  1. There is correspondence in evaluating sulfate resistance of cement paste by three test methods such as rapid boiling, gypsum mixing and wet - dry test. high strength grade cement can meliorate property of sulfate resistance

    外摻石膏法、干濕交替法以及快速沸煮法三種實驗方法對評價水泥砂漿的抗硫酸鹽侵蝕性能有較好的一致性；高標號水泥品種對抗硫酸鹽侵蝕性能有很好的改善作用。
  2. Available in moderate sulfate - resistant ( msr ) and high sulfate - resistant ( hsr ) grades. this product is intended for use as a basic well cement

    有中抗硫酸鹽型（ msr ）和高抗硫鹽鹽（ hsr ）兩類，是一種基本油井水泥。
  3. With the addition of the mineral additives, the structure of the cement paste can be improved and the resistance of sulfate attacks can be advanced

    摻入摻和料可以改善水泥漿體的結構，明顯提高混凝土的抗硫酸鹽侵蝕能力。
  4. The relation between addition content of calcined kaolin, aluminium powders and aluminum sulfate in concrete and compressive strength, slump constant, 30min slump and permeability altitude were studied, and according to the experiment results, the component percent contents of crack - resistant and water - repellent admixture in cement were determined as following : calcined kaolin 6 %, aluminum sulfate 4 % and aluminium powders 0. 005 %

    通過對煅燒高嶺土、鋁粉、硫酸鋁在混凝土中摻量對其抗壓強度、初始武漢理工大學碩士學位論文坍落度、 3omin坍落度保留值及透水高度的影響，確定了配製抗裂防水外加劑的各組成成分以其占水泥質量的百分比分別為:鍛燒高嶺土6 % ，硫酸鋁4 % ，鋁粉為0 . 005 % 。
  5. The calcined kaolin, aluminium powders and aluminum sulfate were used as components of water - repellent agent, which effects on cement hydration and concrete impermeability were discussed in this paper

    本文以煅燒高嶺土、鋁粉、硫酸鋁作為防水劑的組份，研究了它們對水泥水化及混凝土的抗滲性的影響。