鎂砂 的英文怎麼說
中文拼音 [měishā]-
In this paper, the effects of fly ash, cement, lime, fine sands, foam agent, w / c ratio and additional agent on foamed concrete were studied by experiments, the best combination ratio of fly ash foamed concrete whose density varies from 551kg / m3 to 650kg / m3 was obtained through orthogonal test design, the foam agent quantity and the fly ash quantity effect the fly ash foamed concrete greatly, so the author selected them as independents to establish duality linear regression equations, the equations were quite ideal through the test of model summary r. moreover, the author also did some experiments about the water resistance of magnesium oxychloride cement fly ash foamed concrete, the outcome showed that phosphoric acid has good effect on water resistance, and its appropriate quantity was found
本文通過試驗研究了粉煤灰、水泥、石灰、細砂、發泡液、水灰比及外加劑對粉煤灰發泡混凝土性能的影響，採用正交設計試驗方法得出了600級粉煤灰發泡混凝土的最佳配合比，同時發現發泡液和粉煤灰摻量對發泡混凝土的影響最為顯著，因此，以二者為自變量建立了二元線性回歸方程，通過全相關系數的檢驗發現方程較為理想。此外，還對氯氧鎂水泥基粉煤灰發泡混凝土的耐水性進行了相關實驗，發現磷酸有較好的耐水性效果，同時找到了其合適的摻量范圍。Investigation on process flow of high - density magnesia
高密度燒結鎂砂的研究Standard test method for hydration of dead burned magnesite or periclase grain
僵燒鎂砂或方鎂石顆粒水合作用的標準試驗方法Standard specification for magnesium - alloy sand castings
鎂合金砂型鑄件的標準規范Magnesium oxide talc maleic anhydride chemical dyes richchem inc. manufacture export follow : maleic anhydride, phthalic anhydride, magnesium chloride, magnesium sulphate, talc, brucite, dead burnt magnesite, caustic calcined magnesite, magnesium oxide, magnesium hydroxide, magnesium carbonate, fused magnesia, saponite
本公司主要產品有：鎂砂輕砂鎂砂中檔鎂高檔鎂純堿，氯化銨，順酐，高鈣合成砂造渣球噴補料熱態補料耐火澆注料轉爐濺渣護爐改性不定型耐火材料等產品Dangerous trades as defined in the factories and industrial undertakings ordinance ( cap. 59 ) include boiler chipping ; manufacture of glass from basic raw materials ; manufacturing processes involving the use of arsenic, lead, manganese, mercury and phosphorus ; vermillion manufacture ; chromium plating ; machining or grinding of celluloid or magnesium ; and manufacture of hydrochloric, nitric or sulphuric acids, etc
根據《工廠及工業經營條例》 ，危險行業包括鏟修鍋爐，以基本原料製造玻璃，使用砷、鉛、錳、汞、磷的製造工序，製造硃砂，鍍鉻，切削或研磨賽璐珞或鎂，及製造鹽酸、硝酸或硫酸等。This product combines excellent micro structural flexibility with very good coat ability because of dead burned magnesia / low chromite / hercynite combination
由於重燒鎂砂和低鉻鐵礦/鐵鋁尖晶石的組合，該產品結合了優良的微結構彈性和良好的造窯皮能力的優點。Rapid repairing mass for converter ismade of electro baked magnesite and high - quality synthetic sandand manufactured by adding high fluidity recarburizer ( beveloped by ourselves ) as addition agent withspecial technique. lt has the characteristics of well fluidity, well rapid fluidityand rpid sintering etc. it is applied to hot patching of large area before or after the converter as rapping hole patching and other parts for converter
轉爐快速補爐料是以電熔鎂砂和優質合成砂為主要原料，配以自行研製的高流動性的增碳劑為添加劑，以特殊工藝生產製成，具有流動性好、快速燒結等特點，適合於轉爐的前後大面的熱修補及出鋼口等部位的修補The product is manufactured by taking high purity fused magnesia as raw material and adding a special binder, sintering agent and coagutant through a special production process
該產品是以優質高純電熔鎂砂為主要原料，外加特殊結合劑、燒結劑、促凝劑，經過特殊的生產工藝加工而成。Fused magnesia - chrome materials
電熔鎂砂Sales : magnesia, magnesia brick, meitanzhuan, bottom material, a special material that is not stereotypical fire - proof material, the light burning powder, steel
銷售：鎂砂，鎂磚，鎂碳磚，爐底料，搗打料，不定型耐火材料，輕燒粉，鋼材。Method for the determination of mgo, sio sub2 ;, cao. fe sub2 ; o sub3 ;, alo sub3 ;, mno, tio sub2 ; contents in magnesite for export - x - ray fluorescence spectrometric method
出口鎂砂中的氧化鎂氧化硅氧化鈣氧化鐵氧化鋁氧化錳氧化鈦的測定x射線熒光光譜法The quality is a burnt magnesia spinel brick made from fused magnesia ， low iron sintered magnesia and fused hercynite. this synthetic hercynite is a patent by rhi refractories
它由電熔鎂砂、低鐵燒結鎂砂和電熔鐵鋁尖晶石製成的燒結鎂鐵尖晶石磚，這種人工合成的鐵鋁尖晶石是rhi奧鎂公司的專利。Ladle castable is made from high qualified crog, corundum, magnesia and so on, which are mixed by binder. its thermal shock resistance, erosion resistance and volume steadiness are good. it ' s suited to the middle and small ladle and can be used for a long time
鋼包澆注料是用優質礬土熟料、剛玉、鎂砂、鎂鋁尖晶石和超微粉等材料，用不同結合劑和外加劑配製的，其特點是抗侵蝕性強、抗熱震性好，體積穩定性好，適用於中、小型鋼包使用，壽命長。The material of electro - fused magnesia sinter is selected from special grade a natural magnesite or high - purity caustic calcined magnesite, which is fused in arc furnace to finish the products. the products possess high purity, crystal with and compact texture, have high heat - vibration steady and cinder corrosion resistant, it is used for making high quality magnesite bricks, magnesia - carbon bricks
電熔鎂砂是用精選的特a級天然菱鎂石，在電弧爐中熔融制得，該產品具有純度高，結晶緻密，抗渣性強熱震穩定性好，是製作高檔鎂磚，鎂碳磚及不定形耐火材料的重要原料。The product is produced with high quality magnesia and basic refractory raw material, binder and additive, it has higher corrosion resistance and good thermal shock resistance and can prolong the service life of tundish and is easy to remove its lining, it can be used by mechanical gunning and manual smearing on working site
本產品是採用優質鎂砂和堿性復合耐火原料與特殊復合結合劑、添加劑製作而成，該產品具有較高的耐侵蝕性和耐急冷急熱性，可以有效的延長中間包的使用壽命，並易於脫包，本產品可現場機械噴塗施工，又可人工塗抹作業。They have excellent corrosion, thermal shock resistance and spalling resistance. they wide applications and can be used in key locations of thermal processing equipment such as bof, eaf, lf and so on. 2 alumina - magnesia - carbon brick made from high - purity bauxite or fused alumina and fused magnesia grain or high purity magnesia by pressing, resin - bond for thermal shock resistance
1 ，鎂碳磚是不燒的耐火材料，經過摩擦壓磚機的成型以及乾燥處理后而成，它的主要原料是電熔鎂，高純鎂砂和高純石墨，結合劑為樹脂，鎂碳磚有良好的耐侵蝕性，熱震穩定性和抗剝落性，它已經被廣泛地用在鋼廠的轉爐電爐鋼包精煉鋼包等關鍵部位。Additions of carbon for improved slag resistance. spinel formation improves hot strength, slag resistance and brick joint erosion. 3 repairing material for bof uses fused magnesia or sintered magnesia as the main raw material and after modifid pitch and special additives are added, it has the following characteristcs than other conventional converter pitch temperature, shorter sintering time, longer service life and less pollution. it is mainly used for repairing converter working face, also for tapping side, tapping hole and bottom
3 ，轉爐大面補料是採用電熔鎂砂或燒結鎂砂為主要原料，通過加入改性瀝青和特種添加劑使它和傳統瀝青補爐料相比具有高溫附著性好燒結時間短流動性好使用壽命長污染小等特點，主要用於修補轉爐迎鋼面通常稱「大面」也可以用於修補出鋼側，出鋼口及爐底等部位。The mix is produced with high quality sintered magnesite from liaoning as main raw materials, and is processed by matrix strengthening, classifying and proportioning reasonably. it has good performance of high adhesivity, a bit rebound and long service life. each gunning to the large size converter can withstand 6 - 10 heats
我公司生產的鎂質噴補料採用遼寧優質燒結鎂砂為主要原料，強化基質，合理級配、噴補時具有附著率高、回彈小、使用壽命長的優點，在大型轉爐上一次噴補使用壽命一般在6 - 10爐。It is made of fused magnesite and high purity flake graphite by adding metal composite antioxidant and phenolic resin as binder. it has the excellent properties of corrosion resistance, spalling resistance, resistance to oxidation and better thermal shock resistance. it can be used in all kinds of converters, eaf, refining ladles and common ladles. upon request, multiple lining - up designs of reasonable materials can be provided according to the working conditions of above mentioned furnaces
採用電熔鎂砂、高純鱗片石墨為主要原料，添加金屬復合抗氧化劑，以酚醛樹脂為結合劑製成的製品具有優良的抗浸蝕性、抗剝落性、抗氧化性和良好的抗熱震性，適用於各種容量的轉爐、電爐、精煉鋼包及普通鋼包，本公司可根據用戶要求，針對上述4種熱工窯爐的具體使用條件提出爐襯的材質綜合砌築方案。分享友人