The technology of fire prevention and extinguishment with ammonialess gelatine - mud
無氨膠體泥漿防滅火技術Based on the close packing and grain composition theory, a new anti - gas channeling lightweight high performance cement slurry system has been developed with industrial drift beads as lightweight additive and superfine gel as strengthening agent
摘要基於緊密堆積和顆粒級配理論,研製了一種以工業漂珠為減輕劑、以超細膠凝材料為增強劑的新型低密度、高強度防氣竄水泥漿體系。With the very low water to cement ratio, rpc has ultra - high strength high ductility and low permeability. in this paper, the compressive strength of rpc can reach to a high point with the number approximately 135mpa. as illustrated from the study results, we can approve some fundamental conclusions : there are big effects on rpc with deferent kinds and properties of raw materials and deferent curing conditions ; stress - strain curve shows the process of destroy with rpc samples ; x - ray diffraction analysis indicates that heat treatment at temperatures 90 accelerate the hydration of rpc sharply, therefore, mechanical and microstructural properties of rpc are highly dependent on heat treatment ; it is believed that rpc materials have excellent resistance to chloride permeability ; during the heat treatment, the shrinkage of rpc developed quickly because of chemical reactions ; the rpc with slag mostly has the advantage of rpc without slag about resistance to solutions corrosion
研究結果表明:通過對rpc各組分摻量變化的研究,可以找到rpc的最優配合比;試件成型后的熱養護制度對rpc的性能影響巨大; rpc的抗壓應力?應變曲線可以反映出試件受破壞時微裂紋的擴展情況,剛纖維的摻入可以大幅改善rpc的韌性; rpc在成型后存在較大的收縮,而其中的化學收縮要遠遠大於乾燥收縮; rpc具有很強的抗氯離子滲透性能,漿體的密實度很高;通過x射線衍射實驗,可以發現rpc的膠凝體中ch晶體已經幾乎不存在,膠凝體主要由c - s - h凝膠和未水化水泥顆粒組成;在抗溶液侵蝕的實驗中,摻礦渣rpc的抗溶液侵蝕性能在絕大多數情況下要好於不摻礦渣試件,酸、堿溶液和浙江工業大學碩士學位論文摘要一些鹽溶液都會對rpc的結構產生侵蝕作用,但是機理各有不同。Analytical solution of the nearest surface spacing between neighboring binder grains in fresh cement paste
新拌水泥漿體中鄰近膠凝材料粒子表面最近間距分佈的解析解The study results indicated that, arranged in the order of magnitude, the degrees of the effects on the cementing strengths of the two interfaces were the system, emulsion, main emulsifier, fluid loss control agent and white oil respectively ; the cementing strength would be doubled and redoubled after being cleaned by preflush, especially by the system, emulsion and fluid loss control agent ; and, along with the increase in the mix slurry ratio, the initial and final set times of slurry would be obviously lengthened and the compressive strength of bond cement would be remarkably reduced or the slurry wouldn ' t be even set
研究表明:對兩界面膠結強度的影響由大到小依次是體系、乳狀液、主乳化劑、降濾失劑、白油;前置液清洗后,膠結強度成倍提高,尤其對體系、乳狀液和降濾失劑清洗效果最佳;隨混漿比的增大,水泥漿初凝和終凝時間明顯延長,水泥石抗壓強度明顯下降,甚至不凝。In order to study the direct relation between oil - base drilling fluid performance and cement job quality, a new developed evaluation method ( artificial core method ) was adopted ; the effects of the oil - base drilling fluid system and its main components on the shear cementing strengths of the first and second interfaces in cementing operation were investigated ; and those of the different mix slurry ratios on the gel strength, initial set time, final set time of slurry and the compressive strength of bond cement were examined too
摘要為了研究油基鉆井液性能和固井質量之間的直接關系,採用新建立的評價方法人工巖心法,考察了油基鉆井液體系及其主要組分對固井作業中第一、第二界面剪切膠結強度的影響規律,以及不同混漿比例下對水泥漿膠凝強度、初凝時間、終凝時間和水泥石抗壓強度的影響規律。Based on the calculation methods of nominal water - cement ratio of mortar and average paste thickness of standard sand provided by authors, the nonlinear relation between fluidity of mortar and nominal water - cement ratio of mortar, average paste thickness of standard sand, fly ash - binder ratio was established by using artificial neural network ( ann )
摘要在給出水泥膠砂名義水灰比和標準砂平均漿體厚度計算方法的基礎上,採用人工神經網路方法,建立了水泥膠砂流動度與水泥膠砂名義水灰比、標準砂平均漿體厚度、粉煤灰與膠凝材料用量比之間的非線性映射關系。Based on above, the characteristics of hydration hardening process and microstructure of hsc as well as the interfacial layer between cement paste and coarse aggregate are investigated under low water cement ratio, high content superplasticiser and with one kind or more than one kind of mineral materials condition, the reaction mechanisms of different mineral materials are also discussed
研究了不同水膠比、復合緩凝成分高效減水劑及礦物摻合料的摻加方式、摻量對高強混凝土水泥漿體水化放熱過程和水泥漿體的水化熱、水化放熱速率以及最高溫升的影響規律。探明了高強混凝土中水泥漿體的水化硬化過程、礦物摻合料之間的相互作用機理。Under the conditions of high efficiency water - reducing agent, the homogenization of starch mixed composite powder is better than that of blank cement and only mixed fly ash
在高效減水劑存在的情況下,摻復合粉的膠凝材料漿體勻質性優于空白水泥與單摻粉煤灰。分享友人