Development of protection coatings on uranium and uranium alloys
鈾及鈾合金防護鍍層的研究進展The corrosion test, performed in 5wt % salt fog or with the electrochemical calculation of anodic polarization in 50, g / g potassium chloride aqueous solution, indicates the coatings densification corresponds with their corrosion protection to uranium. the denser the coatings are, the more effective their protection to uranium is. compared with the al coatings produced at - 300v bias voltage and al _ ( 2 ) o _ ( 3 ) coatings produced with ps technique, the al coatings at - 100v and al _ ( 2 ) o _ ( 3 ) coatings with rms and to techniques are denser thus providing a better protection for uranium
電化學參數計算或鹽霧腐蝕結果表明,鍍層的緻密程度與其對鈾基體的保護性能呈現了較好的一致性:鍍層越緻密,其保護性越好,即- 100v偏壓下的鋁鍍層和rms 、 to法制備的al _ 2o _ 3鍍層;鍍層越疏鬆,其保護性越差,即- 300v偏壓下的鋁鍍層和ps法制備的al _ 2o _ 3鍍層。Our experiments emphasized the correlation between micro structures and some properties of the coatings and tried to obtain the protective coatings with the comprehensively good properties, in which auger electron spectroscopy ( aes ), scanning electron microscope ( sem ), and x - ray diffraction ( xrd ) were employed to investigate the composition, microstructure and crystal phase of the coatings respectively, and the properties test was primarily considered with the wear resistance and corrosion resistance of the coatings
本論文主要採用pvd技術中的磁控濺射鍍膜( ms或rms )及部分用等離子噴塗( ps )和熱氧化( to )表面處理技術研究了鈾的具有代表性的三種防腐保護鍍層,即單質al 、氧化物al _ 2o _ 3和合金al - zn鍍層。實驗力圖在制備技術、工藝參數及鍍層的微結構和性能之間找到一些內在的聯系,探索綜合性能較好的防腐蝕鍍層。In addition, it is found that the al - zn coatings can change from anodic protection to catholic one with increase of the bias voltage
實驗還發現,相對于鈾基體, al - zn鍍層隨偏壓的增加可由陽極性鍍層轉變為陰極性鍍層。分享友人