Beryllium powders with the same particle size and various contents of beo were prepared by pre - sintering - acid washing processes initiatively and the influence of beo alone on o mys of beryllium was observed and some new results have been obtained - compared with the content of beo, the distribution of beo in beryllium has more critical influence on mys ; finely dispersed beo along the grain boundaries and in the matrix results in the dispersion strengthening of beryllium matrix and thereby the higher mys value ; on the contrary, the coarser beo particles clustering on the grain boundaries results in negative influence on o mys
開創性地用預燒結? ?酸洗工藝制備了相同粒度、不同beo含量的鈹粉，從而開展了beo含量單獨對鈹材_ （ mys ）影響的研究，得出一些新的結果：與beo含量相比， beo在鈹中的分佈狀態對_ （ mys ）的影響更大。沿晶界、晶內彌散分佈的較細小beo對基體鈹有彌散強化作用，使_ （ mys ）即較高；如果beo較粗大地成簇狀聚集在晶界，反而對_ （ mys ）有不良的影響。 -
So, decide which one youx want to beo - and stick with it
因此，決定哪一個你想成為-堅持它。 -
The hiped beryllium material has higher mys value because of not only its lower consolidation temperature and higher consolidation pressure but also the more uniformly and finely dispersed distribution of its beo phase
靜壓鈹材由於其細小均勻beo的彌散分佈，加上在較低溫度和高壓下成形固結，從而_ （ mys ）較高。 -
The test result of the beryllium materials with medium beo content and high strength and high elongation showed that the mys value of a kind of hot - pressed beryllium material of 2. 5 % beo and produced at 1070 ? reaches 71mpa, and its elongation is up to 3. 52 %, 17 % higher than american 1 - 250 hiped beryllium material with the same beo content
5的鈹材，其_ （ mys ）達到71mpa ，且延伸率達到3 52 。延伸率超過了同樣beo含量的美國i - 250靜壓鈹材17 ，為今後用靜壓方法制備綜合性能全面達到和超過i - 250鈹材進行了有益的探索。 -
Preparation and properties of beo - al2o3 ceramic
3陶瓷制備及性能研究 -
The test has also shown that the purer hot - pressed as well as hiped beryllium materials with less content of fe and al impurities mainly consist of two phases - the matrix beryllium and the second phase of beryllium oxide ( beo )
實驗還發現，含fe 、 a1等雜質較少的較高純度的熱壓和靜壓鈹材主要由基體鈹和氧化鈹（ beo ）第二相組成。