acid leaching section中文意思是什麼

acid leaching section解釋
酸浸工段

  • acid: adj. 1. 酸味的。2. 【化學】酸的,酸性的。3. 〈比喻〉尖酸刻薄的,易怒的。n. 1. 酸味物。2. 【化學】酸。adv. -ly ,-ness n.
  • leaching: 焊散漂出,熔出
  • section: n 1 (外科、解剖的)切斷;切割;切開。2 【外科】切片,【金相】磨石。3 (果子的)瓣。4 【數學】截...

※英文詞彙acid leaching section在字典百科英英字典中的解釋。

  1. Some main results of testing research were as fellows : i. in the course of testing of leaching zinc dross, leaching zinc dross by sulfuric acid was researched and the effects on the leaching rate of the zinc dross were analyzed by author, the optimum conditions of leaching testing of zinc dross were determined as fellows : liquid - solid ratio 6 : 1, stirring ratio 250r / min, granularity 120 mesh, the soaking time 5h, the concentration of sulfuric acid of 30 %, and under these conditions, the rate of leaching zinc is above 92. 0 %. ii. in the course of testing of purification, on the basis of comprehending and comparing all present methods of the manganese - removal and iron - removal, the oxidizing method of manganese - removal in zinc sulfate solution using ammonium persulfate was put forward and the oxidizing method of iron - removal in zinc sulfate solution using the goethite process and oxidation - hydrolysis process was adopted

    研究的主要結果具體如下: 1 、研究了硫酸浸出鋅浮渣並分析了影響浸出率的各種因素,確定了浸出鋅浮渣的最佳條件為:液固比為6 : 1 ,攪拌速度為250r min ,粒度為- 120目,酸浸時間為5 . 0h ,硫酸濃度30 ,鋅浮渣的浸出率大於92 . 0 ; 2 、在綜合和比較了目前除錳和除鐵的各種方法基礎上,提出了過硫酸銨氧化除錳方法和選擇了針鐵礦-氧化水解聯合法除鐵方法,並分析和討論了影響除錳率和除鐵率等各種因素,確定了除錳的條件為:溫度90 , ph值5 . 4 ,反應時間3h ,過硫酸銨達到理論值的1 . 2倍,除錳率超過99 . 86 ;聯合法除鐵的條件為:氧化反應時間1 . 5小時、溫度控制在90 92 、 ph值5 . 2 5
  2. In this paper, the progress of in - situ leaching technique is summarized, the characteristics of in - situ weak - acid leaching technique of uranium are discussed, and the leaching mechanism and technology, layout size of injecting and pumping holes, selection and acidity of lixiviant, the determinations of acid consumption and leaching time for in - situ weak - acid leaching of uranium are studied

    摘要總結了地浸技術的發展,論述了低酸浸出采鈾技術的特點,對低酸地浸采鈾的浸出原理和工藝、鉆孔網度、浸出液的選擇及其酸度、耗酸量和浸出時間的計算進行了研究。
  3. By calcining low humidity pelleted kaolin, a kind of metakaolin pellet, inside which the macroporous structure developed , has been prepared. the structure remarkbly benifits reactant ion transference. so, the variety has high acid leaching reactivity, even coarse as the pellets are, its reaction kinetic is still maintained zero order up to a significant conversion rate

    在用鹽酸加熱浸取時,該類球粒內的鋁質組分表現出高酸溶反應活性,不同粒級的該類球粒有相似的浸出率時間曲線,且大部分鋁能被迅速浸出。
  4. Experimental research on increasing white degree of coating material made from coal gangue by acid leaching

    採用酸浸法提高煤矸石制取造紙塗料白度的試驗研究
  5. Study on the optimum reaction parameters of red soil acid - leaching

    紅土酸浸的最佳條件研究