  1. Particularly, cr4 + - doped crystals as passive q - switch ( saturable absorber ) have got extensive attention, such as cr4 + : yag ， cr4 + : gsgg ， cr4 + : mg2sio4 and cr4 + : yso, which have the advantages of wild absorption band, good saturable absorption, long restored time, good photo - chemical stability, no fading, good thermal conductivity and high damage threshold

    特別是近年來，摻cr4 +離子的各種晶體如cr4 + : yag ， cr4 + : gsgg ， cr4 + : mg2sio4和cr4 + : yso等作為被動調q開關受到了廣泛的關注。它們具有很寬的吸收帶和良好的飽和吸收性質，恢復時間較長，光化學性質穩定，無退化現象，熱導性好，損傷閾值高。
  2. In this paper, pure and doped ktp crystals were grown from the flux using a top - seeded method, and special technique have been used to lower the electrical conductivity to three orders of magnitude than common flux ktp, the values is up to 10 - 10 ( cm ) - 1, this overcame the shortcoming that common flux ktp cannot be used in e - o application field because of having higher electrical conductivity. the growth condition, doped elements and annealing technology were investigated. single crystals of ktp with high quality and big z - cut cross section were obtained by optimizing the parameter of crystal growth

    本實驗採用頂部籽晶熔劑法生長了純的以及不同摻雜的ktp晶體，用特殊工藝處理技術將普通熔劑法ktp的電導率降低了三個數量級，達到了10 ~ （ - 10 ） （ cm ） ~ （ - 1 ） ，解決了普通熔劑法ktp晶體由於離子電導率太大而無法用於電光應用領域的困難；對ktp晶體的生長條件、摻雜元素以及退火工藝等進行了研究，通過優化生長工藝技術參數，突破了工藝技術生長難關，得到了高光學均勻性、具有大z切面的ktp單晶。
  3. Blend in molten state make hdpe crystals small, crystallinity large, quantity of cb particle benefit to conductivity decreasing ; in solid state cb aggregate is sheltered with a insulate hdpe film, also cb structure will be broken down during blend ; all of these will make conductivity bad. but processing alds can lower this effect obviously. 3. the effect of crosslink is restricting the movement of molten polymer molecules

    為此筆者認為固相混合使hdpe晶粒尺寸變小，結晶度增大，使得異相成核的晶粒增多，參與導電的炭黑粒子數量減少：熔混卻使炭黑粒子表面被覆一層絕緣膜：這都將導致材料的導電性明顯變差，同時兩種混合還會造成炭黑結構的破壞，皆使得材料的導電性明顯變差。