鋇鐵氧體 的英文怎麼說

中文拼音 [bèitiěyǎngtǐ]
鋇鐵氧體 英文
barium ferrite
  • 鋇 : 名詞[化學] barium （56號元素, 符號 ba）
  • 鐵 : Ⅰ名詞1 （金屬元素） iron （fe） 2 （指刀槍等） arms; weapon 3 （姓氏） a surname Ⅱ形容詞1 （形容...
  • 氧 : 名詞[化學] （氣體元素） oxygen （o）
  • 體 : 體構詞成分。
  1. Research and application of barium ferrite thin films

    鋇鐵氧體薄膜的研究及應用
  2. The effects of the different kinds of rare earths and the doping amount of them on magnetic properties of bafe, 2o19 ultrafine powders ( including the specific saturation magnetization, the specific remanent magnetization and coercive force ) were firstly discussed systematically

    首次查明了鋇鐵氧體粉末的磁性能（包括比飽和磁化強度、比剩餘磁化強度和內稟矯頑力）隨稀土元素種類及其摻雜量的變化規律。
  3. This conclusion can also be applied in other synthesis methods such as chemical co - precipitation, aerosol synthesis, cryochemical method and hydrothermal synthesis

    這一關鍵對稀土摻雜鋇鐵氧體的其他制備方法，如化學共沉澱法、氣溶膠法、低溫化學法和水熱法等也同樣適用。
  4. In 2005, 61 physical and chemical parameters were measured and analysed in sediments. these included particle size, electrochemical potential as highly anoxic sediment with negative potential is related to organic pollution, chemical oxygen demand which indicates organic pollutants, total sulphide inorganic constituents, source of the unpleasant - smelling gas hydrogen sulphide, 15 metals and metalloids aluminium, arsenic, barium, boron, cadmium, chromium, copper, iron, lead, manganese, mercury, nickel, silver, vanadium and zinc, and trace toxic organics pahs and pcbs - 16 compounds and 18 congeners respectively

    2005年，沉積物監測包括分析61種物理及化學參數，其中有粒子大小電化學勢有機污染促使沉積物缺氧，而讓電化學勢呈負數值化學需氧量顯示有機污染程度總硫化物無機物，是造成難聞氣體硫化氫的主因15種金屬及準金屬鋁砷鋇硼鎘鉻銅鐵鉛錳汞鎳銀釩及鋅和痕量毒性有機物多環芳烴及多氯聯苯分別為16種復合物及18種同質物。
  5. The elements of ferrite magnet are ferricoxide barium strontium. ferrite has highter coercive force and highter resistance to bedemagnetized and oxidized than other non - rare earth permanent magnets. the biggest advantage of such magnet is their low cost. it is widely used from motors and loudspeakers to toys and craft etc.

    鐵氧體由氧化鐵、鋇、鍶等元素組成，與其它非稀土磁鋼相比，鐵氧體的矯頑力和抗腐性都比較好，尤其它的低成本更是其它磁鋼所無法比擬的。它被廣泛應用於從電機、揚聲器到玩具、工藝品等各個領域
  6. In this paper based on hexagonal ferrites with high resonance frequency, the electromagnetic properties of the z - type ferrites in the range of 50mhz to 1ghz have been carried out and have sintered at low temperature through the gelatin spontaneous combustion

    本文以具有高截止頻率的六角鐵氧體為基礎，開展了50mhz 1ghz的z型六角鋇鐵氧體電磁性能的研究，並通過凝膠自燃法實現了低溫燒結。
  7. To measure the size of ba - ferrite fine magnetic particles, electromagnetic field was employed to drive the fine magnetic particles displace in order, then scanning electron microscope ( sem ) was used to observe and measure the size of ba - ferrite fine magnetic particles

    為了迅速、準確地測定鋇鐵氧體磁粉顆粒的厚度、直徑和厚徑比的統計分佈，採用對磁顆粒施加外加電磁場的方法，使各個磁顆粒的易磁化軸方向趨於一致，並用掃描電子顯微鏡觀察鋇鐵氧體磁粉顆粒。
  8. The formation mechanism of barexfe12 _ xol9in heat treatment was firstly deeply discussed, and the action mechanism of complexing agent ( citrate ) and dispersant ( glycol ) during the formation of the gel was also firstly studied

    首次對溶膠-凝膠燃燒合成法熱處理過程中稀土摻雜鋇鐵氧體的生成機理進行了深入研究，同時初步查明了過程中絡合劑（檸檬酸）和分散劑（乙二醇）的作用機理。
  9. Studies of microwave - absorbing properties of niznco 2 - w composite ba - ferrite

    型復合鋇鐵氧體吸波特性研究
  10. The hexagonal barexfe, 2. xo, ( re denote la ^ nd > sm and gd ) ultrafine powders with m - type structure were firstly synthesized by a novel technique - - - - - - sol - gel combustion synthesis method which combines sol - gel method with low temperature combustion synthesis method. based on theoretical analysis and experimental study, the effects of the composition of the gel, the different kinds of intermediate, strength of solution, the amount of complexing agent, the different kinds of anions, the adding of dispersant, auto - propagating combustion and the condition in heat treatment of the gel on crystal phase, particle size, morphology and magnetic properties of bare ^ fe ^ o, ultrafine powders were firstly investigated systematically to clarify the optimum forming conditions

    本研究是在前人工作的基礎上，同時從制備方法和摻雜元素兩方面著手，以保證制備的粉體材料具有優異的性能，即首次利用溶膠?凝膠濕化學合成法和低溫燃燒合成法相結合的一種兼具二者優點的超細粉末新型合成技術? ?溶膠-凝膠燃燒合成法來完成稀土元素摻雜鋇鐵氧體bare _ xfe _ （ 12 - x ） o _ （ 19 ） （ re為la 、 nd 、 sm 、 gd ）超細粉末的制備。
  11. In order to meet the requirement of nano - hexaferrites, hydrothermal method and sol - gel self - propagating high - temperature synthesis method were applied. by studying the effects of different precursors, ph value, temperature and time, the optimum conditions were determined, the structure of crystals was studied by x - diffract aat the same time the morphologic and the diameter of crystals were studied by tem

    使用x一射線衍射鑒別晶體結構，通過透射電子顯微鏡觀察粒子的形貌與大小， x一射線衍射鑒別晶體是鋇鐵氧體，透射電子顯微鏡觀察粒子的形態與大小， ，發現粒子分散性較好，結晶性良好，形貌為六角型，通過統計計算粒子粒徑，粒子大小處于納米級，平均粒徑為70nm 。