ceramsite 中文意思是什麼

ceramsite 解釋
素燒粘土
  1. Studies on development of ceramsite mudstone deposit in yunmeng mount of xinan

    新安縣雲夢山陶粒泥巖礦床開發研究
  2. Lightweight and refractory ceramsite concrete block for cement kiln lining

    水泥窯用陶粒輕質耐火混凝土砌塊
  3. Study on preparation of ceramsite by using industrial solid wastes

    赤泥等工業固體廢物制備陶粒的研究
  4. Compounding and application of non - cellular ceramsite concrete with super light weight

    超輕陶粒混凝土的配製與應用
  5. C : is used for purifying water quality to make the tourmaline powder tourmaline ceramsite, is used for purifying in the ore container, can remove the chlorine of the running water, thus change the acidity of water

    電氣石多與氣成作用有關，一般產于花崗偉晶巖中，也可產于交代作用形成的變質巖中。具壓電性的晶體可用於無線電工業，色澤鮮艷者可作寶石，在中國稱為碧璽。
  6. This paper deals with high fluid concrete in which high strength ceramsite made from shale was used as coarse aggregate. effects of cement content, water - cement ratio, sand percentage, mineral admixture, grading and pretreatment of lightweight aggregate on compressive strength and workability of high fluid structural lightweight aggregate concrete have been studied. the rules of water absorption of high strength lightweight aggregate under different pressure and effects on uniformity of high fluid structural lightweight aggregate concrete have been studied too

    本文採用高強頁巖陶粒，摻加高效減水劑配製大流動性結構輕集料混凝土，討論了水泥用量、水灰比、砂率、礦物摻料及輕集料的級配和預濕方式對大流動性結構輕集料混凝土強度和工作性的影響；系統研究了高強陶粒在常壓和壓力下的吸水規律；研究了影響大流動性結構輕集料混凝土勻質性的因素，提出了解決大流動性結構輕集料混凝土分層離析的具體措施。
  7. Water absorption rate of high strength ceramsite in concrete is lower than in water, and it is influenced by water - cement ratio, the higher w / c ratio, the bigger water absorption rate. and the lower w / c ratio in concrete is, the less obvious changes of water absorption rate by outer pressure and time are

    高強陶粒在混凝土中的吸水率低於其在水中的吸水率，且高強陶粒在混凝土中的吸水率要受到混凝土水灰比的影響，水灰比越大，吸水率越大；水灰比越低，吸水率隨壓力和受壓時間的變化越不明顯。
  8. Productive experiments on biological ceramsite filter for water pretreatment of the upper huangpujiang river

    生物陶粒濾池預處理黃浦江上游水的生產性試驗研究
  9. It can be concluded as following : water absorptivity of high strength ceramsite is different from that of extra - light ceramsite. in atmospheric pressure, water absorption rate of high strength ceramsite is very small, which 1hour and 75 days water absorption rate is only 2 % and 5. 7 % respectively

    上述分析研究得出以下結論：高強陶粒的吸水特性不同於超輕陶粒，其常壓吸水率很小， 1小時吸水率為2 ，吸水速度很慢， 75天吸水率僅5 . 7 。