tacky slurry-
According to each ingredients ( water retaining admixture, polymer, inorganic mineral ) " effect to mortar ' s behaviors ( water relentivity, strength, contractility ) in exclusive mortar " s composite addition, the text defines each ingredient ' s quantity scope, then define the mix through cross experiment. we compared the aac exclusive mortar ' s behaviors such as water relentivity, compressive strength, binding strength, shrinkage, flexural strength and others to ordinary mortar ' s ones, it turn out to be that there is much improve in former ' s behaviors such as water relentivity, compressive strength, binding strength, shrinkage, flexural strength etc, it also shows that the aac exclusive mortar can improve the crack in aac brick walling to a certain degree
並根據專用砂漿中復合外加劑的各個組分(保水劑、聚合物、無機礦物等)對砂漿主要性能(保水性、強度、收縮性、抗彎性等)的影響來確定每個組分的摻量范圍,再通過正交實驗確定最佳配合比,然後就普通砂漿與專用砂漿的保水性、抗壓強度和粘結強度、收縮值、抗彎曲性能以及其它性能進行了對比,對比結果表明專用砂漿的保水性、抗壓強度和粘結強度、收縮值、抗彎曲性能以及其它性能較普通砂漿都有了很大的提高,說明加氣混凝土砌塊專用砂漿在一定程度上可以改善加氣混凝土砌塊墻體的開裂情況。In the aspect of improving the cracking feature, compatibility and flexibility, the author has done experiments, including strength, modulus of elasticity experiments, and design some experiments similar to the practical structure and circumstance including adhesion strength between fresh mortars and old ones, between mortar and polystyrene board, mortar shrinkage in concrete circle, mortar shrinkage at different strength and different polymer - cement ratio, and temperature deformability at different strength and different polymer - cement ratio on mortars, on different type of formwork and on mortars with different type of formwork
在改善砂漿抗裂性、提高柔韌性和協調變形能力方面,進行了不同聚合物摻量的強度試驗、彈性模量試驗;設計了與模網混凝土實際結構和情況相接近的新老砂漿粘結強度試驗、砂漿與苯板的粘結試驗以及混凝土環中的砂漿收縮試驗;進行了不同強度、不同聚合物摻量下的砂漿干縮變形試驗、溫度變形試驗,以及不同結構形式的鋼網自身溫度變形試驗和配有鋼網的砂漿溫度變形試驗。This product can disperse in water, increase the adhesion between mortar and its substrates, and improve the mechanic property and manageability of mortar
該產品可在水中分散,提高砂漿與普通支撐物間的粘著力,改善砂漿機械性能。The result of macro - quality experiments show : mineral admixtures markedly slow the hydrating velocity of cement slurry, decrease and delay the hydrating max - temperature, in which steel slag is more effective ; expansive agents compensate concrete shrinkage, enhance the concrete dense degree, strengthen the interfacial layer between fiber and cement matrix and improve the physical mechanics qualities of acic ; minimal admixtures markedly improve the concrete workability property, increase the concrete later intensity & density and the capability of anti - chemical attack and anti - permeability ; hybrid fiber reinforces the toughness of obviously acic by the means of anti - cracking effect of fiber with different sizes and different properties in the corresponding construction levels
實驗結果顯示:鋼渣摻合料能顯著減緩水泥漿體水化速率,降低砂漿的水化溫升並延遲最高溫升時間;補償混凝土收縮,提高混凝土密實度,加強纖維與水泥石的界面粘結,增強混凝土力學性能,但不能明顯改善混凝土韌性。混雜纖維通過纖維的不同尺度與不同性質在相應的結構層次上產生阻裂效應,增韌鋼渣防滲抗裂混凝土;增加混凝土的破壞極限能,極大提高混凝土抗彎曲能力和韌性指數,改善混凝土脆性。Based on the study result, the paper has made a systematic study on the compounding and performance of binding mortar. compared with tradition binding mortar, this new type binding mortar has better performance of water resistance, frost resistance and crack resistance, etc
研究結果表明,新型粘結砂漿具有比傳統粘結砂漿更優良的性能:和易性改善,粘接強度、耐水性以及抗裂性顯著提高,抗凍性良好,從而保證了新型粘結砂漿具有良好的耐候性。In order to overcome the disadvantages of traditional binding mortar, in this paper new type binding mortar, has been developed in the paper, by adding polymer into mortar to improving the wetting binding strength and durability of mortar the key techniques of compounding binding mortar are how to reduce the polymer - cement ratio of binding mortar, and how to improve the creak resistance of binding mortar
針對傳統粘結砂漿施工和易性差、粘結力低、耐久性差、用於粘貼外墻飾面磚易剝落等問題,本文採用在砂漿中摻入一定量的聚合物的方法,以提高砂漿的粘結力和砂漿的耐久性為突破口,開發出來了一種性能優良的新型粘結砂漿。Two kinds of polymer modified mortar with good toughness and high bond strength were produced by investigating how five different polymers affect mortar mechanical performance ( the compressive strength, the flexural strength, the ratio of flexural strength to compressive strength, the bond strength ) in different polymer content and in different curing condition
通過系統研究五種不同的聚合物及不同的摻量對砂漿力學性能的影響(抗壓強度、抗折強度、折壓比、粘結強度) ,不同的養護制度條件下力學性能的變化情況,本文得到了兩種具有韌性好、粘結強度高的聚合物改性砂漿。To significantly improve both strength and durability of repair interfacial layer between old and new concrete, two attempts were firstly put forward in this thesis : ( 1 ) a kind of new modified primer would be produced by introducing shrinkage reducing admixture into cement mortar, which may both reduce the shrinkage of the interfacial layer, and lessen the content of large crystal in the repaired interface layer, accordingly, remarkably increase the van der waals force of interfacial layer
為大幅度提高新老混凝土修補界面層的強度和耐久性,本文首次提出並實現兩個設想: ( 1 )以國產減縮劑為外加劑,配製新型改性水泥砂漿界面劑。該界面劑既能減少界面層宏觀干縮裂縫,又不增加大晶體,使界面層形成密實的微細觀結構,顯著提高粘結界面層內晶體間的范德華力。分享友人