Butyl acrylate was selected as the tender monomer in prepared bpua, and when the viscosity of middle multipolymer is 800 - 1000mpa. s, the last prepolymer had good capability. in the applied research, some influencing factors such as diluent, photoinitiator and photoinitiators that match to different pigments on the coating film were studied
根據研究的結果,進行大量的配方實驗,研製了適合於皮革使用的uv上光油,經性能測試顯示:光澤度110 、耐折性3萬次、耐溶劑性200次、附著力合格,達到皮革上光油的使用要求。 -
Results show that self - crosslinkable latex at room temperature with high elasticity can be prepared when amount of butyl acrylate is 60 %, and amount of methyl methacrylate is 40 %, and mass ratio of nonionic emulsifier to anionic emulsifer is 3 : 1, and amount of initiator is 0. 6 %, and amount of self - crosslinkable monomer and protective colloid is 2 % and 0. 4 % respectively
研究結果表明:當丙烯酸丁酯的質量為60 % ,甲基丙烯酸甲酯的質量為40 % ,非離子乳化劑和陰離子乳化劑的質量配比為3 : 1 ,引發劑的質量為0 . 6 % ,自交聯單體的質量為2 % ,保護膠體的質量為0 . 4 %時,可以制備出高彈性自交聯乳液。