添加電鍍；附加電鍍層-
Reshi chemicals is a specialist in manufacturing and distributing metal surface treatment reagent : phosphorus treatment reagent, water treatment reagents, electro - plating additive reagents, normal temperature nigrescence reagent, pre - treatment reagents, etc
是一家專業從事金屬表面處理藥劑：磷化處理藥劑、水處理劑、電鍍添加劑、鋼鐵常溫發黑劑以及前處理產品的生產商和代理商。 -
Meanwhile, fundamental principles about electroless tin plating by reducing agent and disproportionation reaction were explained. function of every component in the bath was explained that complexing agent can effectively change the potential of copper and tin, and accelerate the beginning of replacement reaction favorably ; reducing agent can increase the rate of chemical reaction and has the effect of promoting reaction dynamics too ; antioxidant can effectively prevent sn2 + in the bath from being oxidated ; additive agent a can improve the stability of the bath ; additive agent b has such effects as refining and brightening for the tin deposits, and it enlarges the range of brightening section ; additive agent c used as leveling agent can not only make the depostis level off, but also improve the dispersive ability of the bath ; surface - active agent can solve bubble problem which gathered on the surface of the deposits, and improve the surface quality of the deposits and the bath stability
闡述了鍍液中各組分的作用：絡合劑能有效地改變銅、錫的電位，促使初期的置換反應順利進行；還原劑能加快化學反應速度，對反應動力學有積極的促進作用；抗氧化劑能有效地防止鍍液中sn ~ （ 2 + ）的氧化；添加劑a能提高鍍液的穩定性，添加劑b對鍍層能有細化和光亮作用，擴大了鍍層光亮區的范圍；添加劑c作為平滑劑，不僅能增強鍍層表面的平整性，而且能提高鍍液的分散能力；表面活性劑較好地解決了化學鍍過程中汽泡在鍍件表面聚集的問題，提高了鍍層的表面質量和鍍液的穩定性。 -
The formulae that didn " t contain fluorine had low rates of corrosion, high stability and easy operation and had distinct improvement in coating quality, surplus of chromium, saving electricity and energy and environmental protection etc. when they were compared with the commercial additive of wr - 1 and the electrolyte formula of fenghui galvanization plant, the results showed that the effect of chromium plating of the formulae obtained in this study are more excellent
所研製的配方，不含氟、腐蝕率低，穩定性好，易操作，在鍍層質量、節鉻、節電、節能、環境保護諸方面都有明顯的改善，並將其與市售的wr 1添加劑和淬惠電鍍廠鍍鉻效果進行了對比，結果表明本研究得到的配方鍍鉻效果更優良。 -
On the basis of electroplating and immersion plating tin, and through large numbers of experiments, a new process of electroless plating tin in acid chloride bath solutions including sncl2 2h2o, nah2po2 h2o, special complexing agent, additive agent, stabilizing agent and antioxidant, was established. continuous self - catalyzed deposition of tin on copper substrate was achieved successfully, and half - bright and silvery - white tin deposits with excellent properties were obtained
本文是在電鍍錫、浸鍍錫工藝配方的基礎上，通過大量的試驗，確立了一種以氯化亞錫、次亞磷酸鈉和特定的絡合劑、添加劑、穩定劑，抗氧化劑為基本鍍液組成的酸性氯化物化學鍍錫體系，成功地在銅上實現了錫的連續自催化沉積，獲得了性能優異的半光亮銀白色錫鍍層。 -
The relationship between leveling in nickel plating and additive molecular connectivity index was studied. the experimental results were compared with the data predicted from the relation
摘要研究了鍍鎳添加劑的分子連接性指數與平滑能力的關系，得到了定量的函數關系式，並用此關系式對一些添加劑的平滑能力進行預測，與實測值進行對照，結果令人滿意。