branched polyethylene 中文意思是什麼
-
Long chain branched polyethylene
長支鏈聚乙烯 -
The crystallization and melting behavior of mellocene - catalized branched and linear polyethylenes of low molecular weight was studied. it was found that the crystalline lattice of branched polyethylene is larger than that of linear polyethylene because of the existence of branched chains. the melting behavior of branched polyethylene is similar to that of linear polyethylene since the branched chains can not enter the lattice. however, the crystalline behavior of low molecular weight branched polyethylene is the same as that of high molecular weight linear polyethylene, but different with that of low molecular weigh linear polyethylene. kinetics theory analysis evidenced that the transition temperature of growth regime of the branched polyethylene is about 20 lower than that of linear polyethylene with the same molecular weight. it may be attributed to the existence of short branched chains
研究了金屬茂催化的低分子量支化聚乙烯和線性聚乙烯的結晶及熔融行為，發現支化聚乙烯的結構與線性聚乙烯相同為正交結構，但晶格略有膨脹.支鏈的存在對熔融行為影響不大，兩種聚乙烯的熔點均隨結晶溫度的升高而非線性增加，表現出低分子量樣品的共同特徵.但支鏈的存在對結晶行為卻有很大的影響，主要是由於支鏈的存在降低了晶體的結晶速率從而影響結晶過程，使得低分子量的支化聚乙烯的結晶行為與高分子量線性聚乙烯的結晶行為相似而與低分子量的線性聚乙烯不同.動力學分析表明，低分子量的支化聚乙烯的結晶生長方式的轉變溫度比同等分子量的線性聚乙烯降低了約20 -
In part 3, the in - situ copolymerization of ethylene was investigated by the combinations of the cobalt - based catalyst and the metallocene to prepare short - branched polyethylene. the major oligomers catalyzed by the cobalt - based catalyst 5, 6 and 7 werel - butene, and the minor were 1 - hexene. the comonomer effects were also observed
在雙亞胺基吡啶鈷配合物與茂金屬復配催化乙烯原位共聚制備短支鏈支化聚乙烯中，合成了3種雙亞胺基吡啶鈷配合物，研究了反應條件對其催化乙烯齊聚活性和所得產物碳數分佈的影響。 -
Studies on ticl4 ni 2 l supported complex catalysts for ethylene polymerization to produce branched polyethylene
配體復合催化劑催化乙烯聚合制備支化聚乙烯的研究 -
Those metallocene branched polyethylene exceed all others in basic properties with processing properties being close to the general polyethylene
開發的茂金屬支化聚乙烯基本性能優于通用聚乙烯，而加工性能接近通用聚乙烯。 -
The application experiment data show that metallocene branched polyethylene prepared by the new method are applicable to tubing and large - scale hollow container
應用試驗表明，開發的茂金屬支化聚乙烯可用於製造管材和大型中空容器。 -
Basic properties of various polyethylene polymerized by metallocene catalysts and various branched polyethylene polymerized by oligomerization cocatalysts were researched, and the results show that metallocene branched polyethylene polymerized by oligomerization cocatalysts have high molecular weight, broad molecular weight distribution, and good tensile properties compared to metallocene - based polyethylenes prepared using mono - metallocene and bi - metallocene catalysts
摘要研究了不同茂金屬催化劑聚合的茂金屬聚乙烯及不同齊聚共聚催化劑聚合的茂金屬支化聚乙烯的基本性能，結果表明：以齊聚共聚催化劑體系的茂金屬支化聚乙烯比以單、雙茂金屬催化劑的茂金屬聚乙烯相對分子質量高、相對分子質量分佈寬，拉伸性能優良。