blending agent 中文意思是什麼
blending agent
解釋
調合劑-
New silicone flame retardant potting compound was prepared by blending of ltv silicone rubber as base gum with diluent, crystalline quartz filler, chain extension agent, crosslinking agent, inhibitor, carbon black and platinum catalyst
以中溫硫化硅橡膠（以下簡稱ltv硅橡膠）為基膠，混入稀釋劑、石英粉、鏈增長劑、交聯劑、阻聚劑、炭黑及鉑催化劑等組分，制得新型有機硅阻燃灌封料。 -
Abstract : new silicone flame retardant potting compound was prepared by blending of ltv silicone rubber as base gum with diluent, crystalline quartz filler, chain extension agent, crosslinking agent, inhibitor, carbon black and platinum catalyst
文摘:以中溫硫化硅橡膠（以下簡稱ltv硅橡膠）為基膠，混入稀釋劑、石英粉、鏈增長劑、交聯劑、阻聚劑、炭黑及鉑催化劑等組分，制得新型有機硅阻燃灌封料。 -
The preparations, drilling rig adjustment, pile distribution control, mixing verticality control, elevation measurement, elevation control of pile top and column bottom, curing agent choice and control of mixing speed and blending quantity, must be done well for strengthening soft soil foundation by mixing cement with soil in construction
在實踐中要做到6點： 1 ）調整好鉆機； 2 ）控制好柱的分佈位里與攪拌軸的垂直度； 3 ）測量好高程； 4 ）控制好樁頂、柱底高程； 5 ）選擇好固化劑； 6 ）控制好攪拌速度和摻加量。 -
The results showed that polygorskite / nbr composite made by mechanical blending was nano - composite, the properties of nbr composite filled with 35 quantities of polygorskite were tantamount to those filled with 30 quantities of half - reiforced black carbon, and properties of polygorskite / nbr composite could be improved by using coupling agent silane to modify polygorskite
試驗表明：機械共混能夠使坡縷石與丁腈橡膠達到納米級復合；坡縷石用量達35份時其補強效果與30份半補強碳黑相當；用硅烷偶聯劑等對坡縷石進行改性，可以改善坡縷石與丁腈橡膠復合材料的物理機械性能。 -
The influence of retarder on the seaing time and ultimate strength of gypsum plaster was investigated in this paper. the experimental results indicate that the effect of single retarder, such as citric acid, is inferior to that of composite retarder which was made of blending citric acid with a few portland cement ( about 0. 5 ?, by weight ). the effect of different water - retention agents, such as polyvinyl alcohol ( pva ), carboxymethyl cellulose ( cmc ), and na - bentonite, etc., was also studied, and the results demonstrate that by means of adding organic and inorganic water - retention agent simultaneously the water - retention of plastering slurry can obviously be improved. the optimal mix proportion of gypsum plaster suitable to finish coat of walls and ceilings of buildings has been got by use of factorial experiment with orthogonal array accounting for interactions between factors each other
研究了分別以檸檬酸、檸檬酸與普通硅酸鹽水泥復合物作緩凝劑，調節粉刷石膏的凝結時間，並對比2種緩凝體系對石膏抗折、抗壓強度的影響.比較不同保水劑（聚乙烯醇、羧甲基纖維素）以及相同量的保水劑在不同工藝流程下保水效果上的區別.探索了有機保水劑和無機保水劑對粉刷石膏的保水性的影響.結果表明，檸檬酸與普通硅酸鹽水泥的復合緩凝劑比單純的檸檬酸更能有效地延緩建築石膏的凝結，同時建築石膏的抗折、抗壓強度降低幅度減小