high strength sinter
  • 高 : Ⅰ形容詞1 （從下向上距離大; 離地面遠） tall; high 2 （在一般標準或平均程度之上; 等級在上的） above...
  • 強 : 強形容詞（強硬不屈;固執） stubborn; unyielding
  • 度 : 度動詞[書面語] （推測; 估計） surmise; estimate
  • 燒 : Ⅰ動詞1 （使東西著火） burn 2 （加熱或接觸某些化學藥品、放射性物質等使物體起變化） cook; bake; hea...
  • 結 : 結動詞（長出果實或種子） bear （fruit）; form （seed）
  • 礦 : 名詞1. （礦床） ore [mineral] deposit 2. （礦石） ore 3. （開采礦物的場所） mine
  • 高強度 : high strength高強度部件 high strength parts; 高強度材料 high strength material; 高強度磁場 high i...
  • 高強 : excel in; be master of
  1. In recent years at iron - making plant of pangang, the coke ratio of pig iron has reduced evidently by insisting on “ burden preparation ” course, improving quality of sinter, raising wind temperature, increasing rich oxygen quantity and injecting abundant pulverized coal into bf. the solid fuel consumption of sinter has been decreased greatly through insisting on using high - quality calces, practising high feed sintering, actualizing many techniques in solving key problems. at the same time, the energy source base management has been strengthened, and energy - saving work has made great progress, profits generated by energy - saving have exceeded a hundred million yuan

    近年煉鐵廠通過堅持「精料」方針，改善燒結礦質量，提高風溫，增大富氧，實施大噴煤，使入爐焦比有明顯下降；燒結堅持用好生石灰，推行厚料層燒結，實施多項技術攻關，固體燃耗大幅度下降；同時加強能源基礎管理，節能工作取得長足進步，節能創效益1億元以上。
  2. In the suitable distribution condition of sinter mixture, the utilization coefficient of sinter machine would be raised, the solid fuel consumption would be reduced and the strength of sinter ore would be raised in micropellet sinter processing

    在適宜的布料條件下，小球團燒結時採用燃料分加工藝可提高燒結杯利用系數、降低燒結礦固體燃料消耗量並提高燒結礦強度。
  3. Some tests for liangang sinter adding bos slag have be done in the laboratory and plant trial. the results show that in the range of bos slag percentage, from 0 % to 8 %, with the increase of bos slag percentage, the sinter speed has been lower, but the sinter strength and productivity of sinter product have been higher, the sinter productivity will be the maximum when bos slag percentage is 4 % ; the siner reducibility has been improved, the normal operation of bof will not be effected anymore because of the circulation of p form bos slag

    對燒結礦配加轉爐鋼渣進行了實驗室研究和工業試驗，在鋼渣配比0 % 8 %的范圍內進行的研究表明：隨著鋼渣配比的增加，燒結速度稍有下降，燒結礦強度、燒結成品率均有所提高，利用系數在4 %左右時達到最大值；燒結礦還原性得到改善；鋼渣中帶入的p的循環富集不會影響煉鋼的現行操作。
  4. Abstract : experiments indicated that under tanggang material conditions and at the basicity range of 1. 4 1. 7, the sinter tumbler strength and reduction desintegration properties were worsen as australian fine ores added ; but at the basicity range of 0. 4 0. 6, the sinter strength can improved with both adding of indian fine ores or australian fine ores

    文摘:試驗表明：在唐鋼原料條件下，堿度1 . 4 1 . 7范圍內，配加澳粉礦使燒結礦強度和低溫還原粉化性能下降，印度粉礦影響不明顯;在堿度0 . 4 0 . 6范圍內，配加印度粉礦和澳粉礦都有利於燒結礦強度的提高。