  1. In order to obtain the strontium titanate nanocrystalline powers materials with small grain, high purity and homo - geneous grain size distribution, the effect of water, waiter - free acetic acid, gel temperature, heat treat temperature and so on were researched

    為了制備出晶粒小、材料純度高以及粒徑分佈均勻的納米鈦酸鍶粉體材料，研究了用水量、冰醋酸加入量、凝膠溫度和煅燒溫度等工藝參數對制備納米鈦酸鍶粉體材料的影響。
  2. Crystalline procedure and phase structure of bst powders

    鈦酸鍶鋇粉體晶化過程和物相結構研究
  3. The thermodynamic properties of batio3 srtio3 superlattices with the effects of stress

    鈦酸鍶超晶格的熱力學性質
  4. Application of chelator in strontium titanate as lean - burning oxygen sensors

    螯合劑在氧敏傳感器鈦酸鍶薄膜制備中的應用
  5. ( 3 ) according to the study of heat treatment process, heat treatment ambience, airflow and heat treatment temperature were considerd as the important influences on the quality and property of ybco films. through optimizing the process, the ybco films were prepared on sto single crystal, and their room temperature resistance was about 200 ybco films also were fabricated on the sto buffered si substrate, and their room temperature resistance was about 300d

    （ 3 ）根據本文熱處理過程的工藝探索，認為熱處理氣氛、氣流量及處理溫度是影響薄膜質量及性能的重要因素，通過優化工藝過程，在鈦酸鍶（ sto ）單晶上制得的ybco薄膜表面質量良好，室溫電阻200左右；而在預制了鈦酸鍶（ sto ）緩沖層的si基板上制備的ybco薄膜的室溫電阻為300左右。
  6. One - step synthesization made the electrical properties more stable, controling the reducing sintering temperature and retention time can adjust the electrical properties in a certain scope, changing the oxidation temperature made the varistor ’ s voltage v10ma changed, using the special double - layer silver plasm can eliminate the voltage - direction problem

    一次配料得到的樣品電性能一致性更好;控制還原氣氛燒結溫度和保溫時間，可以在一定范圍內調節鈦酸鍶壓敏電阻器的電性能，改變氧化溫度可以獲得不同的壓敏電壓，從而得到系列化產品;採用雙層銀漿工藝成功消除了壓敏電壓的方向性問題。
  7. The ceramic is a diclectric whose main material is titanium oxide, barium titanate or strontium. it becomes ceramic capacitor after a process called silver coating and is widely applied in various kinds of electronic equipment

    用氧化鈦、鈦酸鋇、鈦酸鍶等材料製成陶瓷並以此作為介質製成的電容器稱為陶瓷電容器，這種電容器廣泛用於各種電子設備。
  8. Ferroelectric ( ba, sr ) tio3 thin films have excellent ferroelectric / dielectric properties, and own good application prospect in tunable microwave devices, dynamic random access devices, and pyroelectric detector devices

    鐵電鈦酸鍶鋇薄膜具有十分優越的鐵電介電性能，在可調諧微波器件、動態存儲器件，以及熱釋電探測器等方面具有很好的應用前景。
  9. Influences of dispersion media on electrorheological effects of srtio3 system

    分散介質對鈦酸鍶系電流變液電流變性能的影響
  10. The pst thin films in which the perovskite structure primarily formed were fabricated successfully on ito / glass substrates by the sol - gel method

    本文採用溶膠?凝膠技術在ito基板上成功制備了性能優越的多晶鈦酸鍶鉛薄膜材料。
  11. Second, srtios - based double function ceramic was achieved with prepared strontium titanate nanocrystalline powder materials by single - fired process

    然後，在制備的納米鈦酸鍶粉體材料的基礎上，採用一次燒成工藝制備srtio _ 3基電容-壓敏雙功能陶瓷器件。
  12. The results of transmission electron microscopy ( tem ) showed that the grain of strontium titanate powder prepared was spherical and the grain sizes distribution were homogeneous

    通過tem分析可以看出，制備的鈦酸鍶粉體材料的顆粒為球形，並且顆粒大小均勻。
  13. ( 2 ) the ysz and sto buffer layers were prepared by sol - gel process on si substrates. the ysz and sto films could be used as the buffer layers between si substrate and ybco films

    （ 2 ）用sol - gel法在si基板上制的釔穩定氧化鋯（ ysz ）和鈦酸鍶（ sto ）薄膜作為si與ybco間的緩沖層是可行的。
  14. First of all, prepare srtio3 powder materials by sol - gel process and solid phase synthesis process. stir time, gel time, gel temperature, heat treat temperature and so on are researched in sol - gel process

    用固相合成法制備鈦酸鍶粉體材料中研究了ti / sr比、研磨方法對制備鈦酸鍶粉體材料的影響。
  15. Barium strontium titanate ( bst ) shows high dielectric constant and low dissipation factor and holds great promise for wide applications in dynamic random access memory ( dram ), transducer and infrared detector

    鈦酸鍶鋇（ bst ）薄膜具有較高的介電常數和較低的介質損耗，在動態隨機存儲器（ dram ） 、傳感器、探測器等方面應用前景廣闊。
  16. The method of grind, ti / sr ratio are researched in solid phase synthesis process. second, on the base of strontium titanate powder materials prepared, srtio3 - based double function ceramic were fabricated by the conventional ceramic process

    然後，在制備的鈦酸鍶粉體材料的基礎上，採用傳統的陶瓷工藝制備srtio _ 3基電容-壓敏雙功能陶瓷器件。
  17. Their dielectric loss is about 10 - 2, and figure of merit ( fom ) is less than 300. recently, cross etc. found that lead strontium titanate ( pst ) has bigger tunability and lower loss, besides this, pst is a perovskite ferroelectric material which has good solid solution

    就微波可調介電材料而言，目前研究較多、性能較好的主要是鈦酸鍶鋇（ bst ）及其摻雜系列，其可調性一般在50左右，介電損耗在10 ~ （ - 2 ）量級上，綜合反映材料可調性的優值一般在300以下。
  18. Barium strontium titanate ( bst ) film has been investigated extensively for the application in the high density dynamic random access memories ( drams ). one of the most crucial electrical parameters of these films has been the leakage current level of dram cells

    鈦酸鍶鋇（ ba _ （ 1 - x ） sr _ xtio _ 3或bst ）以其高介電常數、低損耗，介電響應快、疲勞強度大等優點，在下一代動態隨機存儲器（ dram ）上的應用前景非常廣闊，是近年來人們研究的熱點。
  19. Research of this thesis include two parts mainly, first part include the preparation of srtio3 powder materials by sol - gel process and solid phase synthesis process. the second part, on the base of strontium titanate powder materials prepared, srtio3 - based capacitor - varistor double function ceramic were fabricated by the conventional ceramic process

    第二部分是在制備的鈦酸鍶粉體材料的基礎上，通過摻雜施主、受主離子對鈦酸鍶材料進行半導化，制備電容-壓敏雙功能器件，並對兩種方法制備的元件性能分析比較。
  20. Among these materials, ba1 - xsrxtio3 ( bst ) thin films have been extensively investigated due to their strong electric - field dependent dielectric constant. in this work, bst thin films have been deposited by using rf magnetron sputtering

    鈦酸鍶鋇（ bst ）材料由於其介電常數可通過外加電場來調節（即介電可調性能） ，從而成為鐵電移相器的主體材料，並獲得了廣泛的研究。