鑄件氣孔 的英文怎麼說

中文拼音 [zhùjiànqìkǒng]
鑄件氣孔 英文
blow hole
  • 鑄 : Ⅰ動詞（鑄造） cast; coin; make Ⅱ名詞1. （古國名） zhu, a state in the zhou dynasty2. （姓氏） a surname
  • 件 : Ⅰ量詞（用於個體事物） piece; article; item Ⅱ名詞1. （指可以一一計算的事物） 2. （文件） letter; correspondence; paper; document
  • 氣 : Ⅰ名詞1 （氣體） gas 2 （空氣） air 3 （氣息） breath 4 （自然界冷熱陰晴等現象） weather 5 （氣味...
  • 氣孔 : [礦物學] blowhole; [植物學] stoma; [動物學] spiracle; pore; stigma; [冶金學] gas hole; gas pocket; [建築] air hole
  1. Abstract : hydrogen and oxygen solubility in molten copper, condition of gas - absorption during smelting of pure coper, mechanism of gas hole formation, gas hole appearance on worked material and measure to gas absorption prevention have been briefly described

    文摘:論述了氫和氧在銅液中的溶解能力、熔鑄紫銅時的吸氣條件、氣孔形成的機理、氣孔在加工型材上的表現、防止吸氣的措施等。
  2. The product is produced according to general standard. as inoculant alloy in cast iron, deoxidizer in steel - smelting, the product is used widely in steel industry. it has unique and special function on a long time of anti - declining, reducing gasholes of cast material and improving processing function

    以硅為基礎的硅鍶合金按通用標準生產，作為高牌號灰鑄鐵的孕育劑，煉鋼中的脫氧劑，合金劑而廣泛應用於鋼鐵工業之中，作為孕育劑在抗衰退時間長，減白口能力強，減少鑄件氣孔，改善加工性能方面均有著獨特的作用。
  3. The quality of furan sand castings is usually better than clay sand castings, however, some defects are also very easy take place with furan sand castings such as blow hole, metal penetration, veining, cracking, slag inclusion, hardness too low, surface recarburation, surface sulphuration, nodularity degeneration etc, which were usually caused by improper raw materials selection, improper method design, incorrect moulding or / and core - making

    摘要呋喃樹脂砂鑄件質量一般比黏土砂鑄件好，但如果原材料選擇、工藝設計、造型和制芯操作不當，也會產生氣孔、粘砂、脈紋、裂紋，夾渣、硬度不足、滲碳、滲硫和球化不良等鑄造缺陷。
  4. Abstract : porosity of die castings caused by air entrapped into the liquid metal in the shot sleeve is common problem of die csating process

    文摘:壓室中氣體捲入金屬液內而造成壓鑄件內部氣孔是壓鑄過程常見的問題。
  5. Solidification process simulation and shrinkage cavity prediction of cylinder head casting

    氣缸蓋鑄件凝固過程數值模擬及縮松縮孔預測
  6. Abstract : introduced is the experience in replacing atmosperic riser with thermal - isolation riser and improving pouring system to eliminate shrinkages

    文摘:介紹了用保溫冒口代替大氣壓力冒口，改進澆注系統解決鑄件縮孔問題的經驗。
  7. Analysis results of histogram statistics and section electron microscopic scan technique, are that fracture feature of the cracks of the hbbb is similar and the crack is multi - source strain fatigue one. internal defects of the cast, such as impurities, gas holes, etc, are the main causes for early cracks. the contrast analysis of static strength, model and transient respond on three structures with fem proves that geometrical stress concentration in partial area has influence on early crack, also

    利用直方圖等統計方法和電鏡掃描技術對該抱軸箱體裂紋分析的結果是：抱軸箱體的裂紋斷口特徵相近，裂紋性質屬于多源性低周疲勞裂紋，鑄件中的夾雜、氣孔等內部缺陷是導致過早裂損的主要原因；利用有限元法對該抱軸箱體三種結構的靜強度、模態和動態響應對比分析，證實了局部幾何性應力集中對過早裂損也有一定影響。
  8. Prevention of fissured nitrogen hole in cast iron produced with resin sand

    樹脂砂生產鑄鐵件裂隙狀氮氣孔及其防止
  9. Metal poured into a mold cavity during the casting process solidifies with the possibility of shrinkage, segregation or porosity, which can prevent an " as - poured " casting from being acceptable for severe applications

    在鑄造過程中，澆鑄到模腔內的金屬在凝固過程中可能會產生收縮、分離或氣孔，這些問題使得「澆鑄」鑄件無法被苛刻環境應用領域所接受。
  10. In addition, imperfections like drag and gas holes were easy to turn out in the surface of epc casting for imperfect technology design, and this was verified by the actual castings

    同時發現，在消失模鑄件表面容易因殘余泡沫而造成表面渣氣孔，實際鑄件的表面質量也證明了這一點。
  11. Important advantages are still achieved in cycle time reduction and the ability to cast near net shape castings with minimal porosity

    最大的優點仍是減少生產周期，並且能鑄造出含有最少量氣孔的鑄件。