中文拼音 [gāolǐng]
高嶺土法 英文
kaoline methods
  • : Ⅰ形容詞1 (從下向上距離大; 離地面遠) tall; high 2 (在一般標準或平均程度之上; 等級在上的) above...
  • : 名1. (頂上有路可通行的山) mountain; ridge 2. (高大的山脈) mountain range 3. (專指大庾嶺等五嶺) the five ridges
  • : Ⅰ名詞1 (由國家制定或認可的行為規則的總稱) law 2 (方法; 方式) way; method; mode; means 3 (標...
  • 高嶺 : cao lamh
  1. Method for measurement of brightness of calcined kaolin in coal measures

    煤系煅燒白度測定方
  2. The kaolinite / acetate intercalation composites prepared by means mentioned in this paper can use as the intermedia for preparation of kaolinite / polymer nanocomposites directly

    通過本制備出的乙酸鹽插層復合物,可以直接用作聚合物納米復合物的中間體。
  3. An iron - containing material with an iron grade of over 20 % can be recovered from magnetic separation tailings of liuling iron mine by gravity method. this material can be used instead of partial clayey material to produce portland cement so as to reduce the mine tailings discharge amount to 43. 52 %, to raise the iron recovery from 70. 89 % to 84. 62 % and to reduce the iron ore powder consumption in raw cement mixture and the energy consumption of raw material grinding

    用重選從劉鐵礦磁選尾礦中回收鐵礦物,可獲得鐵品位大於20 %的含鐵物料,用此物料代替部分粘質原料生產硅酸鹽水泥,使礦山尾礦排放量減少至43 . 52 % ,鐵的回收率由70 . 89 %提到84 . 62 % ,並且減少了水泥生料配料中鐵礦粉的用量,降低了生料粉磨能耗。
  4. Abstract : an iron - containing material with an iron grade of over 20 % can be recovered from magnetic separation tailings of liuling iron mine by gravity method. this material can be used instead of partial clayey material to produce portland cement so as to reduce the mine tailings discharge amount to 43. 52 %, to raise the iron recovery from 70. 89 % to 84. 62 % and to reduce the iron ore powder consumption in raw cement mixture and the energy consumption of raw material grinding

    文摘:用重選從劉鐵礦磁選尾礦中回收鐵礦物,可獲得鐵品位大於20 %的含鐵物料,用此物料代替部分粘質原料生產硅酸鹽水泥,使礦山尾礦排放量減少至43 . 52 % ,鐵的回收率由70 . 89 %提到84 . 62 % ,並且減少了水泥生料配料中鐵礦粉的用量,降低了生料粉磨能耗。
  5. In this paper, using partly neutralized acrylic as monomer and kaolin as abio - filler, poly ( sodium acrylate ) / kaolin composite superabsorbent was prepared and its properties were studied

    摘要以部分中和的丙烯酸為單體,以為無機填充料,通過反相懸浮聚合合成出聚丙烯酸鈉復合吸水性樹脂。
  6. Introducing xrf analyzer, which can analyse quantitatively the content of each element in the clay quickly

    採用xrf能夠快速地對中各元素進行定量分析。
  7. Determination of the sediment volume of kaolin and calcined kaolin in coal measures

    煤系及其煅燒沉降體積測定方
  8. The factors influencing the viscosity property of kaolin pigment were introduced, followed by the modification methods, such as mechanical process, treatment with dispersant, etc

    摘要介紹了的黏度改進加工方,如機械加工,分散劑處理等。
  9. Considering energy conservation and effects of calcined kaolin on the strength of cement, it was optimum method to produce calcined kaolin by calcining it at 980 c for 0. 5h and then cooling it suddenly

    結合煅燒對水泥強度的影響,考慮到節約能源,以採用980恆溫0 . 5h然後快速冷卻的方作為最佳煅燒溫度與時間。
  10. Study on mechanism of separating kaolin and hematite using diffused reflection differential infrared spectroscopy

    用漫反射差示紅外光譜研究與赤鐵礦的分離機理
  11. Test method of kaolin clay physical properties

    物理性能試驗方
  12. The method of kaolin clay physical properties

    物理性能試驗方
  13. In this paper, we integrate properties of kaolinite, dimethylsulfoxide, and carboxylmethyl starch, proposing a novel way to improve electrorheological effect by intercalating. the experimental result are given as follows : 1 dimethyl sulfoxide / kaolinite hybrids were synthesized using an direct intercalation method and characterized by xrd and ftir

    有機插層復合物是一種新型納米復合材料,具有粘礦物和有機化合物的綜合性能,本項研究綜合了幾種廉價原料的特點,提出一種利用插層的方,改進電流變性能的思路。
  14. Kaolin clay chemical analysis

    化學分析方
  15. The research now mainly concentrate on polymer / montmorillonite nanocomposites. having typical layered structure, kaolinite and montmorillonite are all ideal host minerals for preparing polymer / layered silicate nanocomposites by intercalation composite method

    與蒙脫同屬于層狀硅酸鹽,兩者都具有典型的層狀結構,是用插層復合制備聚合物層狀硅酸鹽納米復合材料理想的主體礦物。
  16. Determination of the function in suspension of kaolin and calcined kaolin in coal measures

    煤系及其煅燒懸浮性能測定方
  17. The activated alumina content had a reduce with time prolonging from 2h to 5h at calcined temperature of 1000 c. the research results also revealed that products obtained by sudden cooling from high temperature had a higher content of activated alumina than that by cooling naturally

    1000時煅燒中活性氧化鋁的含量在煅燒時間2h 5h隨煅燒時間的延長還有所下降。另外,煅燒后採用急冷方比採用自然降溫方中制得的煅燒具有更的活性氧化鋁含量。