脆斷 的英文怎麼說

中文拼音 [cuìduàn]
脆斷 英文
brittle failure
  • 脆 : 形容詞1 （容易折斷破碎） fragile; brittle 2 （較硬的食物容易弄碎弄裂） crisp 3 （聲音清脆） （of ...
  • 斷 : Ⅰ動詞1 （分成段） break; snap 2 （斷絕;隔斷） break off; cut off; stop 3 （戒除） give up; abstai...
  1. Within the dark woods the liquid silver voices of the birds called unceasing.

    黑暗的樹林里不斷傳出行雲流水般的清脆鳥語聲。
  2. It can be seen from the results that the control beam had good plastic property in the static failure experiment after two million fatigue loading circles. all specimens with corroded main bars were failure under the fatigue loads within one million fatigue circles. fatigue lifespan of reinforced concrete beam was sharply shortened after main bars corroded in it and the beam was destroyed bristly without any prediction

    試驗結果表明，振動測試不能夠對銹蝕鋼筋混凝土梁的疲勞破壞做出可靠的預測;對比梁在經過200萬次疲勞循環加載后的靜力試驗中仍表現出良好的延性破壞特徵;銹蝕梁在100萬次疲勞循環內均因主筋疲勞斷裂而破壞;主筋銹蝕使得梁的疲勞壽命急劇縮短;梁發生脆性破壞而沒有徵兆。
  3. Crazing is the invariable precursor of brittle fracture.

    出現小裂紋必然是脆性斷裂的前兆。
  4. Analysis on the causes of no yield point in tension and brittle fracture in cold bending of 20mnsi hrb

    熱軋帶肋鋼筋冷彎脆斷和無屈服點原因分析
  5. Abstract : by means of metallographical examination and sem, the microstructure characteristics, macro - and microfractographs of the brittle broken wheel hull bolt of bj212 automobile have been studied. the results show that the thin - headed screw, with excessively deep carbonitriding layer and hardening layer, has less resistance to brittle fracture in the thin area of its head. at the root of the head connecting the stem, a tensile stress may emerge owing to the non - even quenching stress. those are the two reasons for low torque fracture of bolt

    文摘:藉助金相、掃描電鏡等手段對低扭矩脆斷的bj212汽車輪殼螺栓的金相組織特徵，宏觀和微觀斷口形貌等進行了研究，結果表明：這種頭部薄的螺栓，滲層和淬透層過深，使頭部薄區脆斷抗力降低，在頭部與桿的根部，由於淬火應力不均勻導致根部產生拉應力，均是導致螺栓低扭矩斷裂的原因。
  6. The brittle fracture of steel columns and the damage to column bases were found in kobe earthquake

    在阪神地震中還發生了鋼柱的脆斷和柱腳的破壞。
  7. Brittleness mechanism and fracture characteristics of yus701 au stenitic stainless steel rof internal cover

    內罩的脆斷特徵及脆化機理
  8. Brittle fracture criterion for mixed - type of sharp v - notch

    形切口脆斷準則
  9. Study on the brittle fracture mechanism of crwmn nail die by composite treatment

    制釘模脆斷機理研究
  10. Three kinds of fracture facet of a high nitrogen bearing austenitic steel in low temperature brittle fracture

    高氮奧氏體鋼低溫脆斷中的三種斷裂刻面
  11. The fracture of ct20 alloy was of plastic dimples character at rt, while some holes and cleavage appeared at 20k, showing some brittle feature

    Ct20合金室溫拉伸斷口以塑性韌窩為主要特徵， 20k拉伸時斷口上出現了一些孔洞和解理臺階，表現出一定的低溫脆斷特徵。
  12. The results shows that the failure parts has high silicon content and uneven hardness, the impact toughness and elongation is far below the specification of the material

    結果發現，失效件的硅含量偏高、硬度值很不均勻，沖擊韌度和伸長率遠低於材質要求，因而導致脆斷。
  13. With the decreasing of heterogeneity, the main failure process presents brittle behavior, and vice versa, with the increasing of heterogeneity, failure process presents ductile behavior

    隨著非均勻程度的降低，主破裂呈現脆斷模式，而隨著非均勻程度的增加而呈現韌性破壞特徵。
  14. With carbon content increasing, the carbide network on the fertile grain boundary sprouting and propagating. the fracture mode has been changed from cleavage to along boundary and the intergranular corrosion induced by solution chromium decreasing

    隨碳含量提高，晶界上碳化物萌發、擴展呈網狀，鑄件脆斷由解理斷裂發展為沿晶斷裂，同時鐵素體不銹鋼晶間腐蝕傾向增大。
  15. Testing of high - strength steel building elements for resistance to hydrogen - induced brittle fracture and advice on the prevention of such fracture

    高強度結構鋼部件耐氫誘導易脆斷裂的特性.用支柱試驗
  16. Color and luster, outside hardness, fracture, acid value, saponification value, iodine value, benzene insoluble, white to light yellow, smooth and shining on surface, without obvious impurity, being hard and crispy, fracture being horse tooth structure with luster

    色澤與外觀硬度、斷面酸值皂化值碘值苯不溶物白色至微黃，表面光滑有光澤，無明顯雜質，質硬而脆，斷面呈馬牙狀有光澤
  17. Hydrogen brittle fracture analysis of two specimens in different conditions

    兩種零件不同條件下氫脆斷裂分析
  18. But during the 1994 northridge earthquake and 1995 hyogoken - nanbu earthquake, beam - to - column connections experienced a great deal of brittle fracture phenomenon, which indicated that the performance on the damage mechanism of some style joints were rather inadequate

    但在1994年northridge和1995年阪神地震中，樑柱連接發生了大量的脆斷現象，顯示出了人們對于鋼框架樑柱栓焊連接節點認識上的不足。
  19. The course of developing composite insulators and its large scale application in china are reviewed, and the statistics of domestic operating experience of composite insulators is given. the main failures which appear during the application of composite insulators, such as brittle fracture of rods, mechanical property, interface breakdown, creepage flashover, ageing performance and so on, are summarized and analyzed. the prospects of applying composite insulators in uhv transmission lines are forecasted

    回顧了我國復合絕緣子的研製以及大規模應用的歷史，對于國內復合絕緣子在使用中出現的一些主要問題，如芯棒脆斷、機械性能、界面擊穿、沿面閃絡及老化性能等方面進行了統計、分析和總結，最後展望了復合絕緣子在特高壓輸電線路中的應用前景。
  20. Abstract : in this paper, through the hydrogen - filling test for the kovar alloy of austenite under fixed load, the kovar alloy hydrogen brittleness sensitivity is measured its feature on hydrongen brittleness fracture is studied, and the way of solving the fracture of the kovar alloy is put forward

    文摘:通過對面心立方奧氏體的可伐合金衡載荷充氫試驗，測試了其氫脆敏感性並研究了氫斷裂特徵，提出了解決可伐合金脆斷的方法。