air-content ratio
解釋
空氣含量比-
Under the different freezing - thawing cycle circumstance, three factors of water binder ratio, air content and mineral admixture are analyzed by using the method of orthogonal table. the test results show that the chief influencing factor is the water binder ratio in water freezing - thawing cycle circumstance, and in salt freezing - thawing cycle circumstance is the air content. this could illustrate that entraining air into concrete can improve the frost resistance of concrete effectively in salt freezing - thawing cycle
分析了在純水和3 . 5 % nacl溶液中受凍后，水膠比、含氣量和摻合料對混凝土飽和系數及變化速率的影響規律，試驗結果表明水膠比對混凝土水凍時的飽和系數及變化速率影響顯著，而鹽凍情況下含氣量則是主要影響因素，說明引氣能顯著提高混凝土的抗鹽凍性能。 -
According to relative criteria, the performance of ash - jd such as ratio of water - reducing, ratio of compressive strength, effect of enhancing strength, ratio of bleeding, air entrainment content, effect of keeping slump value, compatibility with cement, resistance to concrete shrinkage and damage by freezing and thawing and impermeability to water etc are all equal to the traditional aminosulfonic - based superplasticizers, and the ratio of performance to price is better than naphthalene series superplasticizers
按照相關標準，對產品進行了測試，所開發的低成本改性氨基磺酸鹽高效減水劑ash - jd的各項性能如減水率、抗壓強度比、增強效果、引氣性、坍落度保持效果、與水泥適應性、收縮性能、抗凍融性能、抗滲性能等相當于傳統氨基磺酸鹽高效減水劑，性能價格比優于萘系高效減水劑。 -
The research results show that aggregate gradation and the nominal maximum aggregate size evidently influence the shear resistance of asphalt mixture ; aggregate flakiness content influences the shear resistance of asphalt mixture, and with the increase of aggregate flakiness content the shear resistance of asphalt mixture decreases ; asphalt binder properties, especially penetration, softening point and viscosity influence the shear resistance of asphalt mixture, and the latter increases with the decrease of penetration and the increase of softening point and viscosity ; asphalt content influences shear resistance of asphalt mixture, and with the increase of binder / aggregate ratio the shear resistance of asphalt mixture decreases ; air void influences shear resistance of asphalt mixture, and usually with the increase of air void the shear resistance of asphalt mixture decreases ; homogeneity does not have a direct and obvious relationship with absolute value of shear resistance of asphalt mixture, but does with variation of shear resistance of asphalt mixture
研究結果表明：集料級配和公稱最大集料粒徑對瀝青混合料抗剪強度有顯著的影響；瀝青混合料抗剪強度受其集料中針片狀含量的影響較大，集料中針片狀含量增大，瀝青混合料抗剪強度減小；結合料的性質，特別是針入度、軟化點和粘度對瀝青混合料抗剪強度有較大的影響，隨著針入度減小，軟化點和粘度增大，瀝青混合料抗剪強度增大；含油量對瀝青混合料抗剪強度有較大影響，隨著油石比的增大，瀝青混合料抗剪強度減小；瀝青混合料抗剪強度受其空隙率的影響較大，一般隨著空隙率的增大，其抗剪強度減小；瀝青混合料均勻性與瀝青混合料抗剪強度絕對數值間沒有明顯的關聯，而與數值間的變異性有著很好的相關性。 -
This means the saturation degree of concrete is different. by means of analyzing the l9 ( 34 ) orthogonal table, the air content is the chief factor, the second factor is water binder ratio and the third is mineral admixture in both high water pressure and low water pressure. the water saturation degree of concrete in damaging point ( e6 / e0 = 60 % ) can be found by measuring the dynamic modulus of elasticity after six freezing - thawing cycles
採用l9 （ 34 ）正交表對水膠比、含氣量和摻合料三個因素進行分析，試驗結果表明:在自然情況下，影響混凝土水飽和系數的主要因素是水膠比，而影響混凝土在鹽溶液中飽和系數的主要因素則是含氣量;在水壓力作用下，無論壓力大小，混凝土水飽和系數的影響次序依次為含氣量、水膠比、摻合料。 -
By using the method of orthogonal table, the water binder ratio, air content and mineral admixtures which affect the saturation degree are analyzed in this paper. meanwhile in freezing and thawing cycle circumstance including water environment and 3. 5 % nacl liquor, the saturation degree and the saturation rate are also analyzed. moisture content of the concrete is different by varying water pressure
本文採用正交分析方法，研究了自然飽水和壓力飽水條件下水膠比、含氣量和摻合料三個因素對混凝土飽和系數的影響規律，並研究了混凝土在純水和3 . 5 % nacl溶液中受凍后飽和系數的變化規律。 -
By testing according to correlation criterions, the performances of jd such as ratio of water - reducing, ratio of compressive strcngth, effect of accelerating and enhancing strength, ratio of bleeding, air entrainment content, effect of keeping slump value, compatibility with cement, resistance to concrete shrinkage and damage by freezing and thawing and water - tightness etc are all better than that of the traditional melamine resin superplasticizer sm and naphthalene series superplasticizer fdn
按照相關標準進行測試，所開發的改性密胺樹脂高效減水劑的各種性能如減水率、抗壓強度比、早強增強效果、泌水率、引氣性、坍落度保持效果、與水泥適應性、收縮性能、抗凍融性能、抗滲性能等都遠遠優于傳統的三聚氰胺高效減水劑sm ，也優于萘系高效減水劑fdn 。 -
The condensation heat - exchange characteristic of a separate - type heat - pipe was studied on a 1 : 1 model. the heat pipe is heated by electricity, and working fluid is distilled water, and it is cooled by air. the experimental results show that, ( 1 ) when charging liquid ratio is 45 %, condensation heat - exchange coefficient reaches to maxium ; ( 2 ) when there is not non - condensing gas, the coeffcient decreases a little with the increase of vapour pressure, and it decreases by 9. 5 % when the pressure increases from 0. 16mpa to 0. 36mpa ; ( 3 ) when there is non - condensing gas, the coefficient decreases a little, but when the gas is discharged by an exhaust value, it can be improved, when the volume content of the gas is 2. 5 %, it can increased by 22 % ; ( 4 ) the effect of the non - condensing gas on the coefficient decreases with the increase of the pressure, and when the volume content of the gas is 5 % and the pressure increases from 0. 16mpa to 0. 36mpa, the coefficient increases by 6 %. the relative curves are given between condensation heat - exchange coefficient and air flowrate, charging liquid ratio and vapour pressure
建立了空氣冷卻實驗臺，熱管的加熱方式為電加熱，工質為蒸餾水.在1 1模型上對分離式熱管管內凝結換熱特性、不凝性氣體對凝結換熱的影響及不凝性氣體的擴散規律進行了試驗，得出分離式熱管有一最佳充液率，其值為45 %左右；凝結換熱系數隨著蒸汽壓力的增加略有降低，在實驗的壓力范圍內，降低了9 . 5 % ；不凝性氣體對分離式熱管的凝結換熱僅影響冷凝段下部較小部分，通過排氣閥排出不凝性氣體可有效地改善冷凝段下部的凝結換熱；隨著壓力的增加，不凝性氣體對分離式熱管冷凝段的影響減少.這些結論可用於分離式熱管換熱器的工程設計和控制 -
Abstract : the condensation heat - exchange characteristic of a separate - type heat - pipe was studied on a 1 : 1 model. the heat pipe is heated by electricity, and working fluid is distilled water, and it is cooled by air. the experimental results show that, ( 1 ) when charging liquid ratio is 45 %, condensation heat - exchange coefficient reaches to maxium ; ( 2 ) when there is not non - condensing gas, the coeffcient decreases a little with the increase of vapour pressure, and it decreases by 9. 5 % when the pressure increases from 0. 16mpa to 0. 36mpa ; ( 3 ) when there is non - condensing gas, the coefficient decreases a little, but when the gas is discharged by an exhaust value, it can be improved, when the volume content of the gas is 2. 5 %, it can increased by 22 % ; ( 4 ) the effect of the non - condensing gas on the coefficient decreases with the increase of the pressure, and when the volume content of the gas is 5 % and the pressure increases from 0. 16mpa to 0. 36mpa, the coefficient increases by 6 %. the relative curves are given between condensation heat - exchange coefficient and air flowrate, charging liquid ratio and vapour pressure
文摘:建立了空氣冷卻實驗臺，熱管的加熱方式為電加熱，工質為蒸餾水.在1 1模型上對分離式熱管管內凝結換熱特性、不凝性氣體對凝結換熱的影響及不凝性氣體的擴散規律進行了試驗，得出分離式熱管有一最佳充液率，其值為45 %左右；凝結換熱系數隨著蒸汽壓力的增加略有降低，在實驗的壓力范圍內，降低了9 . 5 % ；不凝性氣體對分離式熱管的凝結換熱僅影響冷凝段下部較小部分，通過排氣閥排出不凝性氣體可有效地改善冷凝段下部的凝結換熱；隨著壓力的增加，不凝性氣體對分離式熱管冷凝段的影響減少.這些結論可用於分離式熱管換熱器的工程設計和控制
分享友人