Firstly, the surface characteristic of polystyrene particle is changed from water detesting to water intimity by using special techniques and admixtures so mat the compound quality with inorganic materials is insured. secondly, the contradiction between the weight and strength is solved through optimizing the particle size and using composite fiber and the best heat conductivity is achieved under the condition that the necessary strength is met. in the research process, the author solved the problem of fiber dispersing in insulating materials so that the contraction of the material is controlled
課題研究中，首先採用特殊的改性工藝及外加劑實現對聚苯乙烯顆粒表面的成功改性，使其表面由憎水轉化為完全親水，確保與無機材料的復合質量；其次，通過採用優化骨料級配及使用復合纖維等措施解決了保溫材料的輕質與強度的矛盾，使保溫材料在滿足必要的強度的前提下，導熱系數降至最小；並且，課題研究中成功解決了纖維在保溫材料中均勻分散的問題，達到了抑制保溫材料收縮的目的；最後，通過採用復合外加劑、合適的膠凝材料及合理的配比等措施確保該保溫材料具有良好的和易性，滿足施工的要求。 -
In the study, a new kind inorganic anchoring material was developed, which consisted of special binder and aggregate, the former is made from clinker, blast furnace slag and compound admixture, and the later is superfine sand. effects of the factors such as clinker / slag, binder / sand, solution / binder and constituent of solution on the strength, set - time and contraction of the matrix made from the anchoring material were studied
上述分析研究得出以下結論：新型無機錨固材料具有早強、快硬、高強特點， 10h .抗壓強度可達26 . 5mpa ， 365天強度可達144 . 0mpa ；初凝時間在40min . 3h .之間，且初終凝時間差在15分鐘以內；在保濕條件下具有微膨脹性，膨脹率在0 . 5 %以內。