The effect of additives on the properties of permanent ferrite srm
添加劑對鍶永磁鐵氧體的改性研究Development of high performance strontium ferrite magnetic material
高性能鍶鐵氧體磁性材料的研製On the base of the analysis on the advanced technology of hard ferrite in foreign country, the main procedures of preparing hard ferrite pre - sintering material are determined as follows : first, the ferrite oxides coming from the main cold rolling line and strontium carbonate are conveyed to storage tank by gas power and weighed automatically according to the demands of constituent composition. and then they are mixed and grinded by using method of wet treatment. finally the mixtures is transported to the devices of storage by transporting pump
在分析國外先進的永磁鐵氧體生產工藝的基礎上，確定了生產高檔永磁鐵氧體預燒料的主要過程：首先，利用攀鋼冷軋鐵紅為主要原料，將氧化鐵紅及碳酸鍶採用氣力輸送至貯料料倉，經自動稱量裝置，按工藝配方稱量後分別由氧化鐵紅及碳酸鍶發送罐氣力輸送進入預混攪拌筒加水攪拌，然後再送入混磨機濕法混磨；最後，混合物經輸送泵輸送至料漿存儲裝置，經定量進料泵定量輸送至回轉窯進行濕法預燒，預燒料經緩冷至室溫后，再球磨。The research work in this paper was carried out at the second power factory of xici subsidiary. the production technology of strontium ferrite was studied and wet process of strontium ferrite pre - sintering material with anisotropic characteristic was determined. products of y30h - 2 which meet the standard series of sj / t10410 - 1993 were selected to be experimental products
本文以西磁分公司料粉二廠為基點，研究了鍶永磁鐵氧體生產的工藝技術路線，確定了濕法工藝生產各向異性鍶永磁鐵氧體預燒料，並將試驗產品定位在sj t10410 - 1993標準中的y30h - 2產品。In order to develop the permagnetferrite industry and satisfy the instant need of the market, this paper systematically study the impact of the additives on the strontium permagnetferrite and discuss its mechanism from the microstructure
為了發展我國的鍶鐵氧體永磁產業，滿足國內外市場對高性能鍶鐵氧體永磁產品的迫切需求，本文系統地研究了添加劑對鍶鐵氧體永磁磁性能的影響，並從微觀結構方面探討了磁性能提高的機理。Both of the two ways can reach fb5b standard of tdk company. the coercive force of strontium permagnetferrite can be improved when a12o3 or cr2o3 was added to caco3 - sio2 or caco3 - hbo3 multi - additives. ( 4 ) comparing with normal caco3 and sio2, the nano caco3 and sio2 improve the magnetic. for the nano caco3 and sio2 have high chemical activations and excellent distribution, the density of permagnetferrite can be improved and the sinter temperature of it can be reduced
納米caco _ 3 、 sio _ 2與普通caco _ 3 、 sio _ 2加入相比，鍶鐵氧體永磁獲得的最佳磁性能高，獲得最佳磁性能的添加量范圍變寬，即納米caco _ 3 、 sio _ 2提高了磁性能的穩定性，有利於大生產時鍶鐵氧體永磁的磁性能的穩定，對生產有重要的指導四川大學碩士論文意義;由於納米caco3 、 510 :分佈更均勻，具有高的化學活性，降低了銘鐵氧體永磁的最佳燒結溫度，提高了銘鐵氧體永磁的燒結密度，因而增大了caco3 、 510 :添加劑對銘鐵氧體永磁的改性效果。The elements of ferrite magnet are ferricoxide barium strontium. ferrite has highter coercive force and highter resistance to bedemagnetized and oxidized than other non - rare earth permanent magnets. the biggest advantage of such magnet is their low cost. it is widely used from motors and loudspeakers to toys and craft etc.
鐵氧體由氧化鐵、鋇、鍶等元素組成，與其它非稀土磁鋼相比，鐵氧體的矯頑力和抗腐性都比較好，尤其它的低成本更是其它磁鋼所無法比擬的。它被廣泛應用於從電機、揚聲器到玩具、工藝品等各個領域分享友人