The key products of the company are high alumina brick, fireclay brick, phosphate - bonded wearable brick, exfoliation - resistant high alumina brick, high refractoriness under load brick, corundum brick, magnesite brick, magnesite ? chrome brick, series of corundum, sic furnace chamber and pipe, ceramisite brick, corundum - mullite brick, corundum - chrome brick, sillimanite brick, magnesite alumina spinel brick, acid - resistant brick, alkali - resistant brick, zirconia - corundum brick, alumina bubble products, series thermal insulating refractory products, high alumina castable, corundum castable, corundum ramming, brown - corundunm castable, sic castable, low - cement castable, alkali ? resistant castable, light silica alumina products, stainless steel fibre reinforced castable, etc
主要產品有：高鋁質磚、粘土質磚、磷酸鹽耐磨磚、抗剝落磚、高荷軟磚、剛玉磚、碳化硅磚、鎂磚、鎂鉻磚、各種剛玉、 sic爐膛、爐管製品、陶粒磚、剛玉莫來石磚、鉻剛玉磚、硅線石磚、鎂鉻尖晶石磚、耐酸磚、耐堿磚、鋯剛玉磚、氧化鋁空心球製品及各種輕質保溫材料、高鋁質澆注料和剛玉澆注料、搗打料、棕剛玉澆注料、碳化硅澆注料，低水泥澆注料、抗堿性澆注料、輕質硅酸鋁製品、鋼纖維增強澆注料等80餘種系列耐火材料。Scp - zro2 ( gem - grade zirconia ) has high purity and is mainly used for making cubic zirconia crystal ( artificial gems ), and as additive for optical glass and fibre with high index of refraction
具有高純度，是製造立方氧化鋯晶體（人造寶石）的主要原材料，也用作高折射光學玻璃和光學纖維的添加劑。Zro2 fibrous cloths are characterized by their high melting point ( 2600 ), high - temperature resistance ( 2200 ), oxidation - corrosion resistance, quick absorbing alkaline, high alkaline absorption, and low heat - conductivity and resistivity, etc. zroi fibrous cloths that can be used as the nickel - hydrogen battery separators were first developed by using precursor process at home
氧化鋯纖維布具有熔點高（ 2600 ） 、耐高溫（ 2200 ） 、抗氧化、耐腐蝕、熱傳導率低、吸堿速度快、吸堿率高、面電阻小等特點。The parameters of impregnation are as follows : ph is about 3, the range of temperature is from 20 to 45, and the time is about 2 to 6 hours. after the necessary treatments, zirconia cloths had the optimal strength when the diameters of zirconia fibers were controlled in 4um to 7um, and the sizes of zirconia grains were in 50nm to 100nm. the affec - ting factors were discussed and the liner regression analysis of the cloths was made, from w hich they show that the diameters and grain sizes have the significant influences on zirconia cloths. the obtained zirconia cloths have been accepted for use in nickel - hydrogen batteries by practical use
研究結果表明：粘膠類纖維布最適合制備氧化鋯纖維布的前軀體；鋯液濃度以飽和溶液為宜；浸漬工藝參數為ph值3左右，溫度20 45 ，時間2 6小時；多餘鋯鹽的去除、浸鋯液后纖維布的整平處理及平燒施應力燒成有利於氧化鋯纖維布的柔軟及平整; 200 600燒成溫度段應緩慢燒成，控制氧化鋯纖維直徑在4 7 m ，氧化鋯晶粒尺寸50 100nm時氧化鋯纖維布的強度最好。The methods for preparing zro2 fibers, zro2 fibrous mats, rigid zro2 fibrous products, fibrous papers and cloths were introduced in this paper. the mainproperties, application scopes and state - of - the art were also introduced
本文介紹了氧化鋯纖維、氧化鋯纖維氈、剛性氧化鋯纖維製品、氧化鋯纖維紙及氧化鋯纖維布的制備方法、主要性能及應用領域和發展現狀。According to the present status and trend, zro2 fibrous cloths are considered as the optimal separator materials for the alkaline batteries with high capacity, especially for nickel - hydrogen batteries
根據發展現狀及趨勢，提出了氧化鋯纖維布是大容量堿性電池尤其是鎳氫電池最理想的隔膜材料。The results show that the capacity and rate of alka - line absorption is respectively 10 percent more than that of american products, and twice as fast as that of them. the resista - nce is as good as that of them, and the electric property is better than that of them, but the tensile strength is not so good as that of them
研究制備的氧化鋯纖維布作為大容量鎳氫電池隔膜，組裝成電池進行實效考核表明，可以用於鎳氫電池隔膜;性能測試表明，吸堿率比美國產品高10 ，吸堿速率是美國產品的2倍，電性能優於美國產品。分享友人