The curing kinetics parameters of up with lwt % organic montmorillonite were determined by the dynamic dsc. its apparent activation energy is higher than pure up ' s, but reaction order is similar. these results show the addition of organic montmorillonite increase difficulty degree of curing reaction
採用非等溫dsc法計算出的含有機蒙脫土1wt的不飽和聚酯樹脂的表觀反應活化能和固化溫度高於不飽和聚酯樹脂，但反應級數基本沒有變化，說明加入有機蒙脫土使樹脂的固化反應難度增大。 -
The thermal decompostion kinetics of up / montmorillonite nanocomposites under nitrogen was studied. the reaction order and apparent activation energy of nanocomposites were obtained by freeman - carroll method. the results indicate the thermal stability of nanocomposites is higher than pure up ' s
研究了氮氣氣氛下不飽和聚酯蒙脫土納米復合材料的熱分解動力學，用freeman - carroll法確定了復合材料的反應級數n和表觀反應活化能e 。 -
At the same clay content, the properties of acr / mmt / pvc composites were superior to those of pvc and acr, mmt mixture prepared by means of melt mixing. it is because the montmorillonite was dispersed homogeneously in the composites with nano - dimension. the apparent kinetics of the polymerization process was firstly studied by conventional gravimetric methods in this thesis
還現發在蒙脫土加入量相同的情況下，採用復合物進行共混的pvc樹脂，其力學性能要明顯好於採用熔融共混直接制備的聚氯乙烯/蒙脫土復合材料，這主要得益於無機蒙脫土acr復合物中就已經呈納米級分散，其在pvc中的分散狀態要比熔融共混均勻的多。 -
The value of d001 was increased by 1. 1 nm after modification indicated by xrd. the influencee factors of the apparent kinetics of the decomposition rates of aiba and the influence of montmorillonite on the rate of emulsion polymerization were studied. nanostructured methyl methacrylate - n - cyclohexylmaleimide copolymer / montmorillonite composites were prepared by bulk and emulsion methods and the characterization of dsc tga tem xrd optic properties and mechanics properties were carried out
考察了aiba表觀分解速率的影響因素並研究了mmt對乳液聚合反應速率的影響，在此基礎上，用乳液法與本體法制備了p （ mma ? chmi ） ommt納米復合材料，並對納米復合材料進行了dsc 、 tga 、 tem 、 xrd 、光學性能、力學性能等測試。