劑對粉煤灰發泡混凝土性能的影響，採用正交設計試驗方法得出了600級粉煤灰發泡混凝土的最佳配合比，同時發現發泡液和粉煤灰摻量對發泡混凝土的影響最為顯著，因此，以二者為自變量建立了二元線性回歸方程，通過全相關系數的檢驗發現方程較為理想。此外，還對氯氧鎂水泥基粉煤灰發泡混凝土的耐水性進行了相關實驗，發現磷酸有較好的耐水性效果，同時找到了其合適的摻量范圍。The concrete ’ s anti - frozen can reflect concrete ’ s synthesis durability in the certain degree. this paper changed the former research mentality which enhanced concrete anti - frozen to use an extra material, aimed at the inner mongolian characteristic, utilized compound cement substituted ordinary portland cement, mixed the dula - fiber, the grade 2 inner mongolian pulverized coal ash, the extra material that was highly effective reduces the quantity of water outside the concrete to improve the concrete ’ s main performance, especially the concrete ’ s anti - frozen
混凝土抗凍性在一定程度上能夠反映混凝土的綜合耐久性能，本論文改變以往提高混凝土抗凍性只採用一種外摻料的單一研究思路，針對內蒙古地區特點，運用復合水泥取代普通硅酸鹽水泥，在混凝土中摻入杜拉纖維、內蒙2級粉煤灰、荼系高效減水劑三種外摻料，來提高混凝土的主要性能，尤其是混凝土的抗凍性。
分享友人